Growth and etch rate study of low temperature anodic silicon dioxide thin films.

1. Introduction

Silicon dioxide (Si[O.sub.2]) thin films are most extensively used insulating films in the manufacturing of silicon-based semiconductor devices, integrated circuits (ICs), and in microelectromechanical systems (MEMS) for different applications such as gate component in metal oxide semiconductor (MOS) transistors, masking layer against diffusion and implantation of dopants in the silicon [1, 2], and isolation of devices [3]. Silicon dioxide thin film is preferred over other dielectric films due to its ease of synthesis, excellent insulating properties, and high quality Si-Si[O.sub.2] interface. Thermal oxidation technique is known to provide high quality Si[O.sub.2] film and hence widely employed [4]. However, high processing temperature (~900-1100[degrees]C) of this technique causes redistribution of dopants in silicon substrate during oxide growth and develops stress in silicon substrate that leads to wafer warpage [5-7]. Several new synthesis routes have been developed to reduce the process temperature. Atmospheric pressure chemical vapour deposition (APCVD) [8], plasma enhanced chemical vapour deposition (PECVD) [9], sputtering [10], wet anodic oxidation [11-14], liquid phase deposition (LPD) [15], and sol-gel [16] are few of the low temperature thin film deposition techniques. Each and every process has its own advantages and disadvantages. Among these low temperature techniques, anodic oxidation is one which can be operated even below room temperature [17]. Numerous research groups have investigated a nodically grown oxide thin films for gate dielectric component in MOS devices [11, 14, 18]. Anodic oxidation process has several advantages over other techniques such as low cost, simple experimental setup, and room temperature process which minimizes the dopants redistribution and does not involve any toxic and expensive gases. In order to explore anodic oxidation for different applications, further study is required to investigate the properties of as-grown Si[O.sub.2] films with respect to electrolyte solution composition, mode of growth and other relevant processing parameters.

The present work is focused to investigate the effect of applied voltage, electrolyte stirring, current density, and the amount of water on the growth rate, refractive index, and the chemical composition of as-grown oxide thin films.

These properties are studied using Ellipsometry, Fourier Transform Infrared Spectroscopy (FTIR), And Scanning Electron Microscope (SEM).

2. Experimental Details

Czochralski ([C.sub.z]) grown four-inch diameter P-type boron doped (resistivity 1-10 Q cm) {100} oriented single side polished silicon wafers are diced into 23 x 23 [mm.sup.2] chip size for the deposition of oxide film using anodic oxidation technique. After dicing, chips are cleaned ultrasonically in acetone for 10 minutes followed by thorough rinse in deionized (DI) water. Aluminum is deposited on the rough surface side using e-beam evaporation technique for ohmic contact purpose. Ethylene glycol solvent (purity > 99%, Sigma-Aldrich) mixed with 0.04 M potassium nitrate (KN[O.sub.3]) and the certain amount of water is utilized as electrolyte solution. Each time fresh solution is used to avoid the incorporation of glycol by-products in the oxide films. A parallel-plate electrodes system is employed for oxidation process. In the parallel-plate configuration, silicon sample is fixed as anode and the platinum gauge mesh as cathode. A customarily designed sample holder is used to take the contact from the back side of the silicon sample. The design of the chip holder is such that only 2.54 [cm.sup.2] circular area of the sample is exposed to the electrolyte solution. In the experimental setup, anode and cathode are separated by fixed distances of 1.5 cm in potentiodynamic and 2 cm in potentiostatic mode. Prior to oxidation, samples are dipped in 1% hydrofluoric acid (HF) solution until the wetting of the surface is ceased completely to etch out native oxide layer followed by thorough rinsing in DI water to ensure that no traces of HF are left on silicon substrate.

Oxide growth rate is predominantly influenced by water content in the electrolyte, processing parameters such as current density, and temperature of electrolyte. In order to elucidate the effect of these parameters, oxide synthesis is carried out in potentiostatic and potentiodynamic modes with varying water content, current density and voltage. In potentiostatic mode, a fixed quantity (0.5vol%) of water is added into electrolyte. The oxide synthesis is carried out at a fixed impressed voltage (50-250 V) and continued until the initial current fall down to a minimum current of 2 mA. In the case of potentiodynamic mode, the amount of water is varied from 0 (i.e., no water) to 0.7 vol% and the deposition is performed at a fixed applied current density until the final voltage reaches the predetermined voltage of 300 V. Thereafter, the process is continued in potentiostatic mode at 300 V for 15 minutes. After oxidation, the oxide samples are thoroughly cleaned in DI water to get rid of the adsorbed glycol solvent from the oxide surface. In order to investigate the effect of stirring on oxide film characteristics, the deposition is carried out with and without stirring of electrolyte. In all cases, anodic oxidation is performed at room temperature.

Ellipsometry (J. A. Woolam, model: M-2000D) measurements are performed at three incident angles (65[degrees], 70[degrees], and 75[degrees]) to determine thickness and refractive index of the oxide films in the wavelength region of 193-1000 nm. FTIR (Bruker, model: ALPHA) measurement in ATR module is employed to evaluate the chemical bonds present in the oxide films. Scanning electron microscope (ZEISS, model: SUPRA40) is employed to study the surface morphology. The etch rates of oxide films are determined in different types of etchants.

3. Results and Discussions

Several characterization techniques are used to study different properties of as-grown oxide films.

3.1. Kinetics of Oxide Growth. The kinetics of growth of oxide films is studied for the films deposited in potentiostatic and potentiodynamic modes with varying water content, current density, and voltage.

3.1.1. Potentiostatic Mode. Figure 1(a) shows the variation in current density with oxidation time at various voltages in potentiostatic mode of operation. The shape of the curves suggests that the oxide growth is parabolic at voltages greater than 50 V. It can be observed from Figure 1(a) that the current density at higher voltages decreases rapidly in the first 4 or 5 minutes of oxidation (i.e., initial stage of oxidation) which indicates faster growth rate of oxide in the initial stage of oxidation. After the deposition of certain thickness, the current density becomes almost constant. In this stage, oxide growth rate decreases owing to reduction in the diffusion of oxygenic ions, which happens due to fall in electric field [19, 20].

3.1.2. Potentiodynamic Mode. In potentiodynamic mode, oxide growth is performed at fixed current densities with varying water content in electrolyte. At the fixed current density, voltage increases with time up to the predetermined voltage (300 V) of oxidation process. The variation in cell voltage during oxide deposition is recorded for every 1 min of time and a graph is plotted between a nodization time and cell voltage as shown in Figure 1(b). The curves in Figure 1(b) explain that the applied voltage increases in order to maintain the same current density throughout the oxidation process. As can be seen in Figure 1(b), the voltage versus time behaviour is the same for different current densities and water percentages. The role of current density on growth rate of oxide can be understood clearly; for instance, the oxidation time required to attain the predetermined voltage at 8 mA/[cm.sup.2] is shorter than that needed at 5.5 mA/[cm.sup.2]. Larger slope indicates faster growth rate at higher current densities which is attributed to enhanced diffusion rate of oxygenic ions [21]. It is obvious from the slope of the curves in Figure 1(b) that the growth rate of the oxide at fixed current density decreases with increase of water percentage in electrolyte, whereas the time required to attain predetermined voltage is reduced with decrease in water percentage. However, the decrease in growth rate is not significant due to the small variation in water content in the electrolyte solution.

3.2. Ellipsometric Study. Ellipsometric study is performed to characterize the thickness and refractive index of thefilms deposited under different conditions.

3.2.1. Thickness. Thickness of oxide films is measuredby ellipsometry at three incidence angles (65[degrees], 70[degrees], and 75[degrees]). In order to analyze the measured data, a model is generated with two layers, Cauchy type material and an intermediate layer at the interfaceof Si and Si[O.sub.2].

Figure 2(a) shows the effect of applied voltage on thickness of the film deposited under potentiostatic mode. It can be noticed from the graph that the thickness increases linearly with applied voltage. Since increase in voltage enhances the driving force of the transport of oxygenic ions through the oxide layer for the growth to happen at Si/Si[O.sub.2] interface [19, 20], theslope of thestraight linein Figure 2(a) represents the growth rate of the oxide in A/V, which is 5.25 A/V. Similarly, Y intercept gives the native oxide thickness which is zero in this case. Thickness uniformity of the oxide films is evaluated by measuring oxide thickness at four different spots. Figure 2(b) presents film thicknesses measured at four different spots on the samples prepared under potentiostatic mode at 50-250 V.

Films thicknesses grown under potentiodynamic mode with varying concentration of water in electrolyte at 5.5 and 8mA/[cm.sup.2] current density are shown in Figures 3(a) and 3(b), respectively. Small thickness variation (1-5 A) indicates that the films are uniformly grown in potentiostatic and potentiodynamic modes. In potentiodynamic mode, current density does not affect the film thickness significantly as the predetermined voltage (300 V) is the same at 5.5 and 8mA/[cm.sup.2] current densities. Moreover, the oxide growth is performed on the basis of predetermined voltage not on fixed time period basis.

3.2.2. Refractive Index. Refractive index of oxide films is determined by using variable angle ellipsometry at the fixed wavelength of 632.8 nm. In general refractive index of the oxide is a function of composition or stoichiometry [2225] and density/porosity of the oxide film [26-28]. The refractive indexes of the oxide films grown in potentiostatic and potentiodynamic modes are presented in Tables 1 and 2, respectively. In potentiostatic mode, the refractive index of the oxides increases from 1.45 to 1.478 as applied voltage varies from 50 to 250 V. The refractive index of the oxide films prepared above 50 V is slightly larger than that of thermally grown silicon oxide. It may be due to more silicon content in the film [24, 29]. Higher silicon content is confirmed by FTIR measurement results, which are presented in the next section, where the small intense peaks of oxygen deficiency that is, Si-Si bond at 653-670 [cm.sup.-1], and suboxides around 988-1000 [cm.sup.-1] are observed [30, 31].

In the potentiodynamic mode of operation, the refractive index of the films deposited with varying water percentage and current density is obtained in the range of 1.474-1.475. Larger refractive index in this mode could be owing to the enhancement in film density (lower porosity) [32, 33] and/or due to oxygen deficiency in the film [24].

3.3. Fourier Transform Infrared Spectroscopy (FTIR) Characterization. Fourier transform infrared spectroscopy (FTIR) is employed for finding the nature of chemical bonds in the oxide films. In the present work, ATR-FTIR module with 45[degrees] angle of light incidence is utilized for the frequency scan of 550-4000 [cm.sup.-1]. Figure 4 shows the comparison of FTIR absorption spectra of the films prepared under potentiostatic mode at various voltages. The characteristic vibrations of Si[O.sub.2] such as Si-O bending and Si-O-Si asymmetric stretching are observed in the wave number range 817-821 [cm.sup.-1] and 1121-1213 [cm.sup.-1], respectively, with Si-O-Si asymmetric stretching peak as intense peak in all samples [30, 34, 35].

The shift in the position of Si-O-Si asymmetric stretching peak occurs due to alteration in oxide thickness, stress/strain, porosity, and the O/Si ratio of the oxide films [24, 27, 3638]. It canbeobservedinFTIRspectra shownin Figure 4 that the position of Si-O-Si asymmetric stretching peak is shifting with applied voltage. The applied voltage influences the growth rate, which in turn affects the structure and stoichiometry of the oxides that result in shifting of Si-O-Si asymmetric stretching peak position. In addition to two characteristic Si-O vibrational peaks, weak intense peaks corresponding to oxygen vacancies around 653-678 [cm.sup.-1] (Si-Si bond) [30], carbon impurity (1400-1500 [cm.sup.-1])[39], Si-H (2100-2300 [cm.sup.-1])[40], and silicon suboxide species (Si[O.sub.x], x~0.5) in the frequency range of 988-1000 [cm.sup.-1] [31] are also present in the spectrum. The absence of the peaks corresponding to Si-OH at 940 [cm.sup.-1] [41] and H-O-H vibrations bending at 1620 [cm.sup.-1] and stretching at 3640 [cm.sup.-1] [41] in the spectra confirms the absence of water in the deposited oxide films.

3.4. Effect of Stirring on Various Properties of Silicon Dioxide. Mechanical stirring of electrolyte solution is commonly employed in electrochemical based growth/deposition processes for maintaining uniform concentration of electrolyte throughout the solution and also to circumvent the local temperature rises in the bath. In order to find the effect of electrolyte stirring on thickness and other properties of as prepared oxide films, depositions are performed with and without mechanical stirring of electrolyte at 100 and 250 V in potentiostatic regime. Figure 5(a) shows a comparison of film thicknesses grown without and with stirring of electrolyte at two different voltages. The thickness of the film deposited without stirring is about 4% less than that of deposited with stirring of the electrolyte. The reduction in oxide thickness may be due to the lack of convective contribution in the absence of mechanical stirring to the total flux of anionic (O[H.sup.-] or [O.sub.2.sup.-]) species as they are essential for the oxidation to take place at the anode (i.e., silicon) of the cell.

Figure 5(b) shows the comparison of FTIR absorption spectra of oxides grown with and without mechanical stirring at 100 and 250 V. It can be visualized in the spectra that the shape and position of Si-O-Si asymmetric stretching peak differ in two cases of oxidation. This variation may be attributed to the effect of mechanical agitation on the composition and structure of deposited oxides that lead to change in Si-O-Si bond angle [40-42].

The stirring of solution also affects the refractive index as presented in Table 1. The refractive index of the films prepared without stirring of electrolyte at constant voltages 100 and 250 V is slightly less than the films grown with stirring of the solution. This decrease in refractive index could be due to change in composition of the oxides caused by absence of electrolyte stirring.

3.5. Surface Morphology Investigation. Surface morphology of the oxide films is studied using SEM. Figures 6(a)6(d) reveal the surface morphologies of the oxide films developed in two different electrolyte compositions (0.2 and 0.7vol% of water) and current densities (5.5 and 8mA/[cm.sup.2]). It can be observed from SEM micrographs that the oxide films do not show any nodular and agglomerated kind of features. The films appear to be smooth and uniform which is also confirmed by ellipsometric measurements discussed in Section 3.2.1. Moreover, no pinholes are noticeable in SEM images that indicate high integrity and density of the oxide films. Similar kind of surface morphologies was observed in the films deposited with different parameters. It can be concluded that the variation in water percentage and current densities employed in this experiment does not significantly influence surface morphology of the films.

3.6. Etch Rates in HF-Based Solutions. In order to use silicon dioxide in integrated circuit (IC) and MEMS fabrication, the selective etching of oxide film is required for its patterning. Buffered hydrofluoric acid (BHF) (or diluted HF) is commonly used for oxide etching [42-45]. In the following sections, the study of oxide etching in 1 to 5 wt% HF and the buffered hydrofluoric acid (BHF) solutions is presented. Moreover, the etch rate in diluted HF is also employed for the evaluation of the quality of Si[O.sub.2] film [46].

3.6.1. Diluted HF Solutions. Diluted HF is prepared by adding DI water in concentrated HF (i.e., 49wt%), while BHF is prepared by mixing 40 wt% ammonium fluoride (N[H.sub.4]F) in concentrated HF (generally from 6: 1 to 10 : 1). The etch rate of oxide grown at 8 mA/[cm.sup.2] current density and 0.7 vol% of water (thickness 160 nm) is determined in 1 to 5 wt% HF solutions. Prior to etching, sample is thoroughly cleaned in DI water followed by drying and heating at 100[degrees]C for about 5 min. Oxide etching is carried out by immersing the sample in the etchant for fraction of seconds followed by deionized water rinsing. Thereafter, sample is dried and thickness is measured at different spots using ellipsometry. The etching process is continued until oxide thickness is reduced to approximately below 150 A. The effect of HF concentration on the etch rate is shown in Figure 7(a). The etching mechanism of Si[O.sub.2] in HF-based solutions is explained elsewhere [47]. It can be noticed from the graph that the etch rate of oxide increases almost linearly with HF concentration, which is attributed to enhanced concentration of H[F.sub.2.sup.-]; undissociated HF reactants as the concentration of HF increased up to a maximum at 10 M concentration [48, 49]. The etch rate of oxide is a function of its density, strain, and stoichiometry [47, 50]. It is inversely proportional to the density of the film. The reduced etch rate of oxide in the present work is attributed to greater density (less porosity) of the oxide film, which is confirmed by SEM study as shown in Figure 6(d).

Figure 7(b) shows the etch rate behavior of oxide with time for HF concentrations varying from 1 to 5 wt%. It can be noticed from the figure that the trend in etch rate variation with time is the same for all HF concentrations. The variation in etch rate is probably due to change in oxide structure, that is, Si-O-Si bond angle [51].

3.6.2. Etch Rate in Buffered Hydrofluoric Acid (BHF) Solution. Etch rate of the oxide film (thickness 160 nm) grown at 8mA/[cm.sup.2] and 0.7 vol% water is measured in BHF (HF (49%): N[H.sub.4]F(40%):: 1: 7) [45]. The addition of N[H.sub.4]F to HF increases the concentration of H[F.sub.2.sup.-] reactants in the etchant. The etch rate of oxide increases with N[H.sub.4]F concentration up to the maximum at 10-12% of N[H.sub.4]F [52, 53]. The procedure of etch rate determination in BHF is the same as explained in the previous section for diluted HF. Average etch rate in BHF for the oxide film developed in the present work is measured to be 93.0 [Angstrom]/sec.

4. Conclusions

Silicon dioxide thin films with uniform thickness are developed on silicon samples using anodic oxidation process at room temperature. In potentiostatic mode of anodic oxidation, thickness predominantly depends on applied voltage. A linear dependency of oxide thickness on applied voltage is obtained in the range from 50 to 250 V. The mechanical agitation of electrolyte solution during deposition improves thegrowthrateand thechemicalstructure of oxidefilms. In potentiodynamic mode, oxide growth rate is mainly influenced by current density irrespective of the amount of water in the electrolyte. The growth rate increases with rise in current density. No significant effect is observed on growth rate, thickness, refractive index and the surface morphology of the films when the water content in electrolyte is varied by a small amount. The FTIR spectra of the oxides developed in potentiostatic mode reveals that the oxide films contain small percentage of carbon, hydroxyl impurities and the absence of OH and [H.sub.2]O. The dense nature of the oxide films is confirmed by measuring the etch rate in diluted HF (1 to 5 wt%) and using SEM micrographs.

http://dx.doi.org/10.1155/2014/106029

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

References

[1] S. Robles, E. Yieh, and B. C. Nguye, "Moisture resistance of plasma enhanced chemical vapor deposited oxides used for ultralarge scale integrated device applications," Journal of the Electrochemical Society, vol. 142, no. 2, pp. 580-585, 1995.

[2] H. O. Pierson, Handbook of Chemical Vapor Deposition (CVD): Principles, Technologyand Applications, Noyes, Saddle River, NJ, USA, 1992.

[3] C. Zhang and K. Najafi, "Fabrication of thick silicon dioxide layers for thermal isolation," Journal of Micromechanics and Microengineering, vol. 14, no. 6, pp. 769-768, 2004.

[4] W.-F. Wu and B.-S. Chiou, "Optical and mechanical properties of reactively sputtered silicon dioxide films," Semiconductor Science and Technology, vol. 11, no. 9, pp. 1317-1321, 1996.

[5] A.S.Grove, O.LeistikoJr., and C. T. Sah, "Redistributionof acceptor and donor impurities during thermal oxidation of silicon," Journal of Applied Physics, vol. 35, no. 9, pp. 2695-2701, 1964.

[6] B. E. Deal, A. S. Grove, E. H. Snow, and C. T. Sah, "Observation of impurity redistribution during thermal oxidation of silicon using the MOS structure," Journal of the Electrochemical Society, vol. 112, no. 3, pp. 308-314, 1965.

[7] Y. Yorium, "Deformation of silicon wafers by thermal oxidation," Journal of the Electrochemical Society, vol. 129, no. 9, pp. 2076-2081, 1982.

[8] A. Pecora, L. Maiolo, G. Fortunato, and C. Caligiore, "A comparative analysis of silicon dioxide films deposited by ECR PECVD, TEOS-PECVD and Vapox-APCVD," Journal of NonCrystalline Solids, vol. 352, no. 9-20, pp. 1430-1433, 2006.

[9] M. J. Thompson, "Thin filmtransistors forlarge area electronics," Journal of Vacuum Science & TechnologyB, vol. 2, no. 4, pp. 827-834, 1984.

[10] V. Bhatt and S. Chandra, "Silicon dioxide films by RF sputtering for microelectronic and MEMS applications," Journal of Micromechanics and Microengineering, vol. 17, no. 5, pp. 1066-1077, 2007.

[11] T. F. Hung, H. Wong, Y. C. Cheng, and C. K. Pun, "New design of anodic oxidation reactor for high-quality gate oxide preparation," Journal of the Electrochemical Society, vol. 138, no. 12, pp. 3747-3750, 1991.

[12] H. J. Lewerenz, "Anodic oxides on silicon," Electrochimica Acta, vol. 37, no. 5, pp. 847-864, 1992.

[13] E. F. Duffek, C. Mylroie, and E. A. Benjamini, "Electrode reactions and mechanism of silicon anodization in Nmethylacetamide," Journal of the Electrochemical Society, vol. 111, no. 9, pp. 1042-1046, 1964.

[14] H. Aguas, A. Goncalves, L.Pereira, R.Silva, E.Fortunato, and R. Martins, "Spectroscopic ellipsometry study of amorphous silicon anodically oxidised," Thin Solid Films, vol. 427, no. 1-2, pp. 345-349, 2003.

[15] K. S. Kim and Y. Roh, "Silicon dioxide deposited by using liquid phase deposition at room temperature for nanometer-scaled isolation technology," Journal of the Korean Physical Society, vol. 51, no. 3, pp. 1191-1194, 2007.

[16] D. K. Kambhampati, T. A. M. Jakob, J. W. Robertson, M. Cai, J. E. Pemberton, and W. Knoll, "Novel silicon dioxide sol-gel films for potential sensor applications: a surface plasmon resonance study," Langmuir, vol. 17, no. 4, pp. 1169-1175, 2001.

[17] C. Panagopoulos and H. Badekas, "Growth of anodic Si[O.sub.2] films," Materials Letters, vol. 8, no. 6-7, pp. 212-215, 1989.

[18] W.-B. Kim, T. Matsumoto, and H. Kobayashi, "Ultrathin Si[O.sub.2] layer with an extremely low leakage current density formed in high concentration nitric acid," Journal of Applied Physics, vol. 105, no. 10, Article ID 103709, 2009.

[19] L. Sun, S. Zhang, X. W. Sun, and X. He, "Effect of electric field strength on the length of anodized titania nanotube arrays," Journal of Electroanalytical Chemistry, vol. 637, no. 1-2, pp. 6-12, 2009.

[20] Y.-F.Mei, X.-L. Wu, T.Qiu, X.-F. Shao, G.-G. Siu, and P. K. Chu, "Anodizing process of Al films on Si substrates for forming alumina templates with short-distance ordered 25 nm nanopores," Thin Solid Films, vol. 492, no. 1-2, pp. 66-70, 2005.

[21] H. M. A. Soliman and A.-H. B. Kashyout, "Electrochemical deposition and optimization of thermoelectric nanostructured bismuth telluride thick films," Engineering, vol. 3, no. 6, pp. 659-667, 2011.

[22] B. M. Ayupov, S. F. Devyatova, V. G. Erkov, and L. A. Semenova, "Depth profiles of refractive index in thermally grown and LPCVD oxide films on silicon," Russian Microelectronics, vol. 37, no. 3, pp. 141-145, 2008.

[23] M. F. Ceiler Jr., P. A. Kohl, and S. A. Bidstrup, "Plasma-enhanced chemical vapor deposition of silicon dioxide deposited at low temperatures," Journal of the Electrochemical Society, vol. 142, no. 6, pp. 2067-2071, 1995.

[24] C.-F. Lin, W.-T. Tseng, and M. S. Feng, "Formation and characteristics of silicon nanocrystals in plasma-enhanced chemicalvapor-deposited silicon-rich oxide," Journal of Applied Physics, vol. 87, no. 6, pp. 2808-2815, 2000.

[25] T. Roschuk, J. Wojcik, X. Tan, J. A. Davies, and P. Mascher, "Optical and compositional characterization of Si[O.sub.x]Ny and Si[O.sub.x] thin films deposited by electron cyclotron resonance plasma enhanced chemical vapor deposition," Journal of Vacuum Science & TechnologyA, vol. 22, no. 3, pp. 883-886, 2004.

[26] M. Stadtmueller, "Mechanical stress of CVD-dielectrics," Journal of the Electrochemical Society, vol. 139, no. 12, pp. 3669-3674, 1992.

[27] G. Lucovsky, M. J. Manitini, J. K. Srivastava, and E. A. Irene, "Low-temperature growth of silicon dioxide films: a study of chemical bonding by ellipsometry and infrared spectroscopy," Journal of Vacuum Science & Technology B, vol. 5, no. 2, pp. 530-537, 1987.

[28] B. N. Joshi and A. M. Mahajan, "Growth and characterization of porous Si[O.sub.2] thin films for interlayer dielectrics applications in ULSI," Optoelectronics and Advanced Materials, vol. 1, no. 12, pp. 659-662, 2007.

[29] W. A. Pliskin, "Refractive index dispersion of dielectric films used in the semiconductor industry," Journal of the Electrochemical Society, vol. 134, no. 11, pp. 2819-2826, 1987.

[30] M. I. Alayo, I. Pereyra, W. L. Scopel, and M. C. A. Fantini, "On the nitrogen and oxygen incorporation in plasma-enhanced chemical vapor deposition (PECVD) Si[O.sub.x]Ny films," Thin Solid Films, vol. 402, no. 1-2, pp. 154-161, 2002.

[31] J. Lambers and P. Hess, "Infrared spectra of photochemically grown suboxides at the Si/Si[O.sub.2] interface," Journal of Applied Physics, vol. 94, no. 5, pp. 2937-2941, 2003.

[32] A. Sassella, P. Lucarno, A. Borghesi, F. Corni, S. Rojas, and L. Zanotti, "Silicon oxynitride study by the tetrahedron model and by spectroscopic ellipsometry," Journal of Non-Crystalline Solids, vol. 187, pp. 395-402, 1995.

[33] A. del Pradoa, E. San Andres, F. L. Martinez et al., "Composition and optical properties of silicon oxynitride films deposited by electron cyclotron resonance," Vacuum, vol. 67, no. 3-4, pp. 507-512, 2002.

[34] F. L. Galeener, "Band limits and the vibrational spectra of tetrahedral glasses," Physical Review B, vol. 19, no. 8, pp. 4292-4297, 1979.

[35] P. G. Pai, S. S. Chao, Y. Takagi, and G. Lucovsky, "Infrared spectroscopic study of Si[O.sub.x] films produced by plasma enhanced chemical vapor deposition," Journal of Vacuum Science & Technology A, vol. 4, no. 3, pp. 689-694, 1986.

[36] W. A. Pliskin and H. S. Lehman, "Structural evaluation of silicon oxide films," Journal of the Electrochemical Society, vol. 112, no. 10, pp. 1013-1019, 1965.

[37] W. A. Pliskin, "Comparison of properties of dielectric films deposited by various methods," Journal of Vacuum Science & Technology, vol. 14, no. 5, pp. 1064-1081, 1977.

[38] I. W. Boyd and J. I. B. Wilson, "Structure of ultrathin silicon dioxide films," Applied Physics Letters, vol. 50, no. 6, pp. 320-322, 1987.

[39] L. L. Tedder, J. E. Crowell, and M. A. Logan, "The chemical vapor deposition of Si[O.sub.2] from tetraethoxysilane: the effect of the surface hydroxyl concentration," Journal of Vacuum Science & Technology A, vol. 9, no. 3, pp. 1002-1006, 1991.

[40] D. V. Tsu, G. Lucovsky, and B. N. Davidson, "Effects of the nearest neighbors and the alloy matrix on SiH stretching vibrations in the amorphous SiOr:H (0 <r<2) alloy system," Physical Review B, vol. 40, no. 3, pp. 1795-1805, 1989.

[41] W.-S. Liao, C.-H. Lin, and S.-C. Lee, "[O.sub.x]idation of silicon nitride prepared by plasma-enhanced chemical vapor deposition at low temperature," Applied Physics Letters, vol. 65, no. 17, pp. 2229-2231, 1994.

[42] D. J. Monk, D. S. Soane, and R. T. Howe, "Sacrificial layer Si[O.sub.2] wet etching for micromachining applications," in Proceedings of the IEEE International Conference on Solid-State Sensors and Actuators. Digest of Technical Papers (TRANSDUCERS 91), pp. 647-650, San Francisco, Calif, USA, June 1991.

[43] D. J. Monk, D. S. Soane, and R. T. Howe, "Determination of the etching kinetics for the hydrofluoric acid/silicon dioxide system," Journal of the Electrochemical Society, vol. 140, no. 8, pp. 2339-2346, 1993.

[44] J. S. Judge, "A study of the dissolution of Si[O.sub.2] in acidic fluoride solutions," Journal of the Electrochemical Society, vol. 118, no. 11, pp. 1772-1775, 1971.

[45] H. Kikuyama, M. Waki, I. Kawanabe et al., "Etching rate and mechanism of doped oxide in buffered hydrogen fluoride solution," Journal of the Electrochemical Society, vol. 139, no. 8, pp. 2239-2243, 1992.

[46] W. Kern and G.L. Schnable, "Wet etching, "in The Chemistry of the Semiconductor Industry, S. J. Moss and A. Ledwith, Eds., chapter 11, pp. 225-280, Blackie & Son, Glasgow, UK, 1987.

[47] D. J. Monk, D. S. Soane, and R. T. Howe, "A review of the chemical reaction mechanism and kinetics for hydrofluoric acid etching of silicon dioxide for surface micromachining applications," Thin Solid Films, vol. 232, no. 1, pp. 1-12, 1993.

[48] C. A. Deckert, "Etching of CVD [Si.sub.3][N.sub.4] in acidic fluoride media," Journal of the Electrochemical Society, vol. 125, no. 2, pp. 320-323, 1978.

[49] G. I. Parisi, S. E. Haszko, and G. A. Rozgonyi, "Tapered windows in Si[O.sub.2]:the effectofN[H.sub.4]F: HF dilution and etching temperature," Journal of the Electrochemical Society, vol. 124, no. 6, pp. 917-921, 1977.

[50] F. N. Schwettmann, R. J. Dexter, and D. F. Cole, "Etch rate characterization of boron-implanted thermally grown Si[O.sub.2]," Journal of the Electrochemical Society, vol. 120, no. 11, pp. 1566-1570, 1973.

[51] Y. W. Choi, J. H. Ahn, and B. T. Ahn, "Structure of Si[O.sub.2] films grown at low temperature by inductively coupled plasma oxidation with oxygen gas," Electronic Materials Letters, vol. 1, no. 2, pp. 97-102, 2005.

[52] J. Buhler, F. P. Steiner, and H. Baltes, "Silicon dioxide sacrificial layer etching in surface micromachining," Journal of Micromechanics and Microengineering, vol. 7, no. 1, article R1, 1997.

[53] H. Proksche, G. Nagorsen, and D. Ross, "Influence of N[H.sub.4]F on the etch rates of undoped Si[O.sub.2] in buffered oxide etch," Journal of the Electrochemical Society, vol. 139, no. 2, pp. 521-524, 1992.

Akarapu Ashok and Prem Pal

MEMS and Micro/Nano Systems Laboratory, Department of Physics, Indian Institute of Technology Hyderabad, Medak, Andhra Pradesh 502205, India

Correspondence should be addressed to Akarapu Ashok; ph11p1001@iith.ac.in

Received 26 August 2013; Accepted 1 December 2013; Published 2 February 2014

Academic Editors: R. M. Guedes and Y. Xiong

TABLE 1: Refractive index of the oxide films prepared in
potentio-static mode with and without mechanical stirring
of the electrolyte solution.

Regime: potentiostati= 3, water content = 0.5 vol%

Applied voltage (V)   Refractive index (n)
                     (with/without stirring)

50                            1.45
100                       1.470/14.466
150                          1.473
200                          1.475
250                       1.478/1.474

TABLE 2: Refractive index of the oxide films developed in
potentio-dynamic mode.

Regime: potentiodynamic, pH = 4

Current density   Water content   Refractive index
(mA/[cm.sup.2])      (vol%)             (n)

5.5                     0              1.4755
8                       0              1.4756
5.5                    0.2             1.4748
8                      0.2             1.4749
5.5                    0.7             1.4747
8                      0.7             1.4752
COPYRIGHT 2014 Hindawi Limited
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2014 Gale, Cengage Learning. All rights reserved.

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:Research Article
Author:Ashok, Akarapu; Pal, Prem
Publication:The Scientific World Journal
Article Type:Report
Date:Jan 1, 2014
Words:5389
Previous Article:Experimental study of the seismic performance of L-shaped columns with 500 MPa steel bars.
Next Article:Effect of layer thickness in selective laser melting on microstructure of Al/5 wt.%[Fe.sub.2][O.sub.3] powder consolidated parts.
Topics:

Terms of use | Privacy policy | Copyright © 2019 Farlex, Inc. | Feedback | For webmasters