The power-law coefficient.

The geometry of the screw makes shear heating hard to understand. Envision a flightless shaft turning in a tube. Visualize a very viscous fluid filling the space between the shaft and tube, and a slight bit of pressure at the right end. Since this imaginary material is very viscous it will rake take a lot of work to turn the shaft. The slight pressure moves the viscous fluid from right to left.

[ILLUSTRATION OMITTED]

The work by the shaft is converted to heat in the viscous fluid, known as viscous dissipation. The same thing happens with melted polymer in an actual extruder. The nick continues being heated by the rotation of the screw for as long as it remains in the barrel. The heat either stays in the polymer until it exits the extruder, or is removed from the system by passing through the barrel and cooling system.

It's hard to cool polymers because they are poor conductors of heat. Polymers are, in fact, excellent insulators--their heat-transfer rate is less than 1% of that of steel.

Meanwhile, the rotation of the screw is adding heat continuously to the melt, offsetting what is extracted. Minor changes in barrel temperature have a very small effect on the overall withdrawal of heat from the system. As screw speed is increased, addition of heat from viscous dissipation usually overrides the ability of the cooling system to absorb heat, and the melt temperature continues to increase even with maximum cooling being applied.

Screw size is a factor as well. As screw size increases, the amount of polymer vs. the surface area of the barrel increases exponentially, so the effectiveness of barrel cooling is reduced.

Fortunately runaway temperatures are not the norm because polymer viscosity is decreased by both increasing temperature and shear rate (screw speed). As a result, most extrusion processes operate in a relatively narrow range of melt temperatures for a given polymer. That said, different polymers have different sensitivities to either shear rate or temperature.

Polymers can be described by the power-law coefficient, which is a simple relationship derived from the shear-rate/viscosity curves at different temperatures. It describes the viscosity in most of the processing range of the extruder.

Viscosity([micro]) = m(T)[Y.sup.n-1]

Polymers have a consistency index (m) and a power-law coefficient (n) that describe its general viscosity behavior with respect to changing temperature (T) and shear rate (Y). The consistency index is primarily the relationship between the polymer's viscosity and temperature. Although useful in extrapolating the viscosity for design calculations, the consistency index is somewhat considered a dependent variable.
Polymer Consistency Index Power Law Temperature
 Coefficient Region,
 [degrees]C

HDPE 2.0 x [10.sup.4] 0.41 180

LDPE 6.0 x [10.sup.3] 0.39 160

Nylon 66 6.0 x [10.sup.2] 0.66 290

PC 6.0 x [10.sup.2] 0.98 300

PP 7.5 x [10.sup.3] 0.38 200

PS 2.8 x [10.sup.4] 0.28 170

PVC 1.7 x [10.sup.4] 0.26 180

Source: International Plastics Handbook, Table 3.11


The power-law coefficient, however, has significant effect on heat generation, which in turn impacts the final temperature and resultant viscosity. This is important to understanding what can be expected for a polymer's final melt temperature using a particular screw design. Polymers that have lower power-law coefficients will see a greater change in viscosity with changing shear. As the viscosity drops, the amount of energy required to rotate that portion of the screw will decrease and additional heat generated from the screw will be reduced. The accompanying table shows the consistency index and power-law coefficient for several polymer types, and the temperature range in which the values were established.

HDPE, for example, would be expected to reduce its viscosity by a factor of three compared with the viscosity reduction for nylon 66 over the same change in shear rate or screw speed. This means that the additional shear heating of HDPE would be less than for nylon 66 as screw speed increases.

By referring to the power-law coefficient, the effect of barrel override in the metering section of many screws can be explained and anticipated. Polymers with a high power-law coefficient would likely generate more heat in the melt with increasing shear rate through viscous dissipation. This adds another complexity to optimum extruder selection, wherein the ideal L/D can be influenced by the polymer's power-law coefficient. In general, polymers with high power-law coefficients should be processed at lower screw speeds and on shorter LID screws than those with low coefficients.

ABOUT THE AUTHOR

Jim Frankland is a mechanical engineer who has been involved in all types of extrusion processing for more than 40 years. He is now president of Frankland Plastics Consulting, LLC. Contact jim.frankland.comcast.net or (724)651-9196.
COPYRIGHT 2012 Gardner Publications, Inc.
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2012 Gale, Cengage Learning. All rights reserved.

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:extrusion
Author:Frankland, Jim
Publication:Plastics Technology
Date:Sep 1, 2012
Words:811
Previous Article:How do you like your acetal--homopolymer or copolymer?
Next Article:Establish a true '24/7' production process.
Topics:

Terms of use | Privacy policy | Copyright © 2021 Farlex, Inc. | Feedback | For webmasters |