Experimental study on durability improvement of fly ash concrete with durability improving admixture.

1. Introduction

Coal is widely used in China as fuel for power plants because of its dependability and economy. In 2009, more than 375 million tons of fly ash was generated from coal-fired power plants in China. How to effectively use fly ash is still a major social problem. In order to construct recycling society, researchers have found many ways to make efficient use of fly ash in civil engineering field [1-10], but in fact the use of fly ash in building construction is still limited. The main reasons are as follows. (1) The quality of fly ash is unstable because the quality of fly ash changes greatly with that of coals [11, 12]; (2) there is lower early age compressive strength of concrete due to lower activity of fly ash [13,14]; (3) pozzolanic reaction of fly ash leads to decreased pH value of concrete, which results in a poor carbonation resistance [15-17]. In addition, in order to ensure the resistance of freezing-thawing action, it is necessary to entrain a certain amount of air in the concrete. However, air-entraining admixture is adsorbed by the unburned activated carbon in fly ash which reduces air-entraining capability of fly ash concrete [18,19]. Therefore, it is the key issue to keep serial and stable air in fly ash concrete. In other words, the air content control of fly ash concrete is difficult.

On the basis of the above mentioned background, this paper focused on the nonair-entraining concrete. The effects of durability improving admixture, air content, water-binder ratio, and fly ash replacement ratio on strength development, drying shrinkage, carbonation, and freezing-thawing resistance of fly ash concrete are tobe investigated.

2. Experiment Overview

2.1. Materials Used and Concrete Composition. The characteristics of materials used and the properties of fly ash used are shown in Tables 1 and 2. Table 3 shows the experiment factors and ratios. Figure 16 shows the interpretation of marks. The mixture proportion and properties of concrete are shown in Table 4.

In this experiment, fly ash (FA) was used to replace the internal mass of cement, and 10 kg/[m.sup.3] of durability improving admixture was added to the final mixture. Air-entraining water reducing admixture was added to all the concrete, accounting for 1% of the weight of binder. In order to regulate fixed air content (4.5%), the standard air-entraining concrete (hereinafter referred to as "ST") used special air-entraining water reducing admixture. The concrete using durability improving admixture (hereinafter referred to as "D") became nonair-entraining type concrete, because of strong antifoam reaction in the admixture itself. The nonair-entraining concrete (hereinafter referred to as "PL") obtained fixed 1% air content by antifoam admixture. The target slump of concrete was 18 cm, and the target air content was 4.5% (ST) and 1.0% (D, PL).

2.2. Fabrication and Curing of Test Specimens. Cylindrical specimens, 100 mm in diameter and 200 mm in height, for compression tests were encased in light gauge molds in 3 layers and stripped molds after 24 hours. Then, specimens were cured in water at 20[degrees]C until testing ages. Prism specimens were used for drying shrinkage tests, accelerating carbonation tests, and freezing and thawing tests, the dimension of which was 100 mm x 100 mm x 400 mm. The specimens were cast in 2 layers and stripped molds after 24 hours. Then, the specimens for drying shrinkage tests were cured in water at 20[degrees]C for 7 days; the specimens for accelerating carbonation tests were cured in water at 20[degrees]C until 28 days and stored at air dried condition at 20[degrees]C for 28 days; the specimens for freezing-thawing tests were cured in water at 20[degrees]C until 28 days.

2.3. Test Methods for Hardened Concrete

2.3.1. Compressive Strength Tests. The specimens were tested at the age of 7 days, 28 days, and 91 days in wet condition according to JIS A1108-2006. Modulus of elasticity tests were measured at the same time of compressive strength tests according to JIS A 1149-2010.

2.3.2. Drying Shrinkage Tests. The specimens were taken from water at 7 days and then stored at 20[degrees]C and 60% R.H. in air, and were measured their length change and weight loss for 13 weeks according to JIS A 1129-1-2010.

2.3.3. Accelerating Carbonation Tests. After being moist-cured for 28 days and air-dried for 28 days, the specimens were stored in accelerating carbonation chamber at 20[degrees]C, 60% R.H., and 5% C[O.sub.2] concentration according to JIS A11532012. Carbonation depth was determined by phenolphthalein test on sprinkled surface.

2.3.4. Freezing-Thawing Tests. The specimens were subjected to freezing-thawing cycles at the age of 28 days according to ASTM C666/C666M-2003(2008) or JIS A 1148-2010.

3. Test Results and Discussions

3.1. Compressive Strength. Figure 1 shows the compressive strength development of concrete (at W/B = 50%, cured in water at 20[degrees]C). The compressive strength of concrete reduces with the increase of fly ash replacement ratio. This result is not related to water-binder ratio and the presence or absence of durability improving admixture and air content. However, compressive strength growth of concrete is found to be increased with the increase of fly ash replacement ratio after 28 days. The relationship of cement-water ratio and compressive strength and the relationship of binder-water ratio and compressive strength are shown in Figure 2. Since the compressive strength development has no difference between PL and D concrete (nonair-entraining type), both are expressed as an approximate straight line in this figure. Until the age of 28 days, a high correlation is shown between cement-water ratio and compressive strength, regardless of fly ash replacement ratio. After 28 days, however, because the assistance of pozzolanic reaction of fly ash to strength increasing, the correlation between cement-water ratio and compressive strength is poor. Even though there is high correlation between binder-water ratio and compressive strength over a longer period more than 1 year [20], it is unrealistic to evaluate its strength development in short term of 91 days. Also, the effects of air content are as follows: (1) compressive strength of nonair-entraining concrete (D, PL) is 10% higher than air-entraining concrete (ST); (2) to achieve the same strength, the water-cement ratio of nonair-entraining concrete can be increased by around 5%. The correlation between binder-water ratio and compressive strength is higher in the same fly ash replacement ratio. The compressive strength of nonair-entraining concrete (D, PL) is 10%-20% stronger than air-entraining concrete (ST) in the same binder-water ratio depending on the presence or absence of air content (at W/B = 50% or W/B = 43%).

3.2. Tensile Strength and Modulus of Elasticity. Figure 3 shows the relationship between compressive strength and tensile strength. The values of the 28-day tensile strength cured at about 20[degrees]C are in the range of 1/10 to 1/20 in compressive strength. Irrespective of the presence of air content, durability improving admixture, or fly ash replacement ratio, it can be seen that tensile strength is dependent on compressive strength. Figure 4 shows the relationship between compressive strength and modulus of elasticity. The modulus of elasticity of concrete is approximately 3.1 x [10.sup.4] N/[mm.sup.2] at 28 days. Modulus of elasticity showed the same tendency as tensile strength.

3.3. Drying Shrinkage. Upon Figures 5 and 6, drying shrinkage of nonair-entraining concrete (PL) is slightly less than air-entraining concrete (ST), because of differences in air content. From Figure 6, it is also observed that drying shrinkage decreases slightly with the increase of precuring period. On the other hand, when durability improving admixture is used, a significant effect is confirmed in reducing drying shrinkage. Compared to those materials where durability improving admixture is not used, it is possible to suppress change in length by around 60% using durability improving admixture [21]. Figure 7 shows the relation between mass loss and drying shrinkage. There is a clear difference of drying shrinkage in the same mass loss; drying shrinkage of D concrete is much less than PL and ST concrete. It is considered that glycol ether derivative as the main ingredient of durability improving admixture reduces surface tension of the capillary void water, lowers capillary tension, and then greatly reduces drying shrinkage. Furthermore, the reason that mass loss of D concrete is smaller than other concretes in the early age can be considered that most of glycol ether derivative is left in concrete (since only 1% of glycol ether derivative is soluble in water) to prevent capillary void water drying. As can be seen from Figure 15 on void distribution of concrete, the durability improving admixture itself remains in the capillary and gel voids within the concrete. It is assumed that drying shrinkage is reduced by glycol ether derivative suffusing those pores of 10 nm or less that have especially large capillary tension.

3.4. Carbonation Acceleration Experiment. By means of conventional carbonation rate method, the carbonation depth is expressed by (1) given below 22]. Consider

C = A[square root of t], (1)

where C: carbonation depth, mm, t: elapsed time, week, and A: carbonation rate, mm/ [square root of week].

Figure 8 shows the results of carbonation depth by accelerating carbonation test. Carbonation depth is found to be increased with mixing fly ash and decreased with the decreases of water-binder ratio. Moreover, in the case of using ordinary cement, the carbonation depth of air-entraining concrete is slightly larger than nonair-entraining concrete [23]. However, this experiment results show that carbonation depth of nonair-entraining concrete is far less than air-entraining concrete regardless of water-binder ratio. This can be considered that the concrete structure is more compact due to nonair-entraining capability and then inhibited the carbonization.

Figure 9 shows the relation between water-cement ratio and carbonation velocity coefficient which derived from linear regression of Figure 8. The carbonation velocity coefficient is expressed by (2) given below. Consider

x = A [square root t]t + B, (2)

where x: carbonation velocity coefficient; A: carbonation-rate, mm/[square root of week]; B: carbonation depth at the start of carbonation acceleration, mm.

After 4 weeks of curing in water and 4 weeks of curing in air, because the self-carbonation caused by pozzolanic reaction of fly ash is negligible, it is considered that carbonation velocity coefficient is roughly equal in the same water-cement ratio regardless of fly ash replacement ratio. The ratio of carbonation velocity coefficient of fly ash concrete is ST : PL: D = 18.2 : 13.3 : 11.6 = 1.0 :0.7:0.6. It indicates that nonair-entraining mode can significantly reduce the carbonation rate.

The carbonation acceleration experiment is an experiment in raising the carbon dioxide concentration in the surrounding atmosphere, which accelerated carbonation of the concrete and evaluated anticarbonation ability by measuring carbonation depth. In this experiment, 4 different types of precuring carbonation acceleration experiment were applied for water-binder ratio of 50%. Among them, there are initial curing methods I: after 28 days of curing in water then curing in air for 28 days, initial curing methods II: after 28 days of curing in water then curing in seal for 63 days, and finally curing in air for 28 days; initial curing methods III: after 28 days of curing in water then curing in air for 91 days; and initial curing methods IV: after 7 days of curing in water then curing in air for 91 days. Figure 10 shows the relationship between fly ash replacement ratio of different precuring pattern and carbonation velocity coefficient. From this figure, owing to the different precuring mode, carbonation velocity coefficients of PL and ST concrete without adding fly ash were largely affected by precuring, unrelated to the air content. However, carbonation velocity coefficient with fly ash replacement cement reached the same level unrelated to precuring method and period. In other words, for more than 15% of fly ash replacement ratio in concrete, it can be considered that larger carbonation velocity coefficient was affected by self-carbonation of fly ash compared to influence of precuring. From the above results, carbonation acceleration experiment of concrete with more than 15% fly ash replacement ratio depends on the carbonation depth at the start.

3.5. Freezing-Thawing Resistance. In this experiment, 3 different types of precuring freezing-thawing experiments were applied. Among them, there are initial curing methods A: curing in air for 28 days; initial curing methods B: after 28 days of curing in water then curing in air for 14 days; and initial curing methods C: after 28 days of curing in water then curing in air for 28 days.

Figure 11 shows the relation between air content after hardening and the durability index, and Figure 12 shows the relationship between water-cement ratio and the durability index. As shown in Figure 11, regardless of water-binder ratio and fly ash replacement ratio, ST concrete shows favorable freezing-thawing resistance. On the other hand, in this experiment, the durability index of nonair-entraining concrete is below 40% with 4 weeks of water immersion in the precuring stage. However, when durability improving admixture is used, freezing-thawing resistance improved substantially by conducting the drying process for 2 weeks in the precuring stage even in nonair-entraining concrete, regardless of water-binder ratio. In addition, from Figure 12 it can be observed that even the drying process is conducted for PL concrete, and freezing-thawing resistance will not be improved. However, to ensure the water-cement ratio of 60%, freezing-thawing index of concrete with durability improving admixture used can reach above 60%, regardless of the length of the drying process. Considering the curing period in actual construction work which is very short and concrete is stripped after casting and exposed in air, fly ash concrete can be durable to freezing-thawing with the use of durability improving admixture and ensure the proper water-cement ratio, even when using nonair-entraining type [24].

3.6. Characteristics of Air Bubbles. Figure 13 shows the relationship between air bubble diameters and quantity of air bubbles, and Figure 14 shows the relationship between the air void spacing factor and the durability index. It is clear that the number of air bubbles is greater and the average diameter is smaller with durability improving admixture used, compared to PL concrete. The influence of mixing in fly ash is that there is a tendency for the number of air bubbles to increase and the air void spacing factor decreased with the increase of fly ash replacement ratio, without regard to the amount of air or the use of durability improving admixture. The air void spacing factor with durability improving admixture used is lower than 200-250 [micro]m of antifreeze damage index as shown in Figure 14. In addition, there is a strong defoaming reaction of durability improving admixture, which can drive out coarse air bubbles over 500 [micro]m. The air content of fresh concrete is the same in PL and D concrete, but the content of air in D concrete becomes 0.5-1.0% greater. This is considered that the glycol ether derivative of the durability improving admixture exists in hardened concrete in the form of tiny droplets under 150 [micro]m. Here, the mechanism of durability improvement is discussed in the perspective of air bubble system. By 2-week drying process in precuring, resistance to freeze damage is improved significantly. When void water dried, a part of glycol ether derivative in the concrete is taken into capillary and gel air cavities, and the original oil specks perform the same function as air bubbles, easing water freeze expansion. It is thought that this improves the resistance to freeze damage.

Concerning the effect of durability improving admixture in preventing freeze damage, a significant improvement is noted by 2-week drying process in precuring. Considering cavity distribution in concrete, when durability improvement admixture is used, as shown in Figure 15, by its strong bubble elimination action, the admixture reduces the entrapped air and replaces it with the same amount of entrained air bearing 250 [micro]m or less of oil specks into the hardened concrete. Furthermore, accompanying the drying of void water, by injecting a portion into capillary cavities, shrinkage is lowered. The same reaction occurs in gel cavities, which are the lamellar cavities formed in lamellar crystal while C-S-H hydrate is produced. It is believed that hardened concrete is formed and durability is improved through these processes. Figure 15 shows concrete cavity distribution when durability improving admixture is used.

4. Conclusions

The following conclusions were drawn from the work presented above on the effects of durability improving admixture, air content, water-binder ratio, and fly ash replacement ratio on fly ash concrete properties.

(1) By using durability improving admixture in nonair-entraining fly ash concrete, the compressive strength of fly ash concrete can be improved by 10%-20%, and its initial compressive strength improved also.

(2) Irrespective of the presence of air, durability improving admixture, or fly ash replacement ratio, both tensile strength and modulus of elasticity are dependent on compressive strength.

(3) By using durability improving admixture in fly ash concrete, the drying shrinkage is reduced by 60%.

(4) Carbonation resistance of concrete is roughly proportional to water-cement ratio regardless of waterbinder ratio and fly ash replacement ratio. The ratio of carbonation velocity coefficient of fly ash concrete is ST:PL:D = 1.0: 0.7: 0.6. Also, carbonation acceleration experiment of concrete with more than 15% fly ash replacement ratio depends on the carbonation depth at the start.

(5) By using durability improving admixture for 2 weeks of curing in air (drying process), the freezing-thawing resistance can be improved even in nonair-entraining concrete.

By making use of durability improving admixture, it is easier to control the air content and make fly ash concrete into nonair-entraining one. The quality of fly ash concrete is thereby optimized. In the field of application fly ash concrete, the use of nonair-entraining mode and durability improving admixture is a valuable option.

http://dx.doi.org/10.1155/2014/818103

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

References

[1] G. Li, "Sulfate resistance of fly ash concrete," Journal of the Chinese Ceramic Society, vol. 40, no. 1, pp. 39-48, 2012 (Chinese).

[2] V. M. Malhotra and P. K. Mehta, High-Performance, High-Volume Fly Ash Concrete, Marquardt Printing Ltd., Ottawa, Canada, 2002.

[3] W. Khaliq and V. Kodur, "Behavior of high strength fly ash concrete columns under fire conditions," Materials and Structures, vol. 46, no. 5, pp. 857-867, 2013.

[4] W. Chalee, M. Teekavanit, K. Kiattikomol, A. Siripanichgorn, and C. Jaturapitakkul, "Effect of W/C ratio on covering depth of fly ash concrete in marine environment," Construction and Building Materials, vol. 21, no. 5, pp. 965-971, 2007.

[5] J. Huang and H. Su, "Application for fly ash concrete in pavement engineering," Advanced Materials Research, vol. 510, pp. 817-821, 2012.

[6] J. Niu, H. Zhai, and D. Niu, "Experimental study on the carbonation of fly ash concrete," in Proceedings of the International Conference on Consumer Electronics, Communications and Networks (CECNet '11), pp. 2221-2224, April 2011 (Chinese).

[7] W. Chalee, P. Ausapanit, and C. Jaturapitakkul, "Utilization of fly ash concrete in marine environment for long term design life analysis," Materials & Design, vol. 31, no. 3, pp. 1242-1249, 2010.

[8] J.-H. Liu, Y.-M. Sun, S.-M. Song, X.-M. Xu, and Y.-A. Xiong, "The study on reactivity and high-strength mechanism of modified fly-ash concrete," in Proceedings of the Asia-Pacific Power and Energy Engineering Conference (APPEEC '10), pp. 14, March 2010.

[9] D. P. Bentz, M. A. Peltz, A. Duran-Herrera, P. Valdez, and C. A. Juarez, "Thermal properties of high-volume fly ash mortars and concretes," Journal of Building Physics, vol. 34, no. 3, pp. 263275, 2011.

[10] P. Zhang, Q. Li, and Z. Sun, "Influence of silica fume and polypropylene fiber on fracture properties of concrete composite containing fly ash," Journal of Reinforced Plastics and Composites, vol. 30, no. 24, pp. 1977-1988, 2011.

[11] Y. Ishikawa, S. Takada, and H. Kasami, "Research on the quality distribution of JIS type-II fly ash," AIJ Journal of Technology and Design, no. 24, pp. 1-4, 2006 (Japanese).

[12] Y. Ishikawa, "A basic study on activity index in Japanese industrial standard of fly ash for use in concrete," AIJ Journal of Technology and Design, vol. 18, no. 40, pp. 819-822, 2012 (Japanese).

[13] H. Z. Quan and H. Kasami, "Experimental study on effects of the type and replacement ratio of fly ash on strength and durability of concrete," Journal of Structural and Construction Engineering, no. 602, pp. 1-7, 2006 (Japanese).

[14] K. Funamoto, "Study on compressive strength development of concrete with type-II fly-ash in standard curing," AIJ Journal of Technology and Design, vol. 15, no. 31, pp. 627-630, 2009 (Japanese).

[15] H. Quan, "The effects of change in fineness of fly ash on air-entraining concrete," The Open Civil Engineering Journal, vol. 5, no. 1, pp. 124-131, 2011.

[16] H. Quan, "Research on durability of high volume fly ash concrete," Applied Mechanics and Materials, vol. 174-177, pp. 380-383, 2012.

[17] S. Rukzon and P. Chindaprasirt, "Development of classified fly ash as a pozzolanic material," Journal of Applied Sciences, vol. 8, no. 6, pp. 1097-1102, 2008.

[18] M. Hisaka, T. Mano, and M. Shiraiwa, "Study on the effect of coal ash on the air-entraining properties of concrete," Transaction of Cement and Concrete, no. 51, pp. 132-137, 1997 (Japanese).

[19] J. John, T. M. Maya, and T. Meenambal, "Mathematical modeling for durability characteristics of fly ash concrete," International Journal of Engineering Science and Technology, vol. 4, no. 1, 2012.

[20] K. Hwang, T. Noguchi, and F. Tomosawa, "Microstructural approach to compressive strength of high volume fly ash concrete," Journal of Structural and Construction Engineering, no. 571, pp. 11-16, 1999 (Japanese).

[21] M. Sugiyama, K. Tanaka, M. Sakuta, and T. Urano, "Basic properties of concrete using admixtures to decrease drying shrinkage," Proceedings of the Japan Concrete Institute, vol. 8, pp. 281-284, 1986 (Japanese).

[22] M. Hamada, "Carbonation of concrete and corrosion of reinforcing steel," in Proceedings of the Cement Association of Japan, Cement & Concrete, vol. 272, pp. 2-18, October 1969 (Japanese).

[23] I. Izumi, F. Oshida, and H. Kasami, "Cement types, blends and curing conditions influencing concrete carbonation," Proceedings of the Japan Concrete Institute, vol. 7, pp. 117-120, 1985 (Japanese).

[24] Y. Takada, H. Nishi, H. Quan, and H. Kasami, "Study of the quality improvement of fly ash concrete with durability improving admixture," in Proceedings of the Annual Meeting of the Architectural Institute of Japan, pp. 8-14, August 2004 (Japanese).

Hong-zhu Quan (1) and Hideo Kasami (2)

(1) School of Architectural Engineering, Qingdao Agricultural University, Qingdao 266109, China

(2) Japan Association for Building Research Promotion, Tokyo 108-0014, Japan

Correspondence should be addressed to Hong-zhu Quan; quanhz719@aliyun.com

Received 29 January 2014; Accepted 4 May 2014; Published 9 June 2014

Academic Editors: A. Esmaeily, A. K. Gupta, J. Kinuthia, and A. Rodriguez-Castellanos

TABLE 1: Characteristics of materials used.

Cement             Ordinary Portland cement Density: 3.16
                   g/[cm.sup.3]; specific surface area:
                   3280 [cm.sup.2]/g
Binder             Fly ash
Fine aggregate     Mountain sand Density in oven-dried condition:
                   2.56 g/[cm.sup.3]; water absorption: 1.72%;
                   fineness modulus: 2.67
Coarse aggregate   Crushed stone Density in oven-dried condition:
                   2.64 g/[cm.sup.3]; water absorption: 0.81%;
                   maximum size: 20 mm
Admixture          Air-entraining and water reducing admixture
                   Air-entraining admixture for fly ash: nonionic
                   surface active agent Durability improving
                   admixture: glycol ether derivative
                   (nonwater solution)

TABLE 2: Properties of fly ash used.

Ignition loss      Density       Blaine's value   MB absorption
[%]             [g/[cm.sup.3]]   [[cm.sup.2]/g]      [mg/g]

1.4                  2.24             4160            0.51

TABLE 3: Experiment factors and ratios.

Experiment factors                               Levels

Fly ash replacement ratio                     0%; 15%; 25%
Water-binder ratio                            60%; 50%; 43%
Air content                       1.5 [+ or -] 0.5%; 4.5 [+ or -] 0.5%
Durability improving admixture       0kg/[m.sup.3]; 10 kg/[m.sup.3]

TABLE 4: Mixture proportion and properties of fresh and
hardened concrete.

             W/B    W/C    FA/B
             (%)    (%)     (%)

Af0-60PL             60      0
Af0-60ST
Af15-60D      60     71     15
Af15-60ST
Af25-60D
Af25-60ST            80     25

Af0-50PL
Af0-50D              50      0
Af0-50ST
Af15-50PL
Af15-50D      50     59     15
Af15-50ST
Af25-50PL
Af25-50D             67     25
Af25-50ST

Af0-43PL             43      0
Af0-43ST
Af15-43D      43     51     15
Af15-43ST
Af25-43D             57     25
Af25-43ST

               Mixture proportion (kg/[m.sup.3])

              W      C     FA     S       G      D

Af0-60PL     182    303     0    856            --
Af0-60ST     170    283     0    813            --
Af15-60D     166    235    42    880    1014    10
Af15-60ST    166    235    42    815            --
Af25-60D     164    205    68    879            10
Af25-60ST    167    209    70    801            --

Af0-50PL     182    364     0    806            --
Af0-50D      174    348     0    814            10
Af0-50ST     170    340     0    766            --
Af15-50PL    174    296    52    823            --
Af15-50D     166    282    50    831    1014    10
Af15-50ST    166    282    50    766            --
Af25-50PL    172    258    86    820            --
Af25-50D     164    246    82    829            10
Af25-50ST    167    251    84    751            --

Af0-43PL     189    440     0    726            --
Af0-43ST     178    414     0    684            --
Af15-43D     173    342    60    752    1014    10
Af15-43ST    176    348    61    673            --
Af25-43D     171    298    99    748            10
Af25-43ST    177    309    103   655            --

                                        Compressive strength
                Fresh concrete            (N/[mm.sup.2])

             Slump (cm)   Air (%)   7 days    28 days   91 days

Af0-60PL        19.0        1.7      26.0      35.5      41.0
Af0-60ST        18.1        4.0      25.3      36.1      38.7
Af15-60D        18.6        1.4      20.7      29.2      40.6
Af15-60ST       18.6        4.2      17.6      27.7      35.8
Af25-60D        18.2        1.5      12.3      20.4      26.8
Af25-60ST       17.0        4.1      13.7      22.6      32.4

Af0-50PL        18.8        1.4      36.1      47.5      53.0
Af0-50D         18.7        1.0      35.8      46.4      54.1
Af0-50ST        18.7        4.4      33.3      45.5      50.4
Af15-50PL       18.5        1.7      30.3      43.2      55.6
Af15-50D        18.2        1.2      28.6      38.3      51.4
Af15-50ST       18.2        4.5      25.0      36.5      45.8
Af25-50PL       18.5        1.6      26.3      34.5      51.4
Af25-50D        17.7        1.5      22.8      33.8      43.7
Af25-50ST       18.6        4.1      20.2      31.3      43.1

Af0-43PL        19.2        1.5      45.4      57.8      68.1
Af0-43ST        18.3        4.5      38.7      50.7      56.5
Af15-43D        17.8        1.3      35.0      47.9      53.0
Af15-43ST       17.7        4.5      31.9      43.9      55.0
Af25-43D        17.8        1.6      30.0      42.6      55.3
Af25-43ST       18.3        4.4      26.6      37.6      48.6

Notes: W/B, W/C, and FA/B are, respectively, means of water-binder
ratio, water-cement ratio, and fly ash binder ratio. W, C, FA, S, G,
and D are, respectively, means of water, cement, fly ash, fine
aggregate, coarse aggregate, and durability improving admixture.
COPYRIGHT 2014 Hindawi Limited
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2014 Gale, Cengage Learning. All rights reserved.

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:Research Article
Author:Quan, Hong-zhu; Kasami, Hideo
Publication:The Scientific World Journal
Article Type:Report
Date:Jan 1, 2014
Words:4472
Previous Article:The epiphytic fern Elaphoglossum luridum (Fee) Christ.
Next Article:Experimental investigation of the flow on a simple frigate shape (SFS).
Topics:

Terms of use | Privacy policy | Copyright © 2019 Farlex, Inc. | Feedback | For webmasters