Pumice characteristics and their utilization on the synthesis of mesoporous minerals and on the removal of heavy metals.

1. Introduction

Zeolite is a natural porous mineral described as hydrated aluminosilicates containing exchangeable alkali and earth alkaline cations ([Na.sup.+], [K.sup.+], [Ca.sup.2+], or [Mg.sup.2+]) and could be synthesised from the aluminium silicate materials as clay minerals and pumice by alkali attack [1-3]. Zeolites have a large surface area, microporous structure, and high affinity for metal ions, providing an efficient scavenging pathway for heavy metals in toxic systems [4, 5]. Some of the attractive applications of natural zeolites are listed by Taffarel and Rubio [6] and Babel and Kurniawan [7]. Most of these research efforts are undertaken on laboratory scale and are at early stages of investigations to develop the synthesis methods. Synthetic zeolites are carried out in many industrialized countries in Europe, East Asia, and North America. Their consumption is dominated by companies manufacturing detergents and catalysts. Restrictions on the use of phosphate detergents have increased the demand for synthetic zeolites. Synthetic zeolites (molecular sieves) are the major alternate materials to natural zeolites. Na-[P.sub.1] zeolite is one of the synthetic zeolites which are a class of highly porous materials. The unique structural features of these crystalline microporous solids that contain pores and cavities in the order of molecular dimensions (3-10 A) are the main reason for their application in the realms of catalysis, separation, purification, ion exchange, and radioactive waste clean-up. More novel applications for Na-[P.sub.1] zeolites are expected in electrochemistry, photochemistry, pharmaceutical, engineering, membrane science, and nanotechnology as their structures are expanded and more suitably engineered in a foreseeable future. It is well established that these materials that are equivalently called molecular sieves are mainly hydrated aluminosilicates. Zeolite Na-[P.sub.1] contains two-dimensional pore system with two intersecting 8-ring channels [8]. A synthetic zeolite Na-[P.sub.1] has similar pore structure to the natural zeolite phillipsite. Na-[P.sub.1] zeolite is classified as high silica zeolites where it has Si/Al ratio equal to or greater than about 3. It is considered as a hydrated sodium aluminosilicatezeolite that couldbesynthesised from the naturally occurring alkaline volcano with NaOH attack of varying concentrations at different volcanic temperatures. Pumice is a natural rock of volcanic origin, formed by gases released during the solidification of acidic lava. The vesicular structure of pumice is formed during the eruption of gases contained in the molten viscous lava on cooling. In Egypt, pumice occasionally occurs in few locations, at the northern coast of the Mediterranean Sea at El-Arish, North Sinai [9]. The heavy metals contamination of water by the discharge of industrial wastewater of electroplating, metallurgy, chemical manufacturing, mining, and battery manufacturing is a worldwide environmental problem. Adsorption process provides an attractive alternative treatment to other removal techniques because it is more economical and readily available [10-12].

A good number of adsorbents have been used for Cd(II), Fe(II), Cu(II), and Co(II) removal from water. The adsorption of Cd(II) on red mud fitted Langmuir isotherm model having a maximum adsorption capacity of 10.57 mg [g.sup.-1] [13]. Wang [14] used maize cobs for adsorption of Fe(III) from aqueous solution with the Langmuir adsorption capacity and the Freundlich adsorption capacity being 2.53 mg [g.sup.-1] and 0.104 L [g.sup.-1], respectively. The maximum adsorption capacity for Cu(II) on red mud was observed as 19.72mg [g.sup.-1] [13]. Gupta et al. [15] used Spirogyra species for removal of Cu(II) with the maximum adsorption capacity of 133.3 mg [g.sup.-1]. Use of adsorbents like Mg pellets has also been reported for Co(II) removal from water [16] and the adsorption capacityhasbeen found tobe 15.8mg [g.sup.-1].

The aim of this work is to study the best condition of temperature, sodium hydroxide concentration, and time required for synthesis of Na-[P.sub.1] zeolite from the local pumice raw material and utilize the synthetic zeolite as an adsorbent for removing ([Cd.sup.2+], [Fe.sup.2+], [Cu.sup.2+], and [Co.sup.2+]) ions from synthetic solutions in a batch laboratory system. Also, the effect of experimental conditions such as contact time and initial zeolite dose was described.

2. Materials and Methods

2.1. Materials. The main material used in this work is pumice grains received from El-Nile Mining Company from the Mediterranean Sea coast at El-Arish province, North Sinai, Egypt. In addition, commercial NaOH is used for alkaline hydrothermal attack for synthesis of zeolite from pumice. Hydrated chloride salts of Cu, Co, Fe, and Cd of analytical grade (AR) supplied by Merck as analytical-grade reagents and deionized water are used.

2.2. Methods

2.2.1. Adsorbates. All adsorption experiments were carried out using an aqueous solution of Cu[Cl.sub.2]-2[H.sub.2]O, Co[Cl.sub.2]-6[H.sub.2]O, Fe[Cl.sub.2], and Cd[Cl.sub.2]-[H.sub.2]O. The stock solution was prepared by dissolving accurately weighted salt in distilled water to the concentration of 500mg/L. The initial concentrations of solution were done by diluting the stock solutions in appropriate proportions to different initial concentrations.

2.2.2. Adsorbents. Na-[P.sub.1] has been prepared from pumice, which is naturally occurring alkaline volcanic rock with NaOH attack. A series of experiments were conducted to synthesis Na-[P.sub.1] zeolite from locally produced pumice raw material at temperatures (80 to 120[degrees] C), NaOH solution concentrations (1-3 molar), and crystallization periods (12 h, one week, and up to one month. The dry pumice grains were well ground and passed through 63 [micro]m sieve. Pumice powder was mixed with NaOH solution in a well-sealed Teflon cylindrical vessel, heated, and stirred for 12 hours at 80[degrees]C, and then the vessel was kept in the dryer at 80-90[degrees]C for one week. The produced gel was filtered and washed well till becoming free from sodium hydroxide; the wet powder was dried for 24 h in the dryer at 110[degrees]C. The optimum conditions required for synthesis of Na-[P.sub.1] zeolite from locally produced pumice raw material are one molar NaOH concentration, temperature at 80[degrees]C, and one week as a crystallization time. Several investigations for the adsorption of the heavy metal were carried out, including effect of contact zeolite dose, effect of time, and effect of metals concentration.

2.3. Characteristics of Adsorbents. The physical and chemical characteristics of prepared adsorbents such as slurry pH, point of zero charge ([pH.sub.PZC]), bulk density, and moisture were performed to determine the capability of prepared adsorbents in removing the metals [Co.sup.2+], [Cu.sup.2+], [Fe.sup.2+], and [Cd.sup.2+] from an aqueous media. For pH determination, 0.2 g of the dry, grinded adsorbent was mixed with 25 mL of distilled water and allowed to boil for 30 min in stoppered glass bottle. After cooling, the pH of the adsorbent was measured using a digital pH meter (HANNA, model pH20), allowing 5 min for the pH probe to equilibrate. Also, the point of zero charge (PZC) for the samples was determined by the following procedure: 200 mL of deionized water was added to an Erlenmeyer flask, which was then capped with stoppered glass. The deionized water was heated until boiling for 20 min to eliminate the C[O.sub.2] dissolved in the water. The C[O.sub.2]-free water was cooled down as soon as possible and the flask was immediately capped. On the other hand, 0.5 g of each sample was weighed and placed in a 25 mL Erlenmeyer flask to which 20 mL of C[O.sub.2]-free water was added. The flask was sealed with a rubber stopper and left in continuous agitation for 72 h at 25[degrees]C. Then the solution pH was measured and this value is the point of zero charge. The bulk density was estimated by a standard procedure by weighing a known volume of gently tapped adsorbent granules. The apparent density was calculated from the volume of the graduated cylinder closely packed with the powdered sample and from the sample weight in triplicate. For moisture measurement, about 0.5 g of powdered air-dried adsorbent sample is weighed and taken in a crucible. The crucible is placed inside an electric hot-air oven and heated at 150[degrees]C for 3 hours. It is then taken out, cooled in a desiccator, and weighed. From this, the percentage of moisture can be calculated as follows: percentage of moisture = (loss in weight of adsorbent/weight of air-dried adsorbent taken) x 100.

Surface characteristics of prepared zeolite sample were characterized by scanning electron microscope (SEM) using SEM model philips XL 30 attached with EDX unit, with accelerating voltage 30 K.V., magnification 10x up to 400.000x, and resolution for W (3.5 nm). Samples are coated with gold. X-ray powder diffractograms, XRD, of the samples were recorded using a Bruker diffractometer (Bruker D8 advance target) and the scan rate was fixed at 8[degrees] in 20 min-1 for phase identification. The patterns were run with Cu Ka and secondly with monochromator (A = 0.1545 nm) at 40 kV and 40 mA. Mineralogical and chemical study of the pumice were done by using X-ray fluorescence spectrometer (XRF) to identify the chemical composition. XRF, a spectrometer with wavelength dispersion PW 2400 Philips, and centrifuge Hermle were used. XRF shows that quartz, cristobalite, and albite are the main constituents in the pumice (Figure 2). Si[O.sub.2], [Al.sub.2][O.sub.3], and [Na.sub.2]O are the main oxides in the pumice under investigation (93.69%) confirming the mineralogical constituents, whereas Ti[O.sub.2], MnO, MgO, [Fe.sub.2][O.sub.3], and CaO analyzed in the pumice under are calculated as 3.88% (Table 1). The concentrations of heavy metals in all samples were determined according to APHA using Atomic Absorption Spectrometer Unicam model 939 with graphite furnace accessory, equipped with deuterium are background corrector. Precision of the metal measurement was determined by analyzing (in triplicate) the metal concentration of all samples and for each series of measurements an absorption calibration curve was constructed, composed of a blank and three or more standards. Accuracy and precision of the metals measurement were confirmed using external reference standards from Merck.

2.4. Adsorption Isotherms. The adsorption isotherm shows the equilibrium relationship of concentration in the adsorbate-adsorbent system at constant temperature.

The equilibrium adsorption isotherm is fundamentally important in the design of adsorption systems. Such adsorption isotherms may be used for scaling up batch type processes with moderate success. The shape of the equilibrium adsorption isotherm provides us with information about the adsorbent surface whether it is homogeneous or heterogeneous. Also, its study is helpful in evaluating the maximum adsorption capacity of adsorbate for the given adsorbent. For adsorption isotherms models were used in this work, Langmuir and Freundlich isotherms. They differ in their assumption, shape of the isotherm, and nature of the adsorbent surface.

2.5. Langmuir Isotherm Model. Langmuir (1918) model assumes that uptake of metal ion occurs on a homogeneous surface by monolayer adsorption without any interaction between adsorbed ions. The model is also based on the assumption that all the sorption sites are energetically identical and sorption occurs on a structurally homogeneous sorbent. The linear form of Langmuir is given as follows:

[C.sub.e]/[q.sub.e] = 1/[K.sub.L][Q.sub.m] + 1/[Q.sub.m] [C.sub.e]. (1)

Thus, a linear plot of CJqe versus Ce confirms the validity of the Langmuir giving correlation coefficients ([R.sup.2]) close to unity, and [K.sub.L] is a constant related to the free energy of adsorption as expressed ([K.sub.L][alpha] [e.sup.-[DELTA]G/RT]). Deviations from the basic assumption of the Langmuir model do limit interpretation of the values for [Q.sub.m] and [K.sub.L] in terms of absolute surface areas and sorption free energies. The free energy of adsorption, AG, can also be evaluated from the parameter [K.sub.L] according to the expression [DELTA]G = RT ln [K.sub.L]. Values of [Q.sub.m] and [K.sub.L] are obtained from slope and intercept of [C.sub.e]/[q.sub.e] versus [C.sub.e] plot, respectively. A further analysis of the Langmuir equation can be made on the basis of a dimensionless equilibrium parameter, [R.sub.L] (known as the separation factor which is considered as a more reliable indicator of adsorptions). This parameter ([R.sub.L]) can be expressed by Weber and Chakkravorti (1974):

[R.sub.L] = 1/1 + b[C.sub.i], (2)

where C; is the initial concentration metal ion (mg/L) and b (Lm[g.sup.-1]) is the Langmuir constant described above.

Also, the influence of the isotherm shape on whether the adsorption is "favorable" or "unfavorable" at highest initial concentration of the dye, [C.sub.o], can be described by a term "[R.sub.L]", a dimensionless constant separation factor in equation; calculated value for RL indicates the nature of adsorption process as given: irreversible ([R.sub.L] = 0),favorable (0 < [R.sub.L] < 1), linear ([R.sub.L] = 1), and favorable ([R.sub.L] > 1).

2.6. Freundlich Isotherm Model. Freundlich isotherm is an empirical equation that can be described as the reversible adsorption onto heterogeneous surface at sites with different energy of adsorption and is not restricted to the formation of the monolayer of adsorbate. The nonlinear form of this model is expressed as

[q.sub.e] = [K.sub.F][C.sub.e.sup.1/n], (3)

where [K.sub.F] is the Freundlich constant (mg/g)/(L/mg)1/n and also referred to as adsorption capacity, while n is the heterogeneity factor and related to adsorption intensity. The parameter n gives an indication of the adsorption type whether is linear (n = 1) or a physical process (n > 1) is favorable, or a chemical process (n < 1). On the other hand, the value of 1/n < 1 or 1/n > 1 indicates a normal Langmuir isotherm and cooperative adsorption, respectively. Freundlich model can be represented by linear form as follows:

ln [q.sub.e] = ln [K.sub.F] + 1/n ln [C.sub.e]. (4)

A plot of ln [q.sub.e] versus ln [C.sub.e] gives a straight line, where the values of [K.sub.F] and 1/n are determined from the intercept and the slope, respectively.

2.7. Adsorption Kinetic Experiments. The kinetic tests were carried out following the same procedure used for the equilibrium tests. Aqueous samples were taken at different intervals of time and the concentrations of adsorbent were measured at the same intervals. The amount of absorbed onto the developed adsorbents at time t (min), qt (mg/g) was calculated by means of the expression below:

[q.sub.e] = ([C.sub.0] - [C.sub.t])V/m, (5)

where [C.sub.0] and [C.sub.t] are the liquid-phase concentrations at an initial and predetermined time t (mg/L), respectively, V is the volume of solution (L), and m is the dry weight of the added adsorbent (g). The kinetic data were then carried out for the pseudo-first-order and pseudo-second-order.

2.8. Pseudo-First-Order Kinetic Model. The rate constant of adsorption was determined from the pseudo-first-order equation:

log ([q.sub.e] - [q.sub.t]) = log [q.sub.e] - [k.sub.1]t/2.303, (6)

where [q.sub.e] and [q.sub.t] (mg/g) are the amounts of adsorbed (mg/g) at equilibrium and at time t (min), respectively, and [k.sub.t] is the adsorption rate constant ([min.sup.-1]).

2.9. Pseudo-Second-Order Kinetic Model. The pseudosecond-order equation based on the equilibrium adsorption is expressed as

t/[q.sub.t] = 1/[k.sub.2][q.sub.e.sup.2] + t/[q.sub.e], (7)

where [k.sub.2] (g/mg x min) is the rate constant of second-order adsorption.

3. Results and Discussions

3.1. Characterization of Pumice and Synthetic Zeolite. Some physical and chemical features of pumice and Na-zeolite [P.sub.1] are listed in Table 2. It is evident that the treatment with NaOH has a significant efficiency on the physicochemical properties of synthesized adsorbent Na-zeolite [P.sub.1]. The pH of the aqueous slurry and [pH.sub.PZC] of adsorbents may give a good indication about the surface oxygen complexes and the electronic surface charges of adsorbents. This surface charge arises from the interaction between adsorbent surface and the aqueous solution. The complexes on adsorbent surface are generally classified as acidic, basic, or neutral. Based on the slurry pH, the nature of surface oxygen groups on the support and the dominant complexes can be deduced. From Table 2, it is clear that the pH is higher than the [pH.sub.PZC]; the surface of the adsorbent is negatively charged, favoring the adsorption of cationic species ([Co.sup.+2], Cu, [Fe.sup.+2], and [Cd.sup.+2]). Bulk density of the pumice and Na-zeolite [P.sub.1] decreased from 0.85 to 0.50 mg/g and the moisture is 0%. This finding is due to the generation of porous structure and the increase in binding sites after chemical modification. Chemical and phase composition as well as microstructure of the pumice raw material have been studied. The data obtained from the XRF andXRD are discussed before [17]. Table 1 illustrates that Si[O.sub.2] is the major component (~71.0%) with about 14.20% [Al.sub.2][O.sub.3] as well as a total of about 12.4% fluxing oxides. XRD pattern in Figure 1 confirms the glassy phase in addition to minor crystalline quartz phase, which is the only phase. The amorphous nature of the silicate pumice as well as the high content of the pore size with variable distributions is ensured by the SEM in Figure 3(b). Phase composition and microstructure of the synthetic zeolite studied by XRD (Figure 2) and SEM reveal that the zeolite [P.sub.1] is the only phase formed during these conditions of alkali treatment during the alkaline hydrothermal attack of locally produced pumice raw material at the optimum condition of synthesis. The micrograph of synthetic zeolite shows very fine agglomerated crystalline grains (gray) Figure 3(a). XRD analysis was used to prove the formation of Na-zeolite [P.sub.1] before and after treatment with NaOH. The X-ray diffractogram of pumice shows that it was considered a glass because it has no crystal structure. Pumice is an unusually light rock due to the many bubbles inside it, Figure 3(b). Pumice has an average porosity of 90% and initially floats on water. Pumice varies in density according to the thickness of the solid material between the bubbles; many samples float in water. It is formed by volcanic eruptions when molten lava is shot in the air with many bubbles of gas in it. As it cools, it solidifies into pumice. The treatment with NaOH leads to the formation of Na-zeolite [P.sub.1] which has higher degree of crystallinity, Figure 3(a). XRD analysis was used to prove the formation of Na-zeolite [P.sub.1] before and after treatment with NaOH.

3.2. Adsorption Experiments. Adsorption isotherm and kinetics of [Co.sup.+2], [Cu.sup. +2], [Fe.sup. +2], and [Cd.sup. +2] on the synthetic zeolite were investigated using batch experiments. Equilibrium and kinetic studies were carried out on the removal of [Co.sup.+2], [Cu.sup.+2], [Fe.sup.+2], and [Cd.sup.+2] from aqueous solution using synthetic zeolite [P.sub.1]. Adsorption test on prepared adsorbent was studied using a batch process. For this purpose, the effects of adsorbents dose (0.1-1 g), contact time (1-8 min), and metal concentration (300-700 mg/L) on the adsorption of [Co.sup.+2], [Cu.sup.+2], [Fe.sup.+2], and [Cd.sup.+2] (25 mL of 100 mg/L) were evaluated during the present study. For all the above-mentioned equilibrium and kinetic studies, the mixture of adsorbent and solution was magnetically stirred at 150 rpm for 30 min as determined from kinetic tests.

3.3. Effect of Zeolite Dose. Batch adsorption experiments were conducted by mixing 50 [cm.sup.3] solutions of 500 ppm containing one metal of [Co.sup.2+], [Cu.sup.2+], [Fe.sup.2+], and [Cd.sup.2+] with a constant dose of Na-zeolite Px (0.1 g, 0.25 g, 0.5 g, 0.75 g, or 1g) in 100 [cm.sup.3] Pyrex Erlenmeyer flasks with cap. Flasks were shaken (150 rpm) at 25 [+ or -] 1[degrees]C using a Brunswick Scientific G25KC incubator orbital shaker. It is observed that the percentage adsorption for [Co.sup.+2], [Cu.sup.+2], [Fe.sup.+2], and [Cd.sup.+2] ions increases with increasing zeolite weight in aqueous solutions as illustrated in Figure 4. The maximal exchange levels attained were as follows: [Cd.sup.+2] > [Fe.sup.+2] > [Cu.sup.+2] > [Co.sup.+2]. The heavy-metal uptake may be attributed to different mechanisms of ion-exchange processes as well as to the adsorption process 18-20]. During the ion-exchange process, metal ions had to move not only through the pores of the Na-zeolite Px mass, but also through channels of the lattice, and they had to replace exchangeable cations (mainly sodium). Diffusion was faster through the pores and was retarded when the ions moved through the smaller diameter channels. In this case the metal ion uptake 6 could mainly be attributed to ion-exchange reactions in the microporous minerals of the Na-zeolite Pl samples.

3.4. Effect of Contact Time. By varying the contact time (1, 2, 4, 6, and 8 min) while keeping all other parameters constant with respect to pH, temperature, and dose of Na-zeolite Pl, 0.25 gm, the influence of contact time on the zeolite capacity for different metal ions is shown in Figure 5. Removal efficiency increases for Cadmium from 95 to 98%, for copper from 71 to 76%, for iron from 64 to 76%, and for cobalt from 58 to 61% as the time increases from 1 to 8 min. Figure 6 represents the variation in metal ion adsorption with time; however the adsorption rate becomes slower with passage of time up to 4 min. The initial faster rate of removal of each metal ion may be due to the availability of the uncovered surface area of the adsorbents. The slight increase in the percentage of adsorption of each metal adsorbent is [Cd.sup.+2] > [Fe.sup.+2] > [Cu.sup.+2] > [Co.sup.+2]. This maybe attributed to the difference in nature between metal ions with respect to Na-zeolite Px surface. That may be attributed to different mechanisms of ion-exchange processes as well as the adsorption process 18-20].

3.5. Effect of Metals Concentration. The uptake of Cd(II), Cu(II), Ni(II), Pb(II), and Zn(II) onto Na-zeolite P: as a function of their concentrations was studied at 25 [+ or -] 0.1[degrees]C by varying the metal concentrations 300,400,500, and 700 mg/L while keeping all other parameters constant with respect to dose and time.

3.6. Adsorption Isotherms. For adsorption isotherms models were used in this work, Langmuir and Freundlich isotherms. They differ in their assumption, shape of the isotherm, and nature of the adsorbent surface.

3.7. Langmuir Isotherm Model. Langmuir (1918) isotherm which models the monolayer coverage of the sorbent surface assumes that sorption occurs at specific homogeneous sorption site. The model is also based on the assumption that all the sorption sites are energetically identical and sorption occurs on a structurally homogeneous sorbent [1820]. Figure 7 shows that the Langmuir model effectively and significantly described the sorption data with all [R.sup.2] values > 0.96. Table 3 shows the relation between the ionic radius, electronegativity, and Langmuir constant. The maximum sorption capacity (KL) represents monolayer coverage of sorbent; according to the KL (mg/g) parameter, monolayer capacities of zeolite are arranged in the following sequence: [Cd.sup.+2] > [Fe.sup.+2] > [Cu.sup.+2] > [Co.sup.+2]. These metals seem to reach saturation, which means that the metal had clogged possible available sites in zeolite and further adsorption could take place only at new surfaces [21]. The sequence of adsorption of several heavy metals are not correlated either with the sequence of ionic radii or with the sequence of electro-negativity. There is, however, a parallel relation between the adsorption sequence and the hydrolysis properties of the heavy metal cations, as pointed out by several investigators [22-24].

3.8. Freundlich Isotherm Model. This isotherm developed by Freundlich (1926) describes the equilibrium on heterogeneous surfaces and does not assume monolayer capacity. This isotherm gives an expression encompassing the surface heterogeneity and the exponential distribution of active sites and their energies. A linear plot is obtained when log [C.sub.e] is plotted against log [q.sub.e] over the entire concentration range of metal ions investigated and the values of KF (mg/g) and n can be calculated from the intercept and the slope of this straight line, respectively (Figure 8). The arrangement of heavy metals according to dose required for the reduction of metal concentrations in Freundlich equation is [Cd.sup.+2] > [Fe.sup.+2] > [Cu.sup.+2] > [Co.sup.+2]. The adsorption isotherm data were fitted well to the Langmuir model from Langmuir model equations.

3.9. Sorption Kinetics. In order to investigate the adsorption kinetics of heavy metals on the prepared zeolite adsorbent, three kinetic models have been tested: pseudo-first-order. The calculated parameters from pseudo-first-order and pseudosecond-order models (Figures 9 and 10) are summarized in Table 4. According to the pseudo-first-order model, the values of [k.sub.1] and [q.sub.e] were calculated from the slope and intercept from the plots of log ([q.sub.e] - [q.sub.t]) versus t. It was found that the experimental values were not adequate with the calculated ones (Table 4), indicating that the first-order model does not reproduce the adsorption kinetic of heavy metals on the prepared adsorbents. In case of the pseudosecond-order model, the calculated values of kinetic studies showed that the zeolite is a good potential as adsorbent for ([Co.sup.2+], [Cu.sup.2+], [Fe.sup.2+], and [Cd.sup.2+]) ions follows the pseudosecond-order, and, hence, this model is more likely to predict the behavior over the whole experimental range of H M adsorption more than pseudo-first-order model. Also, the values of correlation coefficients (2) are close to unity for pseudo-second-order model rather than the pseudo-first-order one; that is, the kinetic removal of H M is quite described by pseudo-second-order model.

4. Conclusion

The alkaline treatment of very cheap local pumice leads to the formation of Na-zeolite [P.sub.1] which has the high degree of crystallinity, the pH is higher than the [pH.sub.PZC], and the surface of the adsorbent is negatively charged, favoring the adsorption of cationic species ([Co.sup.+2], [Cu.sup.+2], [Fe.sup.+2], and [Cd.sup.+2]). The adsorption kinetics study of the heavy metals followed a pseudo-second-order model. This indicates that the adsorption may be controlled by chemical adsorption. Both the Langmuir and Freundlich models fit equilibrium data well implying the existence of a monolayer adsorption and a heterogeneous surface existence in Na-zeolite [P.sub.1], showing a strong adsorption capacity for ([Co.sup.2+], [Cu.sup.2+], [Fe.sup.+2], and [Cd.sup.2+]) ions reaching a maximum capacity for [Cd.sup.2+]. Heavy metal ions uptake is the result of a combination of several interfacial reactions, namely, ion exchange, chemisorption, and adsorption as potential determining ions. Results found showed that the modified zeolite shows a good potential as adsorbent for ([Co.sup.2+], [Cu.sup.2+], [Fe.sup.2+], and [Cd.sup.2+]) ions.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

http://dx.doi.org/10.1155/2014/259379

References

[1] M. K. Doula, "Removal of [Mn.sup.2+] ions from drinking water by using Clinoptilolite and a Clinoptilolite-Fe oxide system," Water Research, vol. 40, no. 17, pp. 3167-3176, 2006.

[2] E. Erdem, N. Karapinar, and R. Donat, "The removal of heavy metal cations by natural zeolites," Journal of Colloid and Interface Science, vol. 280, no. 2, pp. 309-314, 2004.

[3] V. J. Inglezakis, M. D. Loizidou, and H. P. Grigoropoulou, "Equilibrium and kinetic ion exchange studies of [Pb.sup.2+], [Cr.sup.3+], [Fe.sup.3+] and [Cu.sup.2+] on natural clinoptilolite," Water Research, vol. 36, no. 11, pp. 2784-2792, 2002.

[4] W. Zou, R. Han, Z. Chen, Z. Jinghua, and J. Shi, "Kinetic study of adsorption of Cu(II) and Pb(II) from aqueous solutions using manganese oxide coated zeolite in batch mode," Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 279, no. 1-3, pp. 238-246, 2006.

[5] W. Zou, R. Han, Z. Chen, J. Shi, and L. Hongmin, "Characterization and properties of manganese oxide coated zeolite as adsorbent for removal of copper(II) and lead(II) ions from solution," Journal of Chemical & EngineeringData, vol. 51, no. 2, pp. 534-541, 2006.

[6] S. R. Taffarel and J. Rubio, "On the removal of [Mn.sup.2+] ions by adsorption onto natural and activated Chilean zeolites," Minerals Engineering, vol. 22, no. 4, pp. 336-343, 2009.

[7] S. Babel and T. A. Kurniawan, "Low-cost adsorbents for heavy metals uptake from contaminated water: a review," Journal of Hazardous Materials, vol. 97, no. 1-3, pp. 219-243, 2003.

[8] R. Szostak, Handbook of Molecular Sieves, Van Nostrand Reinhold, New York, NY, USA, 1992.

[9] R. D. Crangle, "Pumice and pumicite," in U.S. Geological Survey Minerals Year Book--Mineral Commodity Summaries, pp. 124125, 2010.

[10] G. Fu, H. E. Allen, and C. E. Cowan, "Adsorption of cadmium and copper by manganese oxide," Soil Science, vol. 152, no. 2, pp. 72-81, 1991.

[11] B. H. Tamura, N. Katayama, and R. Furuichi, "The [Co.sup.2+] adsorption properties of [Al.sub.2][O.sub.3], [Fe.sub.2][O.sub.3], [Fe.sub.3][O.sub.4], Ti[O.sub.2] and Mn[O.sub.2] evaluated by modeling with the Frumkin isotherm," Journal of Colloid and Interface Science, vol. 195, no. 1, pp. 192-202,1997

[12] A. Birsen and A. D. Timothy, "Application of Mn[O.sub.2] coated scintillating and extractive scintillating resins to screening for radioactivity in groundwater," Nuclear Instruments and Methods in Physics Research A, vol. 505, no. 1-2, pp. 458-461, 2003.

[13] E. Lopez, B. Soto, M. Arias, A. Nunez, D. Rubinos, and M. T. Barral, "Adsorbent properties of red mud and its use for wastewater treatment," Water Research, vol. 32, no. 4, pp. 13141322, 1998.

[14] Y. H. Wang, S. H. Lin, and R. S. Juang, "Removal of heavy metal ions from aqueous solutions using various low-cost adsorbents," Journal of Hazardous Materials, vol. 102, pp. 291-302, 2003.

[15] V. K. Gupta, A. Rastogi, V. K. Saini, and N. Jain, "Biosorption of copper(II) from aqueous solutions by Spirogyra species," Journal of Colloid and Interface Science, vol. 296, no. 1, pp. 59-63, 2006.

[16] M. M. Nassar, Separation Science and Technology, vol. 41, 943, 2006.

[17] M. S. Elmaghraby, H. S. Mekky, and M. A. Serry, "Light weight insulating concrete based on natural pumice aggregate," InterCeram, vol. 61, no. 6, pp. 354-357, 2012.

[18] M. Akgul, A. Karabakan, O. Acar, and Y. Yuriim, "Removal of silver (I) from aqueous solutions with clinoptilolite," Microporous and Mesoporous Materials, vol. 94, no. 1-3, pp. 99-104, 2006.

[19] B. Aleksiev, E. Djourova, and Z. Milakovska-Vergilova, "Zeolitic rocks from the Mezek Mountains," in Godishnik naSofiiskiya Universitet, N. E. Rhodopes, Ed., vol. 92, pp. 159-165, Sv. Kliment Okhridsk, Geologo-Geografski Fakultet, Kniga 1: Geologiya, 2000.

[20] R. Harjula, A. Dyer, S. D. Pearson, and R. P. Townsend, "Ion exchange in zeolites. Part 1. Prediction of [Ca.sup.2+]-[Na.sup.+] equilibria in zeolites X and Y," Journal of the Chemical Society, Faraday Transactions, vol. 88, no. 11, pp. 1591-1597,1992.

[21] A. Abd-Elfattah and K. Wada, "Adsorption of lead, copper, zinc, cobalt, and cadmium by soils that differ in cation-exchange materials," Journal of Soil Sciences, vol. 32, pp. 273-283, 1981.

[22] H. A. Elliott, M. R. Liberati, and C. P. Huang, "Competitive adsorption of heavy metals by soils," Journal of Environmental Quality, vol. 15, no. 3, pp. 214-219,1986.

[23] U. Schwertmann and R. M. Taylor, "Iron oxides," in Minerals in Soil Environments, J. B. Dixon and S. B. Weed, Eds., pp. 379-438, ASA and SSSA, Madison, Wis, USA, 1989.

[24] M. Prasad, H.-Y. Xu, and S. Saxena, "Multi-component sorption of Pb(II), Cu(II) and Zn(II) onto low-cost mineral adsorbent," Journal of Hazardous Materials, vol. 154, no. 1-3, pp. 221-229, 2008.

[25] D. W. Wertz, Chemistry--A Molecular Science, North Carolina State University, 2010, www.webassign.net/resources/ wertzm2010/pdf/CAMS%20ebook.pdf.

A. I. M. Ismail, (1) O. I. El-Shafey, (2) M. H. A. Amr, (3) and M. S. El-Maghraby (4)

(1) Geological Sciences Department, NRC, Dokki, Cairo 12622, Egypt

(2) Physical Chemistry Department, NRC, Dokki, Cairo 12622, Egypt

(3) Research Department, Trace Elements Lab, Chemistry Administration, 12 Ramsis Street, Cairo 11522, Egypt

(4) Refractories, Ceramics and Building Materials Department, NRC, Dokki, Cairo 12622, Egypt

Correspondence should be addressed to O. I. El-Shafey; olalolo2004@yahoo.com

Received 11 March 2014; Revised 29 June 2014; Accepted 10 July 2014; Published 29 October 2014

Academic Editor: Arthur P Schwab

Table 1: Chemical composition of the pumice determined by X-ray
fluorescence.

Oxides                wt.%

Si[O.sub.2]           70.97
Ti[O.sub.2]           00.14
[Al.sub.2][O.sub.3]   14.24
MnO                   0.140
MgO                   0.350
[Fe.sub.2][O.sub.3]   1.880
CaO                   1.370
[Na.sub.2]O           4.460
[K.sub.2]O            4.020
LOI                   2.410

Table 2: Physicochemical characteristics of the
pumice and zeolite [P.sub.1].

Characteristics              Pumice    Zeolite
                                      [P.sub.1]

Slurry pH                     6.0        9.0
[pH.sub.PZC]                  5.0        8.0
Bulk density, g/[cm.sup.3]    0.85       0.5
Moisture, %                   1.0        1.0
[S.sub.Bet], [m.sup.2]/g       31        40
[V.sub.p], [cm.sup.3]/g       0.01      0.02
[r.sub.p], [Angstrom]         2.0        .2

Table 3: Characteristic parameters and correlation coefficients of
the experimental data according to Langmuir and Freundlich equations
on zeolite at 25 [+ or -] 0.1[degrees]C.

Metal           Ionic          Electro
               radius *     negativity **
             ([Angstrom])

[Co.sup.+2]      1.88           1.88
[Cu.sup.+2]      1.30           1.90
[Fe.sup.+2]      1.83           1.83
[Cd.sup.+2]      1.69           1.69

Metal        Langmuir constant

             [K.sub.L]     b      Correlation   [K.sub.F]
              (mg/g)     (L/mg)   coefficient    (mg/g)
                                  ([R.sup.2])

[Co.sup.+2]    1.27      23.99       0.986        16.16
[Cu.sup.+2]    1.59      45.70       0.986        24.60
[Fe.sup.+2]    2.86      67.12       0.986        26.50
[Cd.sup.+2]    3.12      131.9       0.999        40.00

Metal        Freundlich constant

               n     Correlation
                     coefficient
                     ([R.sup.2])

[Co.sup.+2]  0.340      0.983
[Cu.sup.+2]  0.144      0.999
[Fe.sup.+2]  0.205      0.985
[Cd.sup.+2]  0.094      0.976

* Ionic radius (A) and ** electronegativity from [25].

Table 4: Kinetic parameters of sorption for the metal
ions onto zeolite at 25[degrees]C.

Metal         [q.sub.e exp]
              (mg/g)

[Co.sup.+2]       61.60
[Cu.sup.+2]       75.50
[Fe.sup.+2]       76.50
[Cd.sup.+2]       97.80

Metal         Pseudo-first-order

              [q.sub.e cal]     [K.sub.1]      [R.sub.1.sup.2]
                 (mg/g)       ([min.sup.-1])

[Co.sup.+2]       10.06          -0.3705           0.8357
[Cu.sup.+2]       10.24          -0.6458           0.8170
[Fe.sup.+2]       16.76          -0.5954           0.7651
[Cd.sup.+2]       35.45          -0.7452           0.8337

Metal         Pseudo-second-order

              [q.sub.e cal]  [K.sub.2]    [R.sup.2.sub.2]
                 (mg/g)      (g/mg min)

[Co.sup.+2]      61.95         0.2326         0.9999
[Cu.sup.+2]      77.57         0.1123         0.9994
[Fe.sup.+2]      80.05         0.0274         0.9999
[Cd.sup.+2]      98.32         0.2650            1
COPYRIGHT 2014 Hindawi Limited
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2014 Gale, Cengage Learning. All rights reserved.

 
Article Details
Printer friendly Cite/link Email Feedback
Author:Ismail, A.I.M.; Shafey, O.I. El-; Amr, M.H.A.; Maghraby, M.S. El-
Publication:International Scholarly Research Notices
Article Type:Report
Date:Jan 1, 2014
Words:6054
Previous Article:Symbiotic efficiency of native rhizobia nodulating common bean (Phaseolus vulgaris L.) in soils of Western Kenya.
Next Article:Global stability of an HIV-1 infection model with general incidence rate and distributed delays.