Injection molding research targets micro-molding, sinks & foams.
While injection molding of micro-sized parts with dimensions in the millimeter range is growing in importance, current simulation software reportedly is not appropriate for parts of such scale. Said IKV engineer Axel Cramer, "No simulation software exists that considers the typical characteristics of micro-parts."
He identified several software improvements that would be required. One is a provision for internal runners to fill non-continuous parts--i.e, ones with multiple inserts such as tiny letters. "The internal runners are difficult to predict and have to be designed in CAD software separate from the mold design, then simulated together with the whole part. If that runner needs to be optimized for rheological layout, it is modified in CAD software and the entire system must be meshed again--a time-consuming process," said Cramer.
Heat transfer between part and mold during filling is another area for development. With tiny parts, rapid dissipation of heat from the melt causes fast solidification of the melt. Small variations in mold temperature can dramatically affect filling of parts less than 1 mm thick. Cramer recommended coupling simulation of mold filling with simulation of transient local changes in mold temperature caused by heat transfer from the part.
Cramer added that material models for simulation typically are based on melt-viscosity measurements taken with capillary rheometers at shear rates between 100 and 10,000 [sec.sup.-1]. But in filling micro-sized parts, shear rates can exceed 100,000 [sec.sup.-1] and even reach 1 million [sec.sup.-1], according to Cramer. These values are typically extrapolated with conventional simulation software, which opens the door for inaccuracy in flow prediction.
Another overlooked aspect in conventional simulation software is that capillary rheometers take the viscosity measurements under isothermal conditions (constant temperature), but in micro-molding, very high shear rates generate a rise in temperature.
Cramer and IKV were a part of a consortium of 13 universities and companies on a project funded by the European Union. One partner, Simcon Kunststofftechnische Software GmbH, used its Cadmould simulation software for the research.
The project developed new software for non-continuous parts that allows internal runners to be easily modified within the simulation without further work in a CAD program. To address heat exchange between the part and mold, a new software interface allows the simulation program to use the result of a heat-exchange calculation by standard 3D finite-element software such as Abaqus. The interface makes it possible to calculate mold temperature throughout the process cycle (instead of assuming a constant wall temperature) based on the cooling medium, its temperature and flow rate, and mold cycle time and open time.
Furthermore, a new material model was developed for the simulation that describes viscosity at very high shear rates and determines actual viscosity (not extrapolated values) by accounting for shear at high injection speeds and fill times as short as 0.1 sec.
Ultrasonic sink analysis
A new way to predict the occurrence and severity of sink marks while the part is still in the mold was developed by Oliver Lingk, an engineer in the IKV Dept. of Injection Molding. The speed of travel of ultrasound waves through plastic are affected by temperature and pressure. When the melt is at its hottest, sound travels slowest, and as the part cools, the sound velocity increases until the part detaches from the cavity, at which point the signal ends.
Using pairs of ultrasonic emitters and receivers in a mold, Lingk varied the machine parameters while molding a test part and analyzed the resulting sink depths with an optical laser. He performed a multiple regression analysis to correlate the ultrasonic information and the sink dimensions. Lingk thereby derived a linear equation that estimates the sink depth for a particular material in a particular mold according to ultrasonic measurements taken during molding. This new on-line QC tool could be used to fine-tune molding parameters to minimize sinks.
Rethinking foam molding
One well-known difficulty in foam injection molding is producing parts with smooth unblemished surfaces. Axel Cramer discussed a second project to solve this problem. Unlike the usual low-pressure, short-shot approach for filling a foam mold, Cramer described several alternatives that can yield better surfaces by starting with a full shot under high pressure.
Three of these approaches are well known: gas counterpressure, a movable core or cavity that withdraws after filling to allow foaming, and a textured mold surface to hide swirls or bubbles. A variation on the last approach is what Cramer calls a "structured" cavity surface, which is etched with geometric structures such as pyramids, that permit better venting of the escaping gas and also help conceal defects.
In addition, Cramer suggested using a heat-insulating coating on the cavity surface that's designed to slow the cooling of the outer skin of the part to avoid freezing in gas bubbles or streaks. It does impose a minor increase in cycle time, Cramer concedes.
NEED TO KNOW MORE?
For more information, enter PTDirectcode at www.ptonline.com.
Institut fur Kunststoffverabeitung at RWTH (IKV), Aachen, Germany
+49 241 80 93 806 * PTDirect: 665AR
Simcon Kunststofftechnische Software GmbH, Herzogenrath, Germany
+49 2 407 908 58-0 * www.simcon-worldwide.com
|Printer friendly Cite/link Email Feedback|
|Title Annotation:||Close-Up: INJECTION MOLDING|
|Date:||Oct 1, 2006|
|Previous Article:||New source of collapsible cores.|
|Next Article:||New materials & equipment for decorating in & out of the mold.|