Printer Friendly

Synthesis of Fe-doped ZnO nanorods by rapid mixing hydrothermal method and its application for high performance UV photodetector.

1. Introduction

Diluted transition metals (TMs) doped ZnO nanomaterials result in changing of the structural, electrical, magnetic, and optical properties of ZnO nanostructures. Transition metal doped ZnO especially is promising material as a room temperature ferromagnetic diluted magnetic semiconductors. Therefore, TMs doped ZnO nanomaterials are of interest in many current and future applications such as nanoelectronics, optoelectronics, photonic devices, spin electronics applications, and sensor devices, for example, spin-based light-emitting diodes, UV sensors, spin transistors, nonvolatile memory, and ultrafast optical switches [1-7]. Among the TMs doped ZnO nanomaterials, Fe-doped ZnO nanorods are of great potential in many applications due to the excellent electronic, magnetic, and optical properties [8]. The doping of semiconductor materials prepared by different methods or by the same method but different preparation processes usually shows different properties. New device applications of Fe-doped ZnO nanomaterials have attracted many researchers to synthetize this material using many different physical and chemical methods. Many methods have been used to synthesize Fe-doped ZnO nanomaterial with different morphologies which has been published in the literature. To mention some, Fe-doped ZnO nanoparticles were prepared by the coprecipitation method [9-11], while Fe-doped ZnO powders and Fe-doped ZnO nanorods array have been synthesized via other high temperature methods [12,13]; Fe-doped ZnO thin films were deposited by sputtering and spin coated methods [14-23], and Fe-doped ZnO nanorods were grown by the hydrothermal methods [24-27]. Among the different growth methods, the hydrothermal methods are favorable, friendly, and attractive due to simplicity, low cost, being less hazardous, scale-up possibility, and they are performed at low temperature (lower than 100[degrees]C). Furthermore, the latest property is advantageous since it can be used to grow ZnO nanostructures on flexible and foldable substrates. Moreover, the morphology and properties of ZnO nanostructures can be controlled by varying the growth conditions such as the temperature, growth time, precursor concentration, and the pH of the growth solution [28, 29].

In this work, Fe-doped ZnO nanorods were synthesized by a modified preparation procedure using the low temperature hydrothermal approach. The Fe-doped ZnO nanorods growth developed here represents a new and simple method which adopted approach by using ammonia as a continuous source of [OH.sup.-] for hydrolysis during the growth instead of hexamethylenetetramine (HMT). Morphology, chemical composition, and structural and room temperature magnetic properties of the Fe-doped ZnO have been investigated. Finally, a simple Au/Fe-doped ZnO Schottky diode based UV photodetector was fabricated and IV characteristic and time-dependent photoresponse have been conducted under on/off UV illuminations. The performance of the UV photodetector based Au/Fe-doped ZnO nanorods Schottky diode with large detection area (1 [cm.sup.2]) has been studied.

2. Experiment Procedure

2.1. Growth of Fe-Doped ZnO Nanorods. Zinc nitrate hexahydrate (ZnN[O.sub.3] x 6[H.sub.2]O), iron (II) chloride tetrahydrate (Fe[Cl.sub.2] x 4[H.sub.2]O), and iron (III) chloride hexahydrate (Fe[Cl.sub.3] x 6[H.sub.2]O) were used as precursors. All chemicals were purchased from Sigma Aldrich and were used without further purification. The growth solution was prepared by the mixing of 0.075 M of zinc nitrate hexahydrate and a specific concentration of the iron source prepared by Iron (II) chloride tetrahydrate and Iron (III) chloride hexahydrate with the ratio ([Fe+2]:[Fe+3] = 1:2) in deionized water. Then the growth solution was subsequently stirred with a magnetic stirrer at room temperature for one hour and then ammonia solution is added dropwise to the growth solution at room temperature, resulting in an orange solution with a pH = 9.3. This solution was kept under magnetic stirring for one hour at room temperature. The substrates were cleaned with isopropanol in an ultrasonic bath and then spin coated three times with a seed solution containing zinc acetate at 2500 rpm for 30 s; then the samples were annealed at 120[degrees] C for 10 minutes. Finally, the substrates were placed horizontally in the growth solution and kept in a preheated oven at 90[degrees]C for 6 hours. After the growth duration is completed, the samples were collected and washed with deionized water and dried at room temperature for further characterization. We believe that synthesis of high quality of Fe-doped ZnO nanorods can be useful for nanotechnology applications. In this adopted approach, ammonia was used to tailor pH of the growth solution and to facilitate ZnO nanocrystals growth. Ammonia reacts with water to provide continuous source of [OH.sup.-] required for hydrolysis and aid precipitation of final products. Furthermore, ammonia can generate a large amount of zinc ammine complexes immediately in the solution and these complexes are absorbed on the six side planes of ZnO nanorods, which can facilitate the growth of ZnO nanorods structure by slowing down the growth velocity of the side surfaces [30]. By increasing the ammonia content in the growth solution, the nuclei of ZnO nanocrystals can rapidly form on the substrates, which produces dense and long ZnO nanorods over a large area [31, 32]. Therefore, high ammonia contents as additive to hydrolyze in the growth solution provide Fe ions doped in ZnO nanorods without morphology deformation.

2.2. Characterization Process. The field emission scanning electron microscope (FESEM), EDX, XPS, and XRD are used to characterize the surface morphology, chemical composition, and crystal structural of the grown samples, while the room temperature ferromagnetic properties were investigated by superconducting quantum interference device (SQUID) measurements.

2.3. Device Fabrication Process. For the fabrication of the Au/Fe-doped ZnO nanorods UV photodetector, transparent FTOfilm wastaped on thetop of the Fe-doped ZnO nanorods grown on gold coated glass substrate. The schematic diagram of the simple UV photodetector based on large area Au/ZnO nanorods/FTO Schottky diode is shown in Figure 1. In a UV photodetector, large Schottky barrier height at metal semiconductor interface results in improved responsivity and improved photocurrent to dark current ratio [33, 34]. Therefore, Au with high work function was used to form a large Schottky barrier height on Fe-doped ZnO nanorods. The conducting FTO film was used as the ohmic contact due to its transparency and it also provides almost ideal ohmic contact with n-ZnO [35]. The current-voltage (I-V) curves of the fabricated diodes under dark and under UV illumination were measured by Agilent 4155B Semiconductor Parameter Analyzer. In this experiment, a constant UV illumination of 2mW/[cm.sup.2] emitting at 365 nm was used as the excitation source.

3. Results and Discussion

3.1. Morphology and Chemicals Composition. The surface morphology of the grown Fe-doped ZnO nanorods under different doping concentration has been performed by using SEM. Figures 2(a) and 2(b) show the SEM images of the 1% and 5.0% Fe-doped ZnO nanorods, respectively. The Fe-doped ZnO nanorods have hexagonal shapes with diameters varying between 100 and 300 nm. The chemical composition of the grown [Zn.sub.0.99][Fe.sub.0.01]O was measured by using EDX which is shown in Figure 2(c). The EDX data revealed that the Fe's peaks were at 0.705 keV, 6.404 keV, and 7058 keV. This indicates the Fe ions were presented in the Fe-doped ZnO nanorods samples.

In order to verify the substitutions of the Fe ions in the [Zn.sub.1-x][Fe.sub.x]O nanorods, XPS measurements were performed. Figure 3(a) shows the XPS spectra of O 1s peaks of both ZnO nanorods and Fe-doped ZnO nanorods. For ZnO nanorods, the O 1s spectrum centered at 530.9 which belongs to [O.sup.2-] in the wurtzite structure of a ZnO monocrystal and at 532.3 eV is attributed to the presence of loosely bound oxygen on the surface [15,17]. In Fe-doped ZnO nanorods, the XPS spectra of the [O.sup.2-] were slightly shifted to the higher binding energy value and the shoulder peaks are broader in comparison to the pure ZnO nanorods. This result indicates that the Fe ions indeed influence the optical properties of the ZnO nanorods. The chemical shift of the O 1s of the doped ZnO has also been revealed in the previous works [22, 27]. As we know, the binding energy of Fe 2p signals was between 700 and 740 eV and some of Zn Auger peaks are also presented in this region. Therefore, the XPS measurements were conducted for both ZnO nanorods and [Zn.sub.1-x][Fe.sub.x]O nanorods. As it is known, the FeO has a peak position of Fe 2[p.sub.1/2] at 722.3 eV and Fe 2p at 709.3 eV and [Fe.sub.2][O.sub.3] at 724.9 eV and at 710.5 eV, respectively. In this study, the XPS signals at binding energy from 695 eV to 735 eV for pure ZnO and Fe-doped ZnO are shown in Figure 3(b). From this figure, the Fe related signal in the [Zn.sub.0.99][Fe.sub.0.01]O nanorods is not resolved from the Zn Auger because it is relatively small. This is a very similar case for the Fe-doped ZnO in the previous works [20, 26]. However, the Fe 2p core level photoemission spectrum for [Zn.sub.0.95] [Fe.sub.0.05] nanorods is clearly observed, from which Fe 2[p.sub.3/2] and Fe 2[p.sub.3/2] peaks located at 725.47 and 711.7 eV can be found. These Fe 2p peak positions are almost the same as values which have been reported in many previous works [15,17,19-24, 26, 27]. These obtained binding energies are larger than [Fe.sup.3+]; it is suggested that Fe is incorporated into the ZnO lattice in a state close to [Fe.sup.3+]. Furthermore, the investigated spectra of Fe 2p showed that the spin-orbit split energy difference between Fe 2[p.sub.1/2] and Fe 2[p.sub.3/2] is 13.77 eV. These results suggested that there is no possibility of existence of [Fe.sup.2+] or [Fe.sup.0] in the samples because the energy difference of metallic ion and the FeO should be 13.10 eV and 13.4 eV, respectively [20].

3.2. Structural Characterization. The XRD patterns of the undoped ZnO nanorods, [Zn.sub.0.99][Fe.sub.0.01]O and [Zn.sub.0.95][Fe.sub.0.05]O nanorods, are shown in Figure 4(a). The high diffraction peaks at 002 direction are an indication of the hexagonal wurtzite structure with single crystalline nature and they indicate that the Fe-doped ZnO nanorods grow along the c-axis of the ZnO consistent with the JCPDS number 36-1451 file. No evidence of any other secondary phase such as FeO or [Fe.sub.3][O.sub.4] has been observed. In Figure 4(b), we observed that the peaks position at 002 direction was shifted towards higher 2d diffraction angle with the increasing of the Fe concentration and their full width at half maximum (FWHM) were also becomes larger while increasing the Fe concentration. The shift of the peaks positions and the relatively larger FWHM clearly indicated that the Fe ions replaced the Zn sites in the ZnO nanorods crystal matrix. These observations were also evident in similar samples grown by other techniques reported elsewhere [10,11,14,17-20, 24, 25].

3.3. Magnetic Property. Superconducting quantum interference device (SQUID) measurements have been performed to investigate the room temperature ferromagnetic behavior of our Fe-doped ZnO nanorods samples. Figure 5 shows the magnetic hysteresis (M-H) curves measured from -10 to 10 kOe at 300 K of Fe-doped ZnO samples. From these M-H curves, the room temperature ferromagnetic hysteresis loops are clearly observed. According to theory, Fe-doped ZnO possesses ferromagnetic property at room temperature and the magnetic moments observed are due to the Fe 3d orbitals and the observed magnetization value increases with the increase of the Fe concentration [15-17, 20, 22, 24, 25]. This supports our experimental results since we observed magnetic hysteresis at room temperature and the magnetization values observed increase from 2.5 [micro]mu to 9.1 [micro]emu for [Zn.sub.0.99] [Fe.sub.0.01] O and [Zn.sub.0.95][Fe.sub.0.05]O, respectively. This M-H loop is higher than the results reported in [21, 36]. As we see from the EDX spectra, XPS spectra, and XRD patterns of our samples, it is clearly shown that there was not any other secondary phase of Fe or Fe oxides that has been observed. Therefore, the observed room temperature ferromagnetism in our Fe-doped ZnO nanorods originates from the Fe ions substituting the Zn ions in the ZnO nanorods matrix.

3.4. UV Sensor Based Au/Fe-Doped ZnO Schottky Diode. The I-V characteristics for both the undoped ZnO and the Fe-doped ZnO Schottky diodes were investigated under dark and UV illumination. Figure 6(a) shows I-V characteristics of undopedZnO and [Zn.sub.0.95] [Fe.sub.0.05]O Schottky diodes under dark. It was observed that both Schottky diodes have good rectifying characteristics. However, the Au/[Zn.sub.0.95][Fe.sub.0.05]O Schottky diode has smaller leakage current, smaller turn on voltage with higher current at forward bias voltage than Au/ZnO Schottky diode. Without UV illumination, the observed dark current was approximately 1.62 mA and 3.56 mA at bias of 5 V for the Au/ZnO Schottky and the Au/[Zn.sub.0.95][Fe.sub.0.05]O, respectively. This high dark current indicated that the Fe-doped ZnO nanorods have intrinsic donor defects which generates many free electrons and enhanced the dark conductance [37]. Figures 6(b) and 6(c) show the dark and UV illuminated IV characteristics of the Au/[Zn.sub.0.95][Fe.sub.0.05] O Schottky diode and Au/ZnO Schottky diode, respectively. The responsivity (R) of the photodetector is given by [38-41]

R = [I.sub.ph]/[P.sub.inc], (1)

where [I.sub.ph] = [I.sub.illuminated] - [I.sub.dark] is the photocurrent and [P.sub.inc] is the incident optical power at a given wavelength ([lambda]). The responsivity values calculated at 5 V forward bias are 0.60 A/W for Au/ZnO Schottky diode and 2.33 A/W for Au/[Zn.sub.0.95][Fe.sub.0.05]O Schottky diode. The responsivity value of Au/[Zn.sub.0.95][Fe.sub.0.05]O is also higher than the commercial GaN UV detector (0.1 A/W) and other photodetectors reported in [38-43] and it is comparable to the UV photodetector reported [44]. The responsivity ratio between Au/[Zn.sub.0.95][Fe.sub.0.05]O Schottky diode and Au/ZnO Schottky diode is equal to 3.9 and it is given by

Responsivity Ratio = [R.sub.doped]/[R.sub.undoped], (2)

where [R.sub.doped] and [R.sub.undoped] are the responsivity of the Au/[Zn.sub.0.95][Fe.sub.0.05]O Schottky diode and Au/ZnO Schottky diode, respectively. The device based Au/[Zn.sub.0.95][Fe.sub.0.05]O gives higher responsivity because when Fe ions incorporated into the ZnO latticeit acts as a donor which contributes to carriers and consequently improve its optical property, which possesses more electron-hole pairs generated under UV excitation. Therefore, the incremental mobility of the [Zn.sub.0.95][Fe.sub.0.05]O nanorods exhibits higher values compared to ZnO nanorods. Figures 6(d) and 6(e) show 5 s and 7 s of rising time response for Au/[Zn.sub.0.95][Fe.sub.0.05]O Schottky and Au/ZnO Schottky diodes, respectively. While the decaying time is approximately 29 s for both devices, the rising time response is defined as the times required for the photocurrent reaching 63.3% of its saturated photocurrent and the decaying time response is refereed to 36.7% of its saturated photocurrent.

4. Conclusion

In summary, a series of high quality single crystalline of Fe-doped ZnO nanorods has been successfully synthesized using a modified hydrothermal method. A systematic study was performed to investigate the morphology and structural and magnetic properties of the Fe-doped ZnO nanorods. Finally, the grown Fe-doped ZnO was used to fabricate high performance UV photodetector. SEM results show that the Fe-doped ZnO nanorods have hexagonal shapes and the EDX data revealed that the Fe peaks were presented in the Fe-doped ZnO nanorods samples and the XPS results suggested that [Fe.sup.3+] is incorporated into the ZnO lattice. The XRD analysis showed that by increasing the concentration of the Fe in the growth solution the 002 peak position and the FWHM were shifted to higher angle and become relatively larger, respectively. It is also shown that the Fe ions replaced Zn sites and were incorporated into the ZnO matrix with no secondary phases or clusters of FeO or [Fe.sub.3][O.sub.4] observed in the grown samples. The substitution of the Fe ions in the ZnO nanorods matrix significantly was manifested in a clear ferromagnetic behavior at room temperature (300 K) and the magnetization magnitude was observed to increase from 2.5 [micro]emu to 9.1 [micro]emu for [Zn.sub.0.99][Fe.sub.0.01]O and [Zn.sub.0.95][Fe.sub.0.05]O, respectively. Moreover, the fabricated Au/Fe-doped ZnO nanorods UV photodetector device achieved both high photoresponse and fast time response. Compared to Au/ZnO nanorods Schottky device, an improvement by a factor of 3.9 was achieved.

http://dx.doi.org/ 10.1155/2014/524530

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

References

[1] M. Snure, D. Kumar, and A. Tiwari, "Progress in Zno-based diluted magnetic semiconductors," JOM, vol. 61, no. 6, pp. 72-75, 2009.

[2] T. Dietl, "Dilute magnetic semiconductors: functional ferromagnets," Nature Materials, vol. 2, pp. 646-648, 2003.

[3] S. J. Pearton, D. P. Norton, M. P. Ivill et al., "Ferromagnetism in transition-metal doped ZnO," Journal of Electronic-Materials, vol. 36, no. 4, pp. 462-471, 2007.

[4] K. R. Kittilstved, W. K. Liu, and D. R. Gamelin, "Electronic structure origins of polarity-dependent high-[T.sub.c] ferromagnetism in oxide-diluted magnetic semiconductors," Nature Materials, vol. 5, no. 4, pp. 291-297, 2006.

[5] C. Liu, F. Yun, and H. Morkoc, "Ferromagnetism of ZnO and GaN: a review," Journal of Materials Science: Materials in Electronics, vol. 16, no. 9, pp. 555-597, 2005.

[6] K. Ueda, H. Tabata, and T. Kawai, "Magnetic and electric properties of transition-metal-doped ZnO films," Applied Physics Letters, vol. 79, no. 7, pp. 988-990, 2001.

[7] P. Sharma, A. Gupta, K. V. Rao et al., "Ferromagnetism above room temperature in bulk and transparent thin films of Mn-doped ZnO," Nature Materials, vol. 2, no. 10, pp. 673-677, 2003.

[8] Y. Lin, D. Jiang, F. Lin, W. Shi, and X. Ma, "Fe-doped ZnO magnetic semiconductor by mechanical alloying," Journal of Alloys and Compounds, vol. 436, no. 1-2, pp. 30-33, 2007.

[9] S. Gautam, S. Kumar, P. Thakur et al., "Electronic structure studies of Fe-doped ZnO nanorods by x-ray absorption fine structure," Journal of Physics D: Applied Physics, vol. 42, no. 17, Article ID 175406, 2009.

[10] A. K. Mishra and D. Das, "Investigation on Fe-doped ZnO nanostructures prepared by a chemical route," Materials Science and Engineering B, vol. 171, no. 1-3, pp. 5-10, 2010.

[11] R. Saleh, S. P. Prakoso, and A. Fishli, "The influence of Fe doping on the structural, magnetic and optical properties of nanocrystalline ZnO particles," Journal of Magnetism and Magnetic Materials, vol. 324, no. 5, pp. 665-670, 2012.

[12] H. Colak and O. Turkoglu, "Synthesis, crystal structural and electrical conductivity properties of fe-doped zinc oxide powders at high temperatures," Journal of Materials Science and Technology, vol. 28, no. 3, pp. 268-274, 2012.

[13] B. Ling, J. L. Zhao, X. W. Sun, S. T. Tan, Y. Yang, and Z. L. Dong, "Electroluminescence from ferromagnetic fe-doped ZnO nanorod arrays on p-Si," IEEE Transactions on Electron Devices, vol. 57, no. 8, pp. 1948-1952, 2010.

[14] A. J. Chen, X. M. Wu, Z. D. Sha, L. J. Zhuge, and Y. D. Meng, "Structure and photoluminescence properties of Fe-doped ZnO thin films," Journal of Physics D: Applied Physics, vol. 39, no. 22, pp. 4762-4765, 2006.

[15] L.M.Wang, J.-W. Liao, Z.-A. Peng, and J.-H.Lai, "Doping effects on the characteristics of Fe:ZnO films: valence transition and hopping transport," Journal of the Electrochemical Society, vol. 156, no. 2, pp. H138-H142, 2009.

[16] X. X. Wei, C. Song, K. W. Geng, F. Zeng, B. He, and F. Pan, "Local Fe structure and ferromagnetism in Fe-doped ZnO films," Journal of Physics Condensed Matter, vol. 18, no. 31, pp. 7471-7479, 2006.

[17] W. Cheng and X. Ma, "Structural, optical and magnetic properties of Fe-doped ZnO," Journal of Physics: Conference Series, vol. 152, no. 1, Article ID012039, p. 7, 2009.

[18] A. G. Sobas, A. Galeckas, M. F. Sunding, S. Diplas, and A. Y. Kuznetsov, "An investigation of Fe-doped ZnOthin films grown by magnetron sputtering," Physica Scripta, vol. T141, Article ID 014004, 7 pages, 2010.

[19] J. T. Luo, Y. C. Yang, X. Y. Zhu, G. Chen, F. Zeng, and F. Pan, "Enhanced electromechanical response of Fe-doped ZnO films by modulating the chemical state and ionic size of the Fe dopant," Physical Review B, vol. 82, no. 1, Article ID014116, 2010.

[20] W.-G. Zhang, B. Lu, L.-Q. Zhang et al., "Influence of preparation condition and doping concentration of Fe-doped ZnO thin films: oxygen-vacancy related room temperature ferromagnetism," Thin Solid Films, vol. 519, no. 19, pp. 6624-6628, 2011.

[21] G. Chen, J. J. Peng, C. Song, F. Zeng, and F. Pan, "Interplay between chemical state, electric properties, and ferromagnetism in Fe-doped ZnO films," Journal of Applied Physics, vol. 113, no. 10, Article ID 104503, 2013.

[22] H. Y. Yang, S. F. Yu, S. P. Lau, T. S. Herng, and M. Tanemura, "Ultraviolet Laser Action in Ferromagnetic [Zn.sub.1-x][Fe.sub.x]O Nanoneedles," Nanoscale Research Letters, vol. 5, no. 1, pp. 247-251, 2010.

[23] A. P. Rambu, V. Nica, and M. Dobromir, "Influence of Fe-doping on the optical and electrical properties of ZnO films," Superlattices and Microstructures, vol. 59, pp. 87-96, 2013.

[24] C. Xia, C. Hu, Y. Tian, P. Chen, B. Wan, and J. Xu, "Room temperature ferromagnetic properties of Fe-doped ZnO rod arrays," Solid State Sciences, vol. 13, no. 2, pp. 388-393, 2011.

[25] B. Panigrahy, M. Aslam, and D. Bahadur, "Effect of Fe doping concentration on optical and magnetic properties of ZnO nanorods," Nanotechnology, vol. 23, no. 11, Article ID 115601, 2012.

[26] C. W. Liu, S. J. Chang, C. H. Hsiao et al., "Diluted magnetic nanosemiconductor: Fe-Doped ZnOvertically aligned nanorod arrays grown by hydrothermal synthesis," IEEE Transactions on Nanotechnology, vol. 12, no. 4, pp. 649-655, 2013.

[27] S. Baek, J. Song, and S. Lim, "Improvement of the optical properties of ZnO nanorods by Fe doping," Physica B, vol. 399, no. 2, pp. 101-104, 2007.

[28] M. Willander, L. L. Yang, A. Wadeasa et al., "Zinc oxide nanowires: controlled low temperature growth and some electrochemical and optical nano-devices," Journal of Materials Chemistry, vol. 19, no. 7, pp. 1006-1018, 2009.

[29] G. Amin, M. H. Asif, A. Zainelabdin, S. Zaman, O. Nur, and M. Willander, "Influence of pH, precursor concentration, growth time, and temperature on the morphology of ZnO nanostructures grown by the hydrothermal method," Journal of Nanomaterials, vol. 2011, Article ID 269692, 9 pages, 2011.

[30] X. L. Zhang, H. T. Dai, J. L. Zhao, S. G. Wang, and X. W. Sun, "Surface-morphology evolution of ZnO nanostructures grown by hydrothermal method," Crystal Research and Technology, vol. 49, no. 4, pp. 220-226, 2014.

[31] J.-H. Tian, J.Hu, S.-S. Li et al., "Improved seedless hydrothermal synthesis of dense and ultralong ZnO nanowires," Nanotechnology, vol. 22, no. 24, Article ID 245601, 2011.

[32] C. O. Chey, H. Alnoor, M. A. Abbasi, O. Nur, and M. Willander, "Fast synthesis, morphology transformation, structural and optical properties of ZnO nanorods grown by seed-free hydrothermal method," Physica Status Solidi A, 2014.

[33] L. J. Brillson and Y. Lu, "ZnO Schottky barriers and Ohmic contacts," Journal of Applied Physics, vol. 109, no. 12, Article ID 121301, p. 33, 2011.

[34] S. N. Das, J.-H. Choi, J. P. Kar, K.-J. Moon, T. I. Lee, and J.-M. Myoung, "Junction properties of Au/ZnO single nanowire Schottky diode," Applied Physics Letters, vol. 96, Article ID 092111, 2010.

[35] J. Rodriguez-Moreno, E. Navarrete-Astorga, R. Romero et al., "Electrochemically grown vertically aligned ZnO nanorod array/[p.sup.+]-Si (100) heterojunction contact diodes," Thin Solid Films, vol. 548, pp. 235-240, 2013.

[36] A. Baranowska-Korczyc, A. Reszka, K. Sobczak et al., "Magnetic Fe doped ZnO nanofibers obtained by electrospinning," Journal of Sol-Gel Science and Technology, vol. 61, pp. 494-500, 2012.

[37] X. G. Zheng, Q. S. Li, J. P. Zhao et al., "Photoconductive ultraviolet detectors based on ZnO films," Applied Surface Science, vol. 253, no. 4, pp. 2264-2267, 2006.

[38] Z. Alaie, S. M. Nejad, and M. H. Yousefi, "Recent advances in ultraviolet photodetectors," Materials Science in Semiconductor Processing, 2014.

[39] N. H. Al-Hardan, A. Jalar, M. A. Abdul Hamid, L. K. Keng, N. M. Ahmed, and R. Shamsudin, "A wide-band UV photodiode based on n-ZnO/p-Si heterojunctions," Sensors and Actuators, A: Physical, vol. 207, pp. 61-66, 2014.

[40] L. Luo, Y. Zhang, S. S. Mao, and L. Lin, "Fabrication and characterization of ZnO nanowires based UV photodiodes," Sensors and Actuators, A, vol. 127, no. 2, pp. 201-206, 2006.

[41] C. Periasamy and P. Chakrabarti, "Large-area and nanoscale n-ZnO/p-Si heterojunction photodetectors," Journal of Vacuum Science & Technology B, vol. 29, no. 5, Article ID051206, 2011.

[42] S. J. Young, L.W. Ji, T. H. Fang, S. J. Chang, Y. K. Su, and X. L. Du, "ZnO ultraviolet photodiodes with Pd contact electrodes," Acta Materialia, vol. 55, no. 1, pp. 329-333, 2007.

[43] M. H. Mamat, Z. Khusaimi, M. Z. Musa, M. F. Malek, and M. Rusop, "Fabrication of ultraviolet photoconductive sensor using a novel aluminium-doped zinc oxide nanorod-nanoflake network thin film prepared via ultrasonic-assisted sol-gel and immersion methods," Sensors and Actuators A: Physical, vol. 171, no. 2, pp. 241-247, 2011.

[44] Z. Yang, M. Wang, X. Song, G. Yan, Y. Ding, and J. Bai, "High-performance ZnO/Ag Nanowire/ZnO composite film UV photodetectors with large area and low operating voltage," Journal of Materials Chemistry C, vol. 2, no. 21, pp. 4312-4319, 2014.

Chan Oeurn Chey, (1) Ansar Masood, (2) A. Riazanova, (2) Xianjie Liu, (3) K. V. Rao, (2) Omer Nur, (1) and Magnus Willander (1)

(1) Department of Science and Technology, Linkoping University, 601 74 Norrkoping, Sweden

(2) Department of Materials Science, Royal Institute of Technology, 100 44 Stockholm, Sweden

(3) Department of Physics, Chemistry and Biology, Linkoping University, 881 83 Linkoping, Sweden

Correspondence should be addressed to Chan Oeurn Chey; chan.oeurn.chey@liu.se

Received 4 July 2014; Revised 16 September 2014; Accepted 11 October 2014; Published 6 November 2014

Academic Editor: Fathallah Karimzadeh
COPYRIGHT 2014 Hindawi Limited
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2014 Gale, Cengage Learning. All rights reserved.

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:Research Article
Author:Chey, Chan Oeurn; Masood, Ansar; Riazanova, A.; Liu, Xianjie; Rao, K.V.; Nur, Omer; Willander, Magnu
Publication:Journal of Nanomaterials
Date:Jan 1, 2014
Words:4500
Previous Article:In Vivo imaging of nitric oxide by magnetic resonance imaging techniques.
Next Article:Surface wettability of oxygen plasma treated porous silicon.
Topics:

Terms of use | Privacy policy | Copyright © 2019 Farlex, Inc. | Feedback | For webmasters