Morphology and magnetic properties of ferriferous two-phase sodium borosilicate glasses.

1. Introduction

The macroscopic physical properties of ultradispersed substances under confined geometry differ essentially from the properties of the bulk materials and have a real practical importance. Confined geometry has often been created using artificial or natural insulating porous matrices. The average diameter and topology of pore and wetting ability of embedded materials determine the sizes and spatial organization of embedded substances. But usually the porous matrix plays a passive role in formation of new properties of embedded material: it forms the confined geometry only and does not participate practically (except interface) in modification of macroscopic physical properties of nanostructured materials. On the other hand the utilization of active matrices with magnetic or ferroelectric properties makes it possible to produce a new type of nanocomposite material (NCM) with different spatially separated, but interacted, order parameters. These NCMs with coexisting magnetic and ferroelectric orderings (especially at room temperature) are very perspective materials for practical application and can be considered model objects for nanoferronics [1, 2]. The production of these new multifunctional NCMs is the global idea of our studies. As a magnetic matrix we are going to use the so-called magnetic porous glass obtained by chemical etching of two-phase sodium borosilicate glass doped by hematite ([alpha]-[Fe.sub.2][O.sub.3]). Here it is necessary to note that in this case the interface between both subsystems (ferroelectric and magnetic) can be very developed to support an observable interaction. We have studied the dielectric properties and crystal structure of twophase alkali borosilicate glasses with different weight concentration of hematite in the initial mixture, that is, 25%: Fe25, 20%: Fe20, and 15%: Fe15 [3, 4], and have shown that during the preparation of these matrices nanoparticles of magnetite ([Fe.sub.3][O.sub.4]) and the phase [beta]-[Fe.sub.2][O.sub.3] are formed from the hematite [alpha]-[Fe.sub.2][O.sub.3] added to the initial mixture. Analysis of X-ray high-resolution diffraction (XRD) data [3] has shown that the diffraction sizes of magnetite particles nonlinearly depend on the concentration of hematite in the initial melt: 161 [+ or -] 9 [Angstrom] in Fe15, 150 [+ or -] 5 [Angstrom] in Fe20, and 454 [+ or -] 6 [Angstrom] in Fe25. From phase analysis of diffraction patterns we have determined that Fe15 glasses contain 77 [+ or -] 6 wt.% and 23 [+ or -] 6 wt.% [beta]-[Fe.sub.2][O.sub.3] of total iron oxides concentration. In Fe25 glasses the admixture of [beta]-[Fe.sub.2][O.sub.3] has not exceeded 2 wt.% and in Fe20 glasses we have not observed any traces of [beta]-[Fe.sub.2][O.sub.3] phase. The diffraction size of [beta]-[Fe.sub.2][O.sub.3] nanoparticles within Fe15 glasses was 208 [+ or -] 10 [Angstrom] [3]. Magnetite ([Fe.sub.3][O.sub.4]) is the ferrimagnetic materials and we can expect the appearance of magnetic properties for these glasses, but for production of porous magnetic glasses it is necessary to have the two-phase structure of glasses consisting of interpenetrative silica skeleton and chemically unstable phase, which can be removed at chemical etching of two-phase glasses [5]. The formation of this two-phase structure has been produced by the special heat treatment of alkali borosilicate glasses on cooling [5, 6]. Therefore on the next stage we have studied the morphology and magnetic properties of these ferriferous alkali borosilicate glasses and their convenience for preparation of magnetic porous glasses (MPG). It is necessary to note that MPG are very interesting not only for preparation of multifunctional (ferroelectric and magnetic) nanocomposite materials but for various other applications as well such as biocompatible matrices for drag delivery [7, 8], for hyperthermia treatment of cancer [9], for tissue engineering and regeneration [10,11], and for immobilization of enzymes [12-14]. These matrices have potential application in spin electronic devices, high density magnetic data storage, and magnetic random access memory [15] on the basis of exchange bias effect 16].

2. Methods and Measurement Procedures

The ferriferous borosilicate glasses were produced in Grebenshchikov Institute of Silicate Chemistry (Russian Academy of Sciences) and were kindly given for study of their morphology and magnetic properties. After melting the produced glasses have been kept up at 550[degrees]C during 120 hours for phase separation. As a result of this process one can produce two-phase glasses in which the channels of chemically unstable phase have penetrated into a silica skeleton, but formerly this technology was used for production of conventional (nonmagnetic) porous alkali-borosilicate glasses [5, 6]. After cooling down to RT the glasses were cut and all samples were rectangular polished plates 10 x 10 x 2 [mm.sup.3]. The morphology and surface magnetic properties were measured using the atomic-force microscope (AFM) Attotube AFM1 including magnetic force microscopy (MFM) mode. Attotube AFM1 can operate in the temperature diapason 4-285 K and at applied magnetic field up to 9 T. At studies of surface topology we used the semicontact method and silicon needles with a curvature radius of 10 nm. In the MCM mode the silicon needles with 60 nm cobalt coating (coercive force 20-30 mT) and 20 nm chromium protective layer were used. In these measurements the total curvature radius was 90 nm for magnetic needles. For generation of MFM images we utilized two-pass method: at the first pass the surface topology was obtained (in semicontact mode); at the second pass the needle was lifted up and followed the trajectory obtained at the first pass. The distance "needle-sample" was kept at 100 nm during scanning and we measured the magnetic response only. So additionally to study of surface topology the images of surface magnetization distribution in the zero applied fields have been obtained. In applied magnetic fields the measurement procedure was the same. The images of inner glass structure have been studied by transmission electron microscopy (TEM) using replicas from the fresh chip. We have studied the surface magnetic response of these glasses using magnetic force microscopy at applied fields (-)[10.sup.3] Oe-4 x [10.sup.3] Oe at 4.2 K; the field dependencies of ferriferous glasses magnetization were measured at 4.2 K and in the diapason H (-)1.4 * [10.sup.5]-(+)1.4 * [10.sup.5] Oe in International Laboratory of High Magnetic Fields and Low Temperatures (Wroclaw, Poland) using vibration magnetometer and super-conducting magnet of Oxford Instrument.

3. Results and Discussion

3.1. Morphology. In Figure 1 the topography (left) and the magnetic response (right) at zero applied field and at room temperature for the Fe15, Fe20, and Fe25 are presented. In all topology images one can see the large agglomerates upthrusted from common background (right scale in nanometers on the left figures). A similar picture is characterized for two-phase glasses with drop structure [5, 6, 17]. The average size of these agglomerates increases at a growth of iron oxide concentration. We have estimated the average lateral sizes (230 [+ or -] 10 nm for Fe15, 450 [+ or -] 10 nm for Fe20, and 940 [+ or -] 10 nm and 500 [+ or -] 10 nm for Fe25) and average heights over a common background of agglomerates: 9 [+ or -] 2 nm, 27 [+ or -] 4 nm, and 57 [+ or -] 6 nm for the Fe15, Fe20, and Fe25, respectively. The drop structure is not suitable for production of porous glasses. It is necessary to have the glasses with two interconnected (or interpenetrated) phases: the first one is a so-called chemically unstable alkali-rich borate phase soluble in the hot acids; the second one is practically pure silica skeleton. The procedure of porous glasses preparation is described, for example, in the review [5, 6].

In Figure 2 the part of ACM image (1 x 1 [micro][m.sup.2]) for the Fe25 glass surface, where there is no agglomerates, is presented and one can see that the typical dendrite (for two interpenetrated phases) structure exists there. AFM results are confirmed by TEM data [18,19] presented on Figures 3(a), 3(b), and 3(c). The arrows in Figures 3(a) and 3(b) indicate the positions of large agglomerates formed in the drop structure. Simultaneously as it is easy to see in Figures 3(a) and 3(b) two interconnected phases are evidently present at samples. So we can believe that in these glasses there is a coexistence of drop phase and two interconnected (interpenetrated) phases and it is possible to use these materials for porous glass production.

3.2. Magnetic Properties. The distributions of magnetic response on surfaces of the Fe25, Fe20, and Fe15 glasses at zero applied magnetic field and at room temperature are presented in Figure 1, right column. The small dark and white regions corresponding to the different (resp., magnetization of magnetic cantilever) directions of magnetization are evidently observed. The positions of these magnetic anomalies coincide with locations of surface agglomerates, at which the several nearest magnetic anomalies with different magnetization direction correspond to common surface agglomerate. It means that these agglomerates have the magnetic properties and contain a magnetite really because [Fe.sub.3][O.sub.4] at room temperature demonstrates ferrimagnetic properties.

MFM image in Figure 4 presents the distribution of surface magnetization for the Fe25 glass at 4.2 K and at H = 4000 Oe. It is easy to see that at these conditions one monochromatic (dark) magnetic region corresponds to one surface agglomerate; that is, at H = 4000 Oe the magnetization of every magnetic anomaly orients itself along the applied magnetic field and every surface agglomerate becomes a magnetic monodomain. In case of the Fe25 glass the average lateral size of this monodomain is equal to 980 nm and practically agrees with the lateral size of agglomerates obtained from surface topology studies taking into account experimental uncertainties and resolution.

To study of magnetic switching at 4.2 K we have chosen three neighbor agglomerates on surface of the Fe25 glass and have recorded MCM images at variation of magnetic field induction in the diapason 4-(-) 1 x [10.sup.3] Oe (Figure 5). Initially the directions of magnetization of agglomerates and magnetic cantilever have coincided (left column from top to down) and the three dark areas have been present at the images. In diapason (-) 1-(-) 3 x [10.sup.2] mT we have observed the change of agglomerates color from dark to white--this process connects with the switching of magnetic cantilever. At subsequent increase of magnetic field these areas continue to change color fluently and at 750-900 Oe become dark finally. One can consider this value (750-900 Oe) to be an estimation of coercive force for the Fe25 glass.

The field dependence of the Fe20 glass magnetization has been measured at 4.2 K by vibration magnetometer and is presented in Figure 6. It is easy to see the presence of the hysteresis loop and a saturation of magnetization at fields above 10000 Oe. The same field dependence is typical for superparamagnetic system, in particular for Stoner-Wohlfarth ensemble [20] of monodomain anisotropic magnetic particles. The coercive field of hysteresis loop is about 870 Oe and is in a good agreement with the value of HC obtained for the Fe25 glass from the AFM data. Here it is necessary to note that these results differ essentially from the results presented in the paper [21] for 20[Na.sub.2]O - 1.0[Al.sub.2][O.sub.3] - 13[B.sub.2][O.sub.3] - 6.3CaO - 0.2[Sb.sub.2][O.sub.3] - 4.5BaO - (55-x)Si[O.sub.2] - (x)[Fe.sub.2][O.sub.3] (where x = 0, 5,10, 15, 20, and 25) glasses where the hysteresis loop has been observed at [Fe.sub.2][O.sub.3] concentration of 25% only. For other concentrations (5-20%) these glasses have demonstrated a paramagnetic behavior.

So the combined analysis of X-rays diffraction [3], MFM, and magnetic properties data permits concluding that in ferriferous alkali borosilicate glasses during the melt and phase separation processes the self-organization of iron oxides nanoparticles into large agglomerates with magnetic properties takes place.

4. Conclusion

In the Fe15, Fe20, and Fe25 ferriferous alkali borosilicate glasses the drop-like and two-phase interpenetrative structures coexist and it is possible to use these glasses for production of porous glasses with magnetic properties. At preparation of glasses the transition of initial hematite ([alpha] - [Fe.sub.2][O.sub.3]) into magnetite ([Fe.sub.3][O.sub.4]) takes place, at which the magnetite nanoparticles with average sizes of 16 nm (for Fe15 and Fe20) and 46 nm (for Fe25) [3] self-assemble in the large agglomerates on surface and inside samples. The average sizes of these agglomerates depend on the initial a[Fe.sub.2][O.sub.3] concentration. All types of these glasses demonstrate the magnetic properties corresponding to Stoner-Wohlfarth ensemble of monodomain anisotropic magnetic particles. The field dependences of magnetization and the values of coercive fields have been obtained. The Fe20 glass does not contain the visible admixture of other iron oxides and is the most suitable for production of magnetic porous glasses and for creation of multiferroic artificial nanocomposite materials with spatial-separated magnetic and ferroelectric orderings with developed interface at ambient conditions.

http://dx.doi.org/10.1155/2014/320451

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This work is supported by RFBR (Grant 12-02-00230) and DAAD Grant "Strategic Partnership with St. Petersburg State Polytechnical University and Leibniz Universitat Hannover."

References

[1] M. Bibes, "Nanoferronics is a winning combination," Nature Materials, vol. 11, no. 5, pp. 354-357, 2012.

[2] A. Filimonov, A. Rudskoy, and A. Naberezhnov, "New nanocomposite materials on the basis of dielectric porous matrices," Material Sciences and Applied Chemistry, vol. 28, pp. 73-84, 2013.

[3] T. V. Antropova, I. N. Anfimova, I. V. Golosovskyet al., "Structure of magnetic nanoclusters in ferriferous alkali borosilicate glasses," Physics of the Solid State, vol. 54, no. 10, pp. 2106-2111, 2012.

[4] E. Koroleva, D. Burdin, T. Antropova et al., "Dielectric properties of two-phase and porous ferriferous glasses," Optica Applicata, vol. 42, no. 2, pp. 287-294, 2012.

[5] D. Enke, F. Janowski, and W. Schwieger, "Porous glasses in the 21-st century: a short review," Microporous and Mesoporous Materials, vol. 60, no. 1-3, pp. 19-30, 2003.

[6] N. S. Andreev, O. V. Mazurin, E. A. Porai-Koshits, G. P. Roskova, and V. N. Filipovich, Phenomena of Phase Separation in Glasses, Nauka, Leningrad, Russia, 1974.

[7] A. M. Tomoiaga, B. I. Cioroiu, V. Nica, and A. Vasile, "Investigations on nanoconfinement of low-molecular antineoplastic agents into biocompatible magnetic matrices for drug targeting," Colloids and Surfaces B: Biointerfaces, vol. 111, pp. 52-59, 2013.

[8] S. Huang, C. Li, Z. Cheng et al., "Magnetic [Fe.sub.3][O.sub.4] mesoporous silica composites for drug delivery and bioadsorption," Journal of Colloid and Interface Science, vol. 376, no. 1, pp. 312-321, 2012.

[9] R. K. Singh, A. Srinivasan, and G. P. Kothiyal, "Evaluation of CaO-Si[O.sub.2]-[P.sub.2][O.sub.5]-Na2O-[Fe.sub.2][O.sub.3] bioglass-ceramics for hyperthermia application," Journal of Materials Science: Materials in Medicine, vol. 20, no. 1, pp. S147-S151, 2009.

[10] M. Baikousi, S. Agathopoulos, I. Panagiotopoulos, A. D. Georgoulis, M. Louloudi, and M. A. Karakassides, "Synthesis and characterization of sol-gel derived bioactive CaO-Si[O.sub.2]-[P.sub.2][O.sub.5] glasses containing magnetic nanoparticles," Journal of Sol-Gel Science and Technology, vol. 47, no. 1, pp. 95-101, 2008.

[11] X. Li, F. Qu, W. Li, H. Lin, and Y. Jin, "Synthesis of hierarchically porous bioactive glasses using natural plants as template for bone tissue regeneration," Journal of Sol-Gel Science and Technology, vol. 63, no. 3, pp. 416-424, 2012.

[12] Y.-H. Won, H. S. Jang, S. M. Kim et al., "Biomagnetic glasses: preparation, characterization, and biosensor applications," Langmuir, vol. 26, no. 6, pp. 4320-4326, 2010.

[13] F. Hu, S. Chen, and R. Yuan, "Application of magnetic coreshell microspheres on reagentless immunosensor based on direct electrochemistry of glucose oxidase for detection of carbohydrate antigen 19-9," Sensors and Actuators B, vol. 176, pp. 713-722, 2013.

[14] D. Min, X. Zhang, W. He et al., "Direct immobilization of glucose oxidase in magnetic mesoporous bioactive glasses," Journal of Materials Chemistry B, vol. 1, no. 26, pp. 3295-3303, 2013.

[15] S. Banerjee, P. Hajra, M. R. Mada, A. Bhaumik, S. Bandyopadhyay, and D. Chakravorty, "Exchange bias effect in nickel zinc ferrite-mesoporous silica nanocomposites," Journal of Magnetism and Magnetic Materials, vol. 332, pp. 98-102, 2013.

[16] W. H. Meiklejohn and C. P. Bean, "New magnetic anisotropy," Physical Review, vol. 105, no. 3, pp. 904-913, 1957

[17] I. A. Levitskii, "The effect of iron oxides on the properties and structure of glazed glasses," Glass and Ceramics, vol. 60, no. 3-4, pp. 111-114, 2003.

[18] N. I. Porechnaya, A. A. Naberezhnov, I. A. Drozdova, I. N. Anfimova, and O. A. Pshenko, "Morphology of ferriferous glasses at different hematite concentrations," St. Petersburg State Polytechnical University Journal. Physics and Mathematics, vol. 158, no. 4, pp. 22-28, 2012 (Russian).

[19] O. A. Pshenko, I. A. Drozdova, I. G. Polyakova et al., "Ferromagnetic iron-containing porous glasses," Glass Physics and Chemistry, vol. 40, no. 2, pp. 167-172, 2014.

[20] E. C. Stoner and E. P. Wohlfarth, A Mechanism of Magnetic Hysteresis in Heterogeneous Alloys, vol. 240 of Philosophical transactions of the Royal Society of London. Series A, 1948.

[21] J. Kaewkhao, W. Siriprom, S. Insiripong, T. Ratana, C. Kedkaew, and P. Limsuwan, "Structural and magnetic properties of glass doped with iron oxide," Journal of Physics: Conference Series, vol. 266, no. 1, Article ID 012012, 2011.

Alexander Naberezhnov, (1,2) Nadezda Porechnaya, (2) Viktor Nizhankovskii, (3) Alexey Filimonov, (1) and Bernard Nacke (4)

(1) St. Petersburg State Polytechnical University, Polytechnicheskaya 29, St. Petersburg 195251, Russia

(2) Ioffe Physico-Technical Institute, Polytechnicheskaya 26, St. Petersburg 194021, Russia

(3) International Laboratory of High Magnetic Fields and Low Temperatures, Gajowicka 95, 53-421 Wroclaw, Poland

(4) Leibniz University of Hannover, ETP, Wilhelm-Busch-Street, 30167 Hannover, Germany

Correspondence should be addressed to Alexander Naberezhnov; alex.nabereznov@mail.ioffe.ru

Received 24 April 2014; Revised 15 July 2014; Accepted 16 July 2014; Published 5 August 2014

Academic Editor: Isabel Del Hierro
COPYRIGHT 2014 Hindawi Limited
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2014 Gale, Cengage Learning. All rights reserved.

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:Research Article
Author:Naberezhnov, Alexander; Porechnaya, Nadezda; Nizhankovskii, Viktor; Filimonov, Alexey; Nacke, Bernar
Publication:The Scientific World Journal
Article Type:Report
Date:Jan 1, 2014
Words:3012
Previous Article:On the shape of limit cycles that bifurcate from isochronous center.
Next Article:An improved multidimensional MPA procedure for bidirectional earthquake excitations.
Topics:

Terms of use | Privacy policy | Copyright © 2020 Farlex, Inc. | Feedback | For webmasters