Nb-Doped Ti[O.sub.2] Photocatalysts Used to Reduction of C[O.sub.2] to Methanol.

1. Introduction

The development of photocatalysis began in 1972 [1], aiming to create efficient water treatment systems and to produce [H.sub.2] to use as fuel. Various researchers have conducted investigations in many different fields, such as semiconductor photoelectrochemistry [2], photocatalysis [3, 4], and photoreduction of C[O.sub.2] in aqueous environments, to produce methanol [5]. The Ti[O.sub.2] produced by Evonik, known as Ti[O.sub.2]-P25 (consisting of 75% anatase phase and 25% rutile phase), is the mostly used for this purpose due to its excellent photoactivity and is also used as a reference to compare results with others news materials. Ti[O.sub.2]-P25 has high surface area (~50[m.sup.2]/g), and its complex crystalline microstructure is directly related to the synthesis method [6].

The photocatalysis process consists in the exposition of semiconductor powder to ultraviolet light radiation which will create then the electron-hole pair from the electronic excitation. The hole ([h.sup.+]) is formed in the valence band, and the electrons ([e.sup.-]) are formed in the conduction band. These species can react with adsorbed water or hydroxyl group and produce hydroxyl (O[H.sup.*]) radical and superoxide anion ([O.sup.*-.sub.2]) radical, starting an oxidation and reduction process and then degrading the component of interest [7-9].

The addition of transitional metals to Ti[O.sub.2] seeks to increase the recombination time of electron/hole pair during electronic excitation [10, 11]. It is believed that these transitional metals create acceptor/donator electron centers, influencing the electronic recombination. Perazolli et al. [12] synthesized a ternary mixture of Ti, Sn, and Ag oxides that obtained better Rhodamine B discoloration results than P25 due to the heterojunction Ti[O.sub.2]/Sn[O.sub.2] and formation of metallic Ag reduced from [Ag.sub.2]O increasing the recombination time. The utilization of heterostructures has been studied in degradation of organic compounds. Through the solvothermal synthesis, Li et al. [13] synthesized pure anatase, pure rutile, and mixed anatase-rutile cake-like particles and observed that anatase-rutile particles reached higher photocatalytic activity compared to powders of pure phases (anatase and rutile) and also higher than P25. In the work of Zhou et al. [14], heterostructures of CdS/Ti[O.sub.2] were synthesized in different concentrations (wt.) of CdS and then used in degradation of methyl orange dye. It was observed that the photocatalyst of concentration 2% (wt.) reached total degradation of dye in 75 minutes, a higher activity when compared to pure Ti[O.sub.2] that reached only 90% of degradation at the same time, showing that the heterojunction promotes better charge separation and increases the recombination time of electron-hole pairs ([e.sup.-]/[h.sup.+]). Through the hydrothermal synthesis, Tao et al. [15] deposited the heterostructures of Ti[O.sub.2]/ZnO/Ag on FTO substrate where [Ag.sup.0] acts like antennae capturing the electrons photogenerated and then increased the recombination time for improving the degradation of methyl orange dye. The photocatalyst Ti[O.sub.2]/ZnO/Ag reached 96% of degradation of dye in 120 minutes, better than the results of pure Ti[O.sub.2] (46%) and of Ti[O.sub.2]/ZnO heterostructure (62%) at same conditions.

Research of efficient processes in the conversion of C[O.sub.2] into methanol, ethanol, C[H.sub.4], [H.sub.2], and other compounds has been made since the late 1980s [16]. The use of Pd as a dopant in Ti[O.sub.2] was evaluated on C[O.sub.2] hydrogenation under UV irradiation generating the amount of 355.62 [micro]mol C[H.sub.4]/g-cat by the increase of recombination time of generated electrons and adsorption and activation of C[O.sub.2] molecules on surface of catalyst [17]. Cheng et al. [18] used [Cu.sup.2+]-Ti[O.sub.2] nanorod thin film photocatalysts reducing C[O.sub.2] into methanol and ethanol obtaining, respectively, 36.18 [micro]mol/g-cat x h and 79.13 [micro]mol/g x cat-h in which [Cu.sup.2+] acted as active sites of electron traps and could suppress the electron-hole recombination allied to high surface area of Ti[O.sub.2] nanorods. Pan et al. [19] produced Pt nanoparticle-dispersed gallium oxide (Pt/[Ga.sub.2][O.sub.3]) catalysts calcined in different atmospheres at 600[degrees]C in comparison with Pt/P25; the oxygen vacancies promoted better C[O.sub.2] adsorption leading more efficient separation of the photo-induced electron-hole pairs and reaching 2.1 and 1.9 [micro]mol C[H.sub.3]OH using Pt/[Ga.sub.2][O.sub.3] and Pt/P25, respectively.

The use of a substituent that has a higher electron valence number than [Ti.sup.4+], as [Nb.sup.5+] an example, can lead to a level of electron donation that behaves like an extrinsic n-type semiconductor, which can act in the photoreduction reaction. One way to introduce the elements of the Ti[O.sub.2] ceramic matrix in order to improve the photocatalytic properties by substitution of [Ti.sup.4+] cation for [Nb.sup.5+] is the chemical synthesis through Pechini's method. This method is useful to obtain ceramic powders since it is possible to control parameters as composition and crystalline phase through the immobilization in a complex organic matrix and controlled calcination, decreasing the segregation of metals and then providing homogenous distribution of the components [20,21]. The sputtering method is a powerful tool of deposition of metals on surfaces and can be used in superficial modification of catalysts improving optical and electrical properties [22, 23].

Brazil has the biggest reserve of niobium of the world, possessing 98% of world niobium ore reserves [24]. This work chose niobium due to the abundance and low cost of niobium ([Nb.sub.2][O.sub.5], [Nb.sup.0]) allied with the advantages brought with the structural modification by doping (n-type extrinsic semiconductor/excess of electrons and defects generation) and superficial modification (oxygen vacancies and formation of antennae) both improving charge separation and increasing the electron-hole pair recombination time. The goal of this research was to synthesize and characterize Ti[O.sub.2]-based photocatalytic powders modified with Nb in two ways: into the crystalline structure [Nb.sup.4+] (by chemical synthesis Pechini) and upon the surface [Nb.sup.0] (through sputtering deposition), as well as aiming at improving the photocatalyst properties by combining these two methods (the novelty). The concentration of dopants from 0.0 to 2.5% (w/w) was adopted to guarantee the formation of a solid solution and avoid the appearance of other phases [25]. It also intended to verify the photocatalytic activity of these powders in the reduction of C[O.sub.2] to methanol.

2. Experimental

2.1. Synthesis of Photocatalytic Powders. In this work, we prepared two polymer precursor solutions through the Pechini method:

(a) The titanium polymeric solution was obtained by slow addition of titanium isopropoxide (Aldrich) in ethylene glycol (Synth) at 80[degrees]C with constant stirring, then the heating was raised to 110[degrees]C, and the citric acid (Carlo Erba) was added. The molar ratio for the preparation of this stock titanium solution was 1:4:16 (metal: citric acid: ethylene glycol).

(b) The niobium polymeric solution was obtained by dissolution of niobium oxide ([Nb.sub.2][O.sub.5]) (Carlo Erba) in hydrofluoric acid aqueous solution under stirring and heating (80[degrees]C). The pH of the solution was increased to 8 by addition of ammonium hydroxide (Synth), causing precipitation as hydroxide of niobium [Nb[(OH).sub.5]]. The precipitate was washed with distilled water to eliminate fluoride ions ([F.sup.-]) until the test with calcium carbonate (CaC[O.sub.3]) to give negative fluoride ions. The niobium hydroxide was dissolved in aqueous solution of citric acid under stirring and heating ([+ or -]80[degrees]C), followed by addition of ethylene glycol. The molar ratio for the preparation of stock niobium solution was 1 : 4 : 16 (metal: citric acid: ethylene glycol) [26]. The niobium and titanium solutions were standardized gravimetrically at 900[degrees]C for 2 hours.

After preparation of polymeric solutions, new solutions were obtained from the mixture of the previously prepared solutions according to addition of niobium: 0,0.5,1, and 2.5% (w/w) and then submitted to calcination in a muffle furnace at 500[degrees]C for 1 hour and milling by 500 rpm for 1 hour.

For superficial decoration by deposition of [Nb.sup.0] through sputtering, circular pellets of 1.0 g of each powder were prepared using a hydraulic press (BOVENAU-P15500) applying a load of 2500 kg for 5 minutes and then introduced into the deposition chamber of sputtering (Sorensen DCS 600-1.7) for deposition according to the following conditions: metallic spherical target of niobium, time of deposition of 10 minutes, vacuum of 2 x [10.sup.-3] torr with argon gas plasma, potential of 370 V, and a current of 0.055 A [27]. The pellets were macerated into powders again and submitted to heat treatment at 500[degrees]C for 1 hour promoting a more effective adhesion of the metallic Nb particles on Ti[O.sub.2] surface obtaining the powders modified superficially by sputtering.

2.2. Sample Characterization. The powders were analyzed utilizing TGA/DTA (Netszch Thermische Analyse-STA 409) to evaluate the temperature in which all organic matter can be removed. Furthermore, phase transits from anatase to rutile could be detected using this method.

In order to investigate the crystallinity of the material and identify the present phases, X-ray Diffraction (XRD) and the Rietveld method (XRD-Rigaku Rint-2000) with radiation source of copper emission line (Cu K[alpha], [lambda] = 0.154 nm) and voltage acceleration of 42 kV, 120 mA current, and scan rate of 2[theta] [min.sup.-1] were used.

The Raman spectroscopy was adopted to evaluate the different phases present in the powders utilizing HORIBAHR 800, with laser 632.8 nm. Infrared spectroscopy measurements were made in Shimadzu FTIR 8300 using the transmission technique (resolution: 4 [cm.sup.-1], spectral range: 4000 to 400 [cm.sup.-1], and 50 scans). The XPS technique (UNISPECS UHV) was used to analyze surface changes in the chemical composition due to the substitution to Nb.

The spectrophotometer Varian Cary model 500 was used for quantification of the bandgap values. The SBET technique was used to verify the specific surface area (Micrometrics ASAP 2010). The particle size of the powder and its morphology were evaluated in a field emission scanning electron microscopy (FE-SEM JEOL 7500F model).

2.3. Photocatalytic Activity. The photocatalytic activity of reduction was carried in a reactor (Heraeus) made out of quartz tube housing for the cooling of the mercury UV lamp of 150 W. In this reactor, a magnetic stirrer, a C[O.sub.2] bubbling tube, an inlet and outlet for water cooling, and a sample collector tube were coupled as illustrated in Figure 1.

The volume of 700 mL of deionized water was used, and the pH was increased to 12 with NaOH. Previously a blank test (photolysis) was made using no photocatalyst, and posteriorly in each solution, 0.350 g [28] of each photocatalytic powder was added and the reactions had the duration of 6 hours with removal of aliquots every 30 min that were analyzed through gas chromatography (GC-FID) in the chromatograph Varian CP-3800 with a flame ionization detector in column (Stabilvax-Restec 30 m, 0.25 mm inner diameter) using the technique SPME (solid phase microextraction) that adsorbs volatile organic compounds of aqueous samples on fiber (75 [micro]m Carboxen/PDMS, SUPELCO) by heating (headspace method) and flow rate [N.sub.2] 1.0m L x [min.sup.-1]. To quantify the methanol in the samples, aliquots of 0.5 mL were transferred to 1.5 mL vial and heated for 7 minutes, then the fiber was exposed to the vapor formed for 5 minutes to promote deadsorption, and finally, the fiber was injected into GC.

3. Results and Discussion

3.1. TG/DTA Characterization. Figure 2 showed the results from the photocatalytic powder Nb-Ti[O.sub.2] with 2.5% Nb (w/w). The TG curve of the precalcined powder ("puff") Nb-Ti[O.sub.2] with 2.5% Nb (w/w) showed a weight loss at two distinct times. The first loss occurred between 30[degrees]C and 120[degrees]C and represented 4% of the initial weight and was attributed to water loss. The second loss, 40% of initial weight, was observed between 250[degrees]C and 480[degrees]C and was attributed to the calcination of organic precursors (citrates). There was no significant mass variation over 500[degrees]C. The DTA curve showed two significant thermal events, represented at first by an endothermic peak of around 100[degrees]C and characteristic of dehydration of the sample, and secondly by an exothermic peak at 413[degrees]C, attributed to the decomposition of organic matter. Therefore, in this experiment, the final temperature of 500[degrees]C was adopted because it guarantees total elimination of organic matter in the powders.

3.2. XRD and Rietveld Characterization. The XRD (Figure 3) indicates that the photocatalytic powders are mainly made of the anatase crystalline phase in comparison to characteristic peaks reported in the standard (R) JCPDS-73-1764. However, a peak at 2[theta] = 27.5[degrees], characteristic of the rutile crystalline phase, was observed. This confirms their presence due to the applied calcination temperature of 500[degrees]C, which is sufficient to cause partial phase transition to the rutile phase.

Another fact observed in the XRD patterns was the gradual shrinkage of all of the peaks with increase of Nb concentration in Ti[O.sub.2] powder, attributed to the substitution of Nb in the Ti[O.sub.2] crystalline lattice. Thus, considering the peak 2[theta] = 48[degrees] plane (2 0 0), it is found that the surface modification did not change the results obtained by XRD. Another effect observed by increasing the concentration of Nb was the leftward shift of the [DELTA]2[theta][degrees] peaks. These were justified by the distortion in the crystalline Ti[O.sub.2] lattice generated by vacancies, interstitials, and substitutions [10] and by the difference of cationic rays in [Ti.sup.4+] (0.74 A) substituted by [Nb.sup.4+] (0.82 A), which reinforces the results observed in the TG/DTA analysis described previously.

Figure 4 illustrates the refined XRD pattern through the Rietveld method which can be observed beyond the XRD curves. The overlapping calculated setting curves show the positions of the Bragg peaks in the rutile and anatase crystalline phases in the samples and, further below, the residual adjustments.

The results obtained by Rietveld and shown in Table 1 indicate that the percentages of the anatase phase increased from 91.76% to 98.27% in photocatalytic powders Nb-Ti[O.sub.2] 0.0% (w/w) and Nb-Ti[O.sub.2] 2.5% (w/w), respectively. The percentage of the rutile phase decreased from 8.24% to 1.73%, indicating that the increase in the concentration of Nb in the photocatalytic powders acts as a rutile phase inhibitor.

Considering the change in values of cell parameters (a, b, c) of anatase and rutile crystals that was caused by the replacement of Ti for Nb and comparing them to the Nb-Ti[O.sub.2] photocatalyst 0.0% (w/w), which does not contain Nb, it was observed that there is a decrease in cell volume ranging from 133.74 [[Angstrom].sup.3] to 133.53 [[Angstrom].sup.3] in Nb-Ti[O.sub.2] 0.5 Nb% (w/w) and Nb-Ti[O.sub.2] 2.5% Nb (w/w), respectively. This implies that Nb substituted in octahedral sites of this phase promotes the compression of the individual cell.

3.3. IR and Raman Characterization. The results obtained by IR spectroscopy (Figure 5) indicated that the photocatalytic powders show characteristic bands (3450 and 1640 [cm.sup.-1]) attributed to the presence of water in atmospheric humidity. The O-Ti-O bonds are attributed to strong band at 979 [cm.sup.-1] and the Ti-O-Ti bonds to weak band at the range of 800-465 [cm.sup.-1]. These bands are characteristics of the Ti[O.sub.2]based photocatalysts. It was also observed that the presence of C[O.sub.2] at 2349 and 1337 [cm.sup.-1] and CO at 2070 [cm.sup.-1] is due to the capacity of the photocatalytic powders to adsorb some compounds that come from the decomposition of organic precursors present in the "puff," adsorbed in the calcination process. The comparison of the photocatalytic powders and commercial anatase Ti[O.sub.2] powder in IR analysis confirms that all organic matter was eliminated after heat treatment.

Figure 6 illustrates the Raman spectra of the photocatalytic powders. It is possible to notice that the characteristic peaks matched the theoretical frequencies of Ti[O.sub.2] anatase and that these results also matched with the XRD diffractograms. In contrast, there was a reduction in the intensity of the characteristic peaks at 395, 515, and 638 [cm.sup.-1], respectively, while the concentration of Nb increased in the photocatalytic powders. This indicated the incorporation of Nb into the Ti[O.sub.2] lattice, which confirmed the results obtained by XRD and Rietveld.

3.4. Diffuse Reflectance and SBET Characterization. The results of diffuse reflectance spectroscopy using Tauc extrapolation [29] showed values from 3.33 eV to 3.38 eV for the photocatalytic powders Nb-Ti[O.sub.2] 0.0% (w/w) and Nb-Ti[O.sub.2] 2.5% (w/w), respectively, indicating that the addition of Nb to the Ti[O.sub.2] lattice did not increase the bandgap value significantly. The diffuse reflectance results of all photocatalytic powders analysed were similar and close to the value of 3.38 eV, which indicates that the photocatalytic powders modified through sputtering did not able to promote and/or increase the formation of new defects near the conduction band of the photocatalysts when compared with the photocatalysts not modified through sputtering [30] (Figure 7).

The SBET surface area results for the photocatalytic powders are shown in Table 2. The results indicate a gradual increase from 22.6 to 31.6 [m.sup.2] x [g.sup.-1] in photocatalytic powders Nb-Ti[O.sub.2] 0.0% Nb (w/w) to Nb-Ti[O.sub.2] 2.5% Nb (w/w), respectively. A similar behavior was observed in photocatalytic powders modified by deposition of [Nb.sup.0] through sputtering. A slight increase in the surface area of photocatalytic powders was observed, which is justified by the presence of deposited [Nb.sup.0], which can act as a deagglomerator of particles due to the electrostatic repulsion effect, which increases the surface area.

3.5. SEM Characterization. The SEM images obtained of the photocatalytic powder Nb-Ti[O.sub.2] 0.0% Nb (w/w) without modification, by deposition of [Nb.sup.0] through sputtering, are illustrated in Figure 8. All the compositions (with or without surface modification) showed similar microstructures. It was found that the photocatalytic powders are formed by plates of irregular shapes and sizes, ranging from 1 to 7 [micro]m as seen in Figure 8(a). They are composed of clusters of rounded particles with diameters between 11.3 and 16.2 nm, as shown in Figure 8(b).

3.6. XPS Characterization. The XPS technique was used to analyze the chemical surface structure of the photocatalytic powders and verify changes in chemical composition that happened due to the substitution of Ti for Nb. In the XPS spectra on the [Ti.sub.2p] transition, Figure 9(a), the oxidation state of titanium [Ti.sup.4+] is represented by the characteristic peak of [Ti.sub.2p] (458.5 eV) and the Nb substitution not resulted in modification of the Ti[O.sub.2] oxidation original state. Regarding Nb (Figure 9(b)) represented by characteristic peaks Nb[O.sub.2 3d3/2]-[Nb.sup.4+] in 209.5 eV, Nb[O.sub.2 3d5/2]-[Nb.sup.4+] in 206.7 eV, and [Nb.sub.2][O.sub.5] in 207.4 [+ or -] 0.4 eV, it was observed that the oxidation state of niobium in the photocatalytic powders is [Nb.sup.4+]. However, this paper was based on the fact that the Nb replaced in the Ti[O.sub.2] crystalline lattice is found in the oxidation state 5+. If that should happen, an electron donor level could be generated in the forbidden region of the bandgap, which would be easily removed, becoming a free electron promoted and used in the reaction of C[O.sub.2] reduction.

The substitution of [Ti.sup.4+] for [Nb.sup.5+] is a subject for further studies which will evaluate the influence of temperatures higher than 500[degrees]C in the presence of an oxidizing atmosphere and the Nb oxidation state behavior replaced by Ti[O.sub.2] lattice. Furthermore, the phase transition anatase/rutile seeking favorable conditions for the formation of [Nb.sup.5+] and avoiding the formation of the rutile crystalline phase as much as possible will be observed.

3.7. C[O.sub.2] Reduction Assays. The results of the C[O.sub.2] reduction and the formation of methanol, as shown in Table 3, indicate that the addition of structural Nb favored the formation of methanol. It was found that the photocatalytic powder Nb-Ti[O.sub.2] 0.0% Nb (w/w) did not promote the formation of methanol, and the surface modification through sputtering showed lower results in comparison with the powders not modified by this technique. The concentrations of methanol obtained can be explained by XPS wherein Nb replaced was [Nb.sup.4+] instead of [Nb.sup.5+]. If the replacement by [Nb.sup.5+] occurs in the lattice of Ti[O.sub.2], this replacement can lead to a level of electron donation that could be used in reduction reaction; however, the substitution by [Nb.sup.4+] can act in the reduction reaction in the same way, but with lower activity expected, once there is no remaining electron. The concentration of methanol formed is directly proportional to the Nb concentration in the powders, and the formation of methanol is due to the presence of Nb in the lattice of Ti[O.sub.2]. Concerning the formation of metallic antennae, the reaction of reduction occurs in some preferential sites, and those sites can be covered by the sputtered antennae decreasing photocatalytic activity and the methanol formation when compared with same powders not modified through sputtering. The yield of methanol reached by catalyst Nb-Ti[O.sub.2] 2.5% (w/w) (1.00 [micro]mol/g-cat x h) is superior in comparison with all the catalysts but P25 (1.83 [micro]mol/g-cat-h), demonstrating the doping with [Nb.sup.4+], has potential effect in formation of defects which increases the electron-hole pair recombination time improving the catalytic properties of Ti[O.sub.2].

As discussed above, the formation of methanol is directly proportional to Nb concentration which can open new promising researches to investigate higher concentrations (above 2.5%) of Nb that can reach yields of methanol equal or higher than P25.

4. Conclusions

We obtained nanostructured Ti[O.sub.2] photocatalytic powders structurally modified with Nb using the Pechini method and superficially modified with [Nb.sup.0] through sputtering. The photocatalytic powders are mainly formed by the anatase phase of Ti[O.sub.2]. Utilizing the Rietveld technique, the [DELTA]2[theta][degrees] displacement peaks, observed by the XRD measurement, confirmed the replacement of Ti for Nb in the Ti[O.sub.2] lattice. Using SEM, the experiment investigated the morphology of the photocatalytic powders, which were arranged in plates formed by nanosized particles. The SBET technique showed that the surface area of the photocatalytic powders tends to increase with the concentration of Nb. Followed by the reduction of agglomerate formation. The diffuse reflectance technique quantified the average value of bandgap at 3.35 eV. The XPS indicated that the oxidation state of Ti and Nb in the photocatalytic powders is 4+. The substitution to [Nb.sup.0] through sputtering does not increase photoactivity compared to photocatalytic powders with the same concentration of Nb not modified through sputtering. This is justified by the metallic particles of Nb that assist in the transportation of photogenerated electrons. The formation of methanol was proved by GC-FID in which concentrations up to 1.00 [micro]mol/g-cat x h were obtained by the replacement of [Ti.sup.4+] by [Nb.sup.4+] in the lattice of Ti[O.sub.2]. Future investigations about higher concentrations of Nb can lead to reach yields of methanol equal or higher than P25.

https://doi.org/10.1155/2018/7326240

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

The authors thank the LMA-IQ for providing the FEG-SEM facilities and also thank the Brazilian research funding agencies CAPES, CNPq, and FAPESP (2008/544136-R) and FAPESP-CDMF (2013/07296-2) for providing the financial support of this research project.

References

[1] A. Fujishima and K. Honda, "Electrochemical photolysis of water at a semiconductor electrode," Nature, vol. 238, no. 5358, pp. 37-38, 1972.

[2] Q. Gui, Z. Xu, H. Zhang et al., "Enhanced photoelectrochemical water splitting performance of anodic Ti[O.sub.2] nanotube arrays by surface passivation," ACS Applied Materials & Interfaces, vol. 6, no. 19, pp. 17053-17058, 2014.

[3] G. L. Chiarello, A. Zuliani, D. Ceresoli, R. Martinazzo, and E. Selli, "Exploiting the photonic crystal properties of Ti[O.sub.2] nanotube arrays to enhance photocatalytic hydrogen production," ACS Catalysis, vol. 6, no. 2, pp. 1345-1353, 2016.

[4] M. Nolan, A. Iwaszuk, A. K. Lucid, J. J. Carey, and M. Fronzi, "Design of novel visible light active photocatalyst materials: surface modified Ti[O.sub.2]," Advanced Materials, vol. 28, no. 27, pp. 5425-5446, 2016.

[5] T. E. Rosser, C. D. Windle, and E. Reisner, "Electrocatalytic and solar-driven C[O.sub.2] reduction to CO with a molecular manganese catalyst immobilized on mesoporous Ti[O.sub.2]," Angewandte Chemie, vol. 128, no. 26, pp. 7514-7518, 2016.

[6] T. Ohno, K. Sarukawa, K. Tokieda, and M. Matsumura, "Morphology of a Ti[O.sub.2] photocatalyst (Degussa, P-25) consisting of anatase and rutile crystalline phases," Journal of Catalysis, vol. 203, no. 1, pp. 82-86, 2001.

[7] M. F. Abdel-Messih, M. A. Ahmed, and A. S. El-Sayed, "Photocatalytic decolorization of Rhodamine B dye using novel mesoporous Sn[O.sub.2]-Ti[O.sub.2] nano mixed oxides prepared by sol-gel method," Journal of Photochemistry and Photobiology A: Chemistry, vol. 260, pp. 1-8, 2013.

[8] S. M. Lam, J. C. Sin, A. Z. Abdullah, and A. R. Mohamed, "Degradation of wastewaters containing organic dyes photocatalysed by zinc oxide: a review," Desalination and Water Treatment, vol. 41, no. 1-3, pp. 131-169, 2012.

[9] J. C. Sin, S. M. Lam, A. R. Mohamed, and K. T. Lee, "Degrading endocrine disrupting chemicals from wastewater by Ti[O.sub.2] photocatalysis: a review," International Journal of Photoenergy, vol. 2012, Article ID 185159, 23 pages, 2012.

[10] H. Jaafar, Z. A. Ahmad, and M. F. Ain, "Effect of Nb-doped Ti[O.sub.2] photoanode using solid state method with E. conferta as sensitizer on the performance of dye sensitized solar cell," Optik-International Journal for Light and Electron Optics, vol. 144, pp. 91-101, 2017.

[11] L. Matejova, M. Sihor, J. Lang et al., "Investigation of low Ce amount doped-Ti[O.sub.2] prepared by using pressurized fluids in photocatalytic [N.sub.2]O decomposition and C[O.sub.2] reduction," Journal of Sol-Gel Science and Technology, vol. 84, no. 1, pp. 158-168, 2017.

[12] L. Perazolli, G. F. Pegler, M. R. A. Silva, R. A. F. Ingino, and J. A. Varela, "High activity photocatalyst powder formed by three ceramic oxides," Advances in Science and Technology, vol. 65, pp. 184-193, 2010.

[13] J. Li, X. Xu, X. Liu, W. Qin, M. Wang, and L. Pan, "Metalorganic frameworks derived cake-like anatase/rutile mixed phase Ti[O.sub.2] for highly efficient photocatalysis," Journal of Alloys and Compounds, vol. 690, pp. 640-646, 2017.

[14] P. Zhou, Z. Le, Y. Xie, J. Fang, and J. Xu, "Studies on facile synthesis and properties of mesoporous CdS/Ti[O.sub.2] composite for photocatalysis applications," Journal of Alloys and Compounds, vol. 692, pp. 170-177, 2017.

[15] J. Tao, Z. Gong, G. Yao et al., "Enhanced optical and photocatalytic properties of Ag quantum dots-sensitized nanostructured Ti[O.sub.2]/ZnO heterojunctions," Journal of Alloys and Compounds, vol. 688, pp. 605-612, 2016.

[16] I. Ganesh, "Conversion of carbon dioxide into methanol-a potential liquid fuel: fundamental challenges and opportunities (a review)," Renewable and Sustainable Energy Reviews, vol. 31, pp. 221-257, 2014.

[17] N. Li, M. Liu, B. Yang et al., "Enhanced photocatalytic performance toward C[O.sub.2] hydrogenation over nanosized Ti[O.sub.2]-loaded Pd under UV irradiation," Journal of Physical Chemistry C, vol. 121, no. 5, pp. 2923-2932, 2017.

[18] M. Cheng, S. Yang, R. Chen, X. Zhu, Q. Liao, and Y. Huang, "Copper-decorated Ti[O.sub.2] nanorod thin films in optofluidic planar reactors for efficient photocatalytic reduction of C[O.sub.2]," International Journal of Hydrogen Energy, vol. 42, no. 15, pp. 9722-9732, 2017.

[19] Y. X. Pan, Z. Q. Sun, H. P. Cong et al., "Photocatalytic C[O.sub.2] reduction highly enhanced by oxygen vacancies on Ptnanoparticle-dispersed gallium oxide," Nano Research, vol. 9, no. 6, pp. 1689-1700, 2016.

[20] G. M. M. M. Lustosa, J. P. C. Costa, L. A. Perazolli, B. D. Stojanovic, and M. A. Zaghete, "Electrophoretic deposition of (Zn, Nb)Sn[O.sub.2]-films varistor superficially modified with [Cr.sup.3+]," Journal of the European Ceramic Society, vol. 35, no. 7, pp. 2083-2089, 2015.

[21] M. P. Pechini, "Method of preparing lead and alkaline titanates and niobates and coating method using the same to form a capacitor," US Patent 3330697, 1967.

[22] K. Safeen, V. Micheli, R. Bartali et al., "Synthesis of conductive and transparent Nb-doped Ti[O.sub.2] films: role of the target material and sputtering gas composition," Materials Science in Semiconductor Processing, vol. 66, pp. 74-80, 2017.

[23] A. V. Manole, M. Dobromir, M. Girtan, R. Mallet, G. Rusu, and D. Luca, "Optical properties of Nb-doped Ti[O.sub.2] thin films prepared by sol-gel method," Ceramics International, vol. 39, no. 5, pp. 4771-4776, 2013.

[24] E. E. Nikishina, D. V. Drobot, and E. N. Lebedeva, "Niobium and tantalum: state of the world market, application fields, and sources of raw materials. Part 2," Russian Journal of NonFerrous Metals, vol. 55, no. 2, pp. 130-140, 2014.

[25] X. Cheng, Z. Li, and J. Wu, "Colossal permittivity in ceramics of Ti[O.sub.2] Co-doped with niobium and trivalent cation," Journal of Materials Chemistry A, vol. 3, no. 11, pp. 5805-5810, 2015.

[26] P. D. Spagnol, J. A. Varela, M. A. Z. Bertochi, B. D. Stojanovic, and S. M. Tebcherani, "Effect of precursor solution on the formation of perovskite phase of Pb([Mg.sub.1/3][Nb.sub.2/3])[O.sub.3] thin films," Thin Solid Films, vol. 410, no. 1-2, pp. 177-182, 2002.

[27] C. J. Tavares, M. V. Castro, E. S. Marins et al., "Effect of hot-filament annealing in a hydrogen atmosphere on the electrical and structural properties of Nb-doped Ti[O.sub.2] sputtered thin films," Thin Solid Films, vol. 520, no. 7, pp. 2514-2519, 2012.

[28] I. Tseng, W. Chang, and J. C. S. Wu, "Photoreduction of C[O.sub.2] using sol-gel derived titania and titania-supported copper catalysts," Applied Catalysis B: Environmental, vol. 37, no. 1, pp. 37-48, 2002.

[29] D. L. Wood and J. Tauc, "Weak absorption tails in amorphous semiconductors," Physical Review B, vol. 5, no. 8, pp. 3144-3151, 1972.

[30] A. Kubacka, G. Colon, and M. Fernandez-Garcia, "Cationic (V, Mo, Nb, W) doping of Ti[O.sub.2]-anatase: a real alternative for visible light-driven photocatalysts," Catalysis Today, vol. 143, no. 3-4, pp. 286-292, 2009.

M. V. Nogueira (iD), (1) G. M. M. M. Lustosa, (1) Y. Kobayakawa, (2) W. Kogler, (3) M. Ruiz, (1) E. S. Monteiro Filho, (1) M. A. Zaghete, (1) and L. A. Perazolli (iD) (1)

(1) Instituto de Qumica de Araraquara, UNESP, Araraquara, SP, Brazil

(2) Tokyo University of Science, Tokyo, Japan

(3) Friedrich-Alexander University Erlangen-Nurnberg, Erlangen, Germany

Correspondence should be addressed to M. V. Nogueira; tcep1@hotmail.com

Received 13 June 2017; Revised 26 September 2017; Accepted 15 October 2017; Published 2 April 2018

Academic Editor: Fernando Lusquinos

Caption: Figure 1: Design of the photocatalytic reactor.

Caption: Figure 2: TG/DTA curves of precalcined Ti[O.sub.2] photocatalyst Nb-Ti[O.sub.2] 2.5% Nb (w/w).

Caption: Figure 3: XRD patterns of photocatalytic powders modified by deposition of [Nb.sup.0] through sputtering (SPT) compared to the standard Ti[O.sub.2] rutile (R) JCPDS 78-1510 and Ti[O.sub.2] anatase (A) JCPDS 73-1764. Detail: 2[theta] = 48[degrees] plane (2 0 0) anatase.

Caption: Figure 4: XRD diffractogram refined by the Rietveld method for the photocatalyst powder Nb-Ti[O.sub.2] 2.5% Nb (w/w) without modification by deposition of [Nb.sup.0] through sputtering.

Caption: Figure 5: IR spectra of photocatalytic powders compared to commercial Ti[O.sub.2] anatase Synth powder: (a) Nb-Ti[O.sub.2]1% Nb (w/w), (b) Nb-Ti[O.sub.2] 2.5% Nb (w/w), (c) Nb-Ti[O.sub.2] 0% Nb (w/w), (d) Anatase Ti[O.sub.2], and (e) Nb-Ti[O.sub.2] 0.5% Nb (w/w).

Caption: Figure 6: Raman spectra of the photocatalytic powders modified by deposition of [Nb.sup.0] through sputtering (A, anatase; R, rutile peaks).

Caption: Figure 7: Bandgap (Tauc extrapolation) graph of Nb-Ti[O.sub.2] 2.5% Nb (w/w) photocatalytic powder.

Caption: Figure 8: SEM images of photocatalytic powder Nb-Ti[O.sub.2] 0.0% Nb (w/w) without modification by deposition of [Nb.sup.0] through sputtering. Different magnifications.

Caption: Figure 9: XPS spectra of Nb-Ti[O.sub.2] 2.5% Nb (w/w) photocatalyst: (a) Ti2p peaks and (b) Nb[O.sub.2] 3d3/2 Nb[O.sub.2 3d5/2] peaks.
Table 1: Anatase/rutile percentages and unit cell parameters
calculated for the powders.

Photocatalyst            Percentage
(% Nb (w/w))                                    Anatase

                     Anatase   Rutile     a       b       c

Nb-Ti[O.sub.2] 0.0    91.76     8.24    3.770   3.770   9.477
Nb-Ti[O.sub.2] 0.5    94.90     5.10    3.762   3.762   9.445
Nb-Ti[O.sub.2] 1.0    97.74     2.26    3.760   3.760   9.446
Nb-Ti[O.sub.2] 2.5    98.27     1.73    3.759   3.759   9.446

                          Cell parameter
Photocatalyst                                  Cell volume
(% Nb (w/w))                 Rutile          [[Angstrom].sup.3]

                       a       b       c     Anatase   Rutile

Nb-Ti[O.sub.2] 0.0   4.580   4.581   2.951   134.74    61.95
Nb-Ti[O.sub.2] 0.5   4.582   4.582   2.952   133.70    61.99
Nb-Ti[O.sub.2] 1.0   4.589   4.589   2.943   133.58    62.00
Nb-Ti[O.sub.2] 2.5   4.581   4.581   2.955   133.53    62.04

Table 2: Surface area and average particle size of the synthesized
photocatalytic powders.

Photocatalyst                   SBET area           Average particle
(% Nb (w/w))              ([m.sup.2] x [g.sup.-1]       size (nm)

Nb-Ti[O.sub.2] 0.0%               22.6                     15
Nb-Ti[O.sub.2] 0.5%               23.4                     15
Nb-Ti[O.sub.2] 1.0%               32.6                     15
Nb-Ti[O.sub.2] 2.5%               31.6                     13

Photocatalyst                   SBET area           Average particle
(% Nb (w/w))              ([m.sup.2] x [g.sup.-1]       size (nm)

Nb-Ti[O.sub.2] 0.0% SPT            25.8                    15
Nb-Ti[O.sub.2] 0.5% SPT            28.2                    14
Nb-Ti[O.sub.2] 1.0% SPT            37.3                    14
Nb-Ti[O.sub.2] 2.5% SPT            37.2                    13

SPT: modification through sputtering.

Table 3: Methanol concentrations obtained, quantified by GC-FID.

Photocatalytic powder         Methanol yield
(% Nb (w/w))              ([micro]mol/g-cat x h)

Blank (photolysis)                  0
Nb-Ti[O.sub.2] 0.0%                 0
Nb-Ti[O.sub.2] 0.5%                0.54
Nb-Ti[O.sub.2] 1.0%                0.76
Nb-Ti[O.sub.2] 2.5%                1.00

Photocatalytic powder         Methanol yield
(% Nb (w/w))              ([micro]mol/g-cat x h)

P25                                1.83
Nb-Ti[O.sub.2] 0.0% SPT             0
Nb-Ti[O.sub.2] 0.5% SPT           <0.01
Nb-Ti[O.sub.2] 1.0% SPT            0.16
Nb-Ti[O.sub.2] 2.5% SPT            0.40
COPYRIGHT 2018 Hindawi Limited
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2018 Gale, Cengage Learning. All rights reserved.

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:Research Article
Author:Nogueira, M.V.; Lustosa, G.M.M.M.; Kobayakawa, Y.; Kogler, W.; Ruiz, M.; Filho, E.S. Monteiro; Zaghe
Publication:Advances in Materials Science and Engineering
Date:Jan 1, 2018
Words:6118
Previous Article:Utilization of Sandy Soil as the Primary Raw Material in Production of Unfired Bricks.
Next Article:Comparison of Asphalt Mixtures Designed Using the Marshall and Improved GTM Methods.