Effects of aluminum on hydrogen solubility and diffusion in deformed Fe-Mn alloys.

1. Introduction

High strength structural steels are a material class key to further developments in automotive light-weight construction [1-3]. At Mn weight fractions between 15 and 25 percent, high manganese steels offer a combination of high strength and desirable plasticity characteristics. The stable austenitic structure offers high cost efficiency [4-8], and investigations on Fe-Mn systems revealed the relation of high work hardening rates and ductility to the austenitic microstructure [9,10]. In addition, high manganese steels exhibit a lower susceptibility to hydrogen embrittlement [11] than ferritic and martensitic steels [12,13].

The systematic investigation of hydrogen embrittlement in high manganese steels is challenged by the microstructural, interfacial, and chemical complexity of these materials. The scientific focus has been on intergranular failure modes and general heterophase interface failure [14-18]. Hydrogen induced degradation [19] is a major hindrance for the implementation of promising steel designs for automotive applications [20]. While the austenitic phase itself exhibits low diffusivity and high solubility of hydrogen, the transformation induced plasticity (TRIP) moderated martensitic transformation yields strong gradients of solubility and diffusivity due to the presence of ferritic phases.

An improved resistance to hydrogen induced delayed fracture can be realised by adding temper softeners like Cr, Mo, and V in martensitic steels. This highly desirable effect originates from the suppressed fracture by carbide precipitation, shifting the intergranular fracture to intragranular fracture [21]. In austenitic steels, the addition of Ni and Si is an established method to increase the ductility of hydrogen-loaded steels [22-25], and the beneficial effect of Mn on hydrogen solubility has been investigated for instance in [26, 27]. The successful alloying of high manganese steels with Al, which reduces the weakness against hydrogen embrittlement, suggests studying the effect of Al on the different aspects of hydrogen in Fe-Mn systems. As it is an integral part of production processes, we also study the influence of mechanical loading, in practice isotropic and tetragonal distortions, on solubility and mobility of hydrogen.

The article is organized as follows. In Section 2 we describe the methodical basis of our approach, including several aspects of the systematic approximations we make. Section 3 contains the results of our investigations, where we distinguish between stress-free, isotropically distorted, and tetragonally distorted systems and discuss their influence on hydrogen solubility and diffusivity. Finally we conclude with a brief discussion of the presented results in the context of different material configurations and future perspectives.

2. Methods

The methodical basis of our investigation is electronic structure density functional theory (DFT). It allows predicting the quantities of interest for exactly defined crystal geometries and chemical compositions. The systems which we investigate are introduced in Figures 1 and 2. They consist of 2 x 2 x 2 supercells of an austenitic [Fe.sub.24][Mn.sub.8] matrix and the resulting system when we substitute one Fe atom by an Al atom, [Fe.sub.23][Mn.sub.8]Al. Hydrogen is introduced on interstitial sites. We obtained our ab initio results from DFT calculations employing the Vienna ab initio simulation package (VASP) [28]. For the PAW pseudopotentials [29] we use the GGA-PBE exchange and correlation functional [30]. The convergence of DFT related parameters has been carefully tested. We find that an 8 x 8 x 8 k-point Monkhorst-Pack [31] mesh for the 2 x 2 x 2 supercell and a plane wave energy cutoff of 600 eV are sufficient to ensure a convergence of the calculated formation energies to better than 10 meV. An electronic smearing of 0.1 eV was chosen within the Methfessel-Paxton scheme [32]. Further, subject-specific numerical details will be discussed at the appropriate places of this publication.

3. Results

3.1. Hydrogen Solubility. The goal of this section is to determine the concentration of hydrogen as solid solution in the fcc Fe-Mn-Al system. Two aspects are of primary interest here: first, the local arrangement of the hydrogen atoms in the interstitial sites in different environments of iron, manganese, and aluminum, to find a site preference for the hydrogen; second, the dependence of the solubility on mechanical deformation conditions, in particular for pure volume changes due to isotropic straining and for volume-conserving tetragonal distortions.

The central quantity required to determine the equilibrium hydrogen concentrations is the solution energy, which is defined as


Here, [E.sub.MH][[sigma]] is the energy of the metal-hydrogen system, where a denotes the occupied interstitial site of the hydrogen, as illustrated in Figure 2. [E.sub.M] is the energy of the purely metallic alloy system, and [MATHEMATICAL EXPRESSION NOT REPRODUCIBLE IN ASCII] is the reference potential for half an isolated [H.sub.2] molecule. We note that for vanishing external stress the solution energy and enthalpy coincide. This energy difference Ea will in the following be computed using ab initio techniques. It serves as an input for the calculation of the equilibrium hydrogen concentration (or occupation probability for the different interstices), which is in the dilute limit of noninteracting hydrogen atoms given by Sievert's law [33]:


where [MATHEMATICAL EXPRESSION NOT REPRODUCIBLE IN ASCII] is the partial pressure of the surrounding [H.sub.2] gas. We have to distinguish this pressure from a mechanical pressure P acting on the solid solution phase, which can be independently controlled by mechanical constraints. In the following, we will focus on the mechanical part and not further discuss the gas pressure [MATHEMATICAL EXPRESSION NOT REPRODUCIBLE IN ASCII]. The value of the (suppressed) proportionality constant in the above expression (2) depends on the choice of a reference pressure and the precise definition of the hydrogen concentration.

3.1.1. Stress-Free Systems. We calculate the energy contributions mh and EM for the supercells shown in Figures 1 and 2, using full ionic relaxation and vanishing external (mechanical) pressure, P = 0. In this case the solution energies are identical to the solution enthalpies. The resulting values are given in Table 1.

For the Fe-Mn reference system we only consider those octahedral sites which exhibit the energetically most favorable chemical neighbourhood, where the hydrogen atom is surrounded by 4 iron and 2 manganese atoms; see Figure 1. Such a site exists 24 times in the [Fe.sub.24][Mn.sub.8] supercell. The other type of octahedral sites, where the H atom is surrounded by 6 Fe atoms, exists 8 times but has a higher solution energy when the system is deformed.

This energyis compared to different atomic arrangements for a [Fe.sub.23][Mn.sub.8]Al system, where one iron atom is replaced by aluminum. For this configuration, there are four chemically inequivalent environments for the H atom, as depicted in Figure 2. For the configuration denoted by "oc1" the nearest neighbours of the H atom are 3 Fe and 2 Mn atoms and one Al atom, which exists four times in the supercell. The configuration "oc2" has the neighbourhood 4 Fe, 2 Mn, and 0 Al, with a multiplicity of 20. "oc3" has the environment 6 Fe, 0 Mn, and 0 Al, and it exists six times. Finally, "oc4" has 5 Fe, 0 Mn, and 1 Al neighbours and exists twice. Apart from the chemical environment, also the local geometric arrangement influences the solution energies. In the case of the "oc2" configuration, which is of specific interest due to its energetic preferability, we find the most attractive local arrangement in 9 of the 20 sites. The resulting 11 sites are less attractive and split into three subgroups of local geometric arrangements. The resulting solution energies for the most attractive sites for each chemical environment are listed in Table 1.

By comparison to the reference system [Fe.sub.24][Mn.sub.8], we see that there are two types of interstices with identical next neighbour configuration there and in [Fe.sub.23] Mn,Al. The oc2 site is energetically more favorable by about 60 meV than the reference site with 4 Fe and 2 Mn atoms as nearest neighbour. This is attributed to the nonlocal effect of the substitutional Al atom. The oc3 site is about 70 meV less attractive than the reference site with 6 Fe atoms as nearest neighbour, which has nearly the same energy as the reference site with 4 Fe and 2 Mn atoms in the immediate neighbourhood. This discrepancy shows that the solution energy is lowest in a manganese rich environment, which is in agreement with the predictions in [26,27]. It also exhibits that, in the [Fe.sub.23][Mn.sub.8]Al system, the volumetric effect of the Mn atoms is limited to the direct vicinity of the Mn atoms.

The general observation is, therefore, that Al atoms as next neighbour make octahedral sites energetically less favorable. We can therefore conclude that for low temperatures and hydrogen concentrations the sites close to aluminum atoms will not be populated. In the room temperature regime with kBT 25 meV the occupation probability ratio of the energetically most attractive oc2 configuration of the Fe-MnAl system in comparison to the Fe-Mn reference system is therefore according to (2) given by


where the factor roc2/ref takes into account the multiplicity of the amount of reference sites and relevant "oc2" sites.

Since for chemical trends only differences of solution energies are important, not the absolute values, the contribution of quantum mechanical zero point vibrations is neglected. In fact, they turn out to be only about 0.02 eV as upper limit, for example, for Fe1-XMr, at x = 0,1 as reported in [26]. Similar to the arguments in [26] we can therefore ignore this contribution.

In the calculations we have ignored magnetic effects. The antiferromagnetic double layer ordering has been shown to be the energetically most stable collinear configuration [34] and a good approximation to the true ground state in y Fe. However, we recall that two important effects of magnetism, namely, the repulsion of the hydrogen atoms by the magnetic moment and the increased interstitial volume due to the larger lattice constant with increasing magnetic ordering--from nonmagnetic, via antiferromagnetic to ferromagnetic--are large by magnitude, but they mainly compensate each other. While this assumption is sufficient here, we refer to [26,35] for details about the nonmagnetic approximation. For a recent review on ab initio modelling of magnetism in steels see [36]. Taking paramagnetism into account will be part of our future work to clarify the role of magnetic interactions on hydrogen bonding and diffusion.

3.1.2. Isotropic Deformation. In contrast to the calculations above, where we used a fixed pressure P = 0, we now fix the volume of the supercell. This means that we evaluate the energies MH[<r] and EM both at the same lattice constant. Specifically, for the equilibrium lattice constant of the system with hydrogen, the purely metallic system is therefore under tension and has a higher energy due to these elastic effects, compared to the results in Table 1, where both energies were calculated at their individual equilibrium volumes. Consequently, the solution energies are lower for the present fixed volume boundary conditions.

For isotropic deformations we strain the supercell equally in all three principal directions, which can be described by the diagonal transformation tensor


The resulting solution energies are shown in Figure 3 for the different configurations in Figures 1 and 2. The first observation is that to good accuracy all energies follow a linear behavior in the interval of investigated lattice constants [] with almost the same slope, hence only having a parallel offset. This is in agreement with the generic picture that hydrogen mainly leads to an isotropic expansion of the stress-free system by an amount AV, which differs only weakly for different metals [37]. Hence the coupling to an isotropic strain leads to an energy term proportional to P[DELTA]V. With the pressure P being proportional to the deviation of the lattice constant from its equilibrium value, we therefore expect a linear dependence of the solution energy on the lattice constant.

We can further support this picture by a separation of the solution energy in a volumetric (elastic) and a chemical contribution, as indicated by the vertical and horizontal arrows in Figure 3, respectively. For the volumetric contribution we consider the hydrogen solution energy difference of the chemically identical system, but evaluated once at its equilibrium lattice constant and once at the lattice constant of the Al free reference system. Hence, this energy difference contains the release of mechanical work due to the adjustment to the appropriate lattice constant. In contrast, the chemical contribution is calculated from the solution energy difference of two chemically different systems, namely, the Fe-Mn-Al and the Fe-Mn systems, but this time evaluated at the same lattice constant. Hence, this energy contribution expresses the energy difference for insertion of a single hydrogen atom into the same rigid atomic structure, but with different chemical environment due to the exchange of Fe by Al.

As can be seen from Figure 3 exemplarily for the configurations oc1 and oc2, the volumetric contribution is basically identical, in agreement with the above argument, but the chemical contributions differ significantly. This difference is in line with the stress-free results in Table 1. Therefore, also under isotropic strain, we find that hydrogen prefers a direct environment which does not contain aluminum.

3.1.3. Tetragonal Deformation. Again, the starting point for the consideration is the system with a [Fe.sub.24][Mn.sub.8] supercell with cubic symmetry. By the substitution of one of the Fe atoms by Al, the supercell experiences in equilibrium a shape relaxation with a slight tetragonal distortion. On a larger scale the Al atoms will be randomly distributed, and therefore the effects from the different specific arrangement will average out. As a result, the supercells will mainly preserve their cubic shape, which we take as basis for additional external tetragonal distortions.

In contrast to the isotropic deformations in the previous section we consider here a case where the distortion is volume-conserving, to clearly demonstrate the different behavior. For that, the supercell undergoes a transformation as described by the tensor


which is volume-conserving up to third order in the tetragonal strain [delta]. The supercell is stretched in two principal directions and compressed in the other. The aforementioned dependence of the small intrinsic tetragonal distortion is equivalent to the application of different directions of the compression. The resulting energy curves as function of the tetragonal strain 5 are shown in Figure 4 for the [Fe.sub.23][Mn.sub.8]AlH supercell in configuration oc1. It shows the characteristic quadratic dependence of the elastic energy as function of strain when deformed from the cubic reference state. The dashed curve is the arithmetic means of the cases with the three different orientations of the principal axes and reflects the averaged elastic response for a larger system with random distributions. Such an averaging will therefore also be employed for the following calculations, while we still distinguish between the different configurations shown in Figure 2.

Similar to the isotropic case we computed the hydrogen solution energy as function of the tetragonal distortion, and the results are shown in Figure 5. Obviously, the behavior is very different than for the isotropic deformation in Figure 3. For that we note that the considered strain interval [DELTA][delta] = 0.06 in the present plot is much larger than in the previous one, where we had [DELTA][delta] = 0.017. Still, the energetic variation is much smaller here, despite the larger strain interval. Together with the shape of the curves we can therefore conclude that strain effects to the solution energy are a higher order correction here. This is in agreement with the argument above that the interstitial hydrogen mainly leads to an isotropic expansion of the system, and therefore it only weakly interacts with a volume-conserving external strain.

As a result, the chemical influence of the Al atom is clearly dominant compared to the contributions from the tetragonal deformation. The hydrogen sites in the vicinity of the Al atom, oc1 and oc4, exhibit solution energies which are not distinguishable within the accuracy limits of our approach. The oc3 site is comparably attractive as the reference site, while the oc2 site exhibits the shift of about -60 meV relative to the reference system basically over the full range of tetragonal deformations.

3.2. Hydrogen Diffusion. In this section we intend to obtain information on the hydrogen diffusion coefficient for different strain states and to understand the influence of aluminum. For that, we consider diffusion of hydrogen in the Fe-Mn(-Al) matrix via trap site and Einstein diffusion. To discuss the influence of aluminum induced trapping we apply Oriani's theory [38], which is applicable when the trap sites and the regular lattice sites for the diffusing species are in local equilibrium. The term local equilibrium means that the kinetics of the equilibration of the regular sites and trap sites are described by sufficiently separated timescales. Then, important parameters are the solution energies and the trap densities. This allows drawing conclusions on the relative change of the diffusion coefficients depending on composition and strain.

For Einstein diffusion, we obtain estimates for the changes of the diffusion coefficients based on the diffusion barriers of the involved transition paths. We employ climbing image nudged elastic band calculations (CINEB) [39, 40], which search the saddle point of the reaction path, that is, the barrier between two connected sites.

In the spirit of the above discussion we use initial octahedral and final tetrahedral states of the reaction path with cubic cell symmetry and averaged lattice constants and therefore can refrain from using solid state nudged elastic band calculations [41]. The energy difference due to the averaged lattice constant--for example, aat = 3.502 [angstrom] for Mn32 H with hydrogen in an octahedral position and [] = 3.506 A for occupation of a tetrahedral site, leading to an averaged value alat = 3.504 A--is in the range of 5meV. We used Mn32H to test the validity of this approximation against available data on transition points and found good agreement [26]. Here alat for the [Fe.sub.23][Mn.sub.8]Al system is chosen to minimize the error in the energies. For TWIP steels, it would need to be adjusted to other values. We also have checked the convergence of the CINEB calculations with respect to the number of images which initially discretize the transition path.

3.2.1. Stress-Free Systems. The oc2 sites are traps with a strain dependent binding energy. In absence of any deformation they have a depth of 60 meV, relative to the sites in the reference system [Fe.sub.24][Mn.sub.8]. There are 20 possible hydrogen oc2 sites which are preferential and we assume that at most half of them are accessible due to the indirect hydrogen repulsion when placed in adjacent sites. This leads to the estimate of the trap density as [N.sub.t] = 1.34 x [10.sup.28] [m.sup.-3], and the N is the density of regular sites, with the ratio [N.sub.t]/[N.sub.l] [approximately equal to] 0.28.

The apparent diffusivity relative to the trap-free diffusivity (aluminum-free) diffusivity is according to Oriani's theory


which is plotted in Figure 6 as function of temperature. We see that the presence of aluminum suppresses the hydrogen diffusivity in the room temperature range by about one order of magnitude.

3.2.2. Isotropic Deformation. Before discussing the influence of an isotropic deformation on trap site diffusion, we mention that differences in the bulk moduli between the hydrogen-free and hydrogen-loaded systems are typically small; see Table 2. Thus, equal strains correspond in good approximation to equal pressures.

Figure 6 shows in addition to the stress-free case the ratio of the trap site diffusion coefficient according to the Oriani model for isotropic compression ([delta] = -0.01) and tension ([delta] = 0.01). This leads to a change of the diffusion coefficient relative to the case without aluminum by up to one order of magnitude at room temperature, based on the consideration of the oc2 traps. In general, a tensile strain increases the diffusion coefficient, as the larger interatomic spacing allows for easier jumps of the interstitial hydrogen via a reduction of the energy barriers.

For Einstein diffusion we focus on the configurations oc1 and oc2 and the reference case of the supercell without Al, as these are most illustrative in discussing the influence of the Al alloying with respect to deformation effects.

For isotropically strained systems with only one Al atom in the 32 atom supercell, the diffusion coefficient behaves as

D ~ [n.sub.tb][a.sup.2] exp (- [E.sub.Diff]/[k.sub.B]T), (7)

and both changes of the exponent and the preexponential factor for variations of composition and strain state have to be considered. Here, is the number of transition bonds to the next sites, a is the distance to these sites, and Diff is an effective diffusion barrier which reflects the dominant transitions contributing to the diffusion process.

In Figure 7 we show the barriers, that is, the energy difference [E.sub.Diff] between the transition and starting point, as function of lattice constant. The starting point is a hydrogen atom in position oc1, which then crosses a tetrahedral site close to the Al atom, with one Fe atom, two Mn atoms, and one Al atom as next neighbours. This initial site is relevant when local accumulations of Al yield a low density of available more attractive sites. The barrier of this transition close to the Al atom is increased by about 126 meV, which means that this transition will play a negligible role when other transitions are accessible. Under expansion, the system yields a substantial decrease of the barrier height.

The density of high-barrier transitions in the system with an Al atomic concentration of 1/32 is still low, and therefore one cannot assume that they efficiently reduce the number of transition paths from the considered site in the spirit of shutting down percolation paths. Therefore, this leads only to a weak decrease of the preexponential factor nth. However, when the number of high-barrier transition paths is increased, that is, when the atomic concentration of Al is increased to 2/32 or 3/32, the probability that only the high-barrier transitions along sites of type oc1 are accessible from a considered site increases. Under these circumstances the energy barriers related to jump processes starting at oc1 type positions become dominant, which leads to a change of the relevant exponential factor. It leads to a reduction of the diffusion coefficient relative to the aluminum-free system by a factor

exp([E.sup.oc1.sub.Diff] - [E.sup.ref.sub.Diff]/[k.sub.B]T), (8)

which can reach ~[10.sup.-3] at room temperature. The contribution of direct jumps between octahedral sites can be expected to remain negligible even at appreciable strains. The energetic penalty of this transition of about [approximately equal to]0.4-0.5 eV relative to the octahedral-tetrahedral transition and the maximal effect of the strains of about [approximately equal to]0.1-0.15 eV suggest no change of the preferred diffusion path.

3.2.3. Tetragonal Strain. We can proceed in a similar way for systems under tetragonal strain. We distinguish between the three different possible strains relative to the elastically stiff axis, as they all appear in a random distribution of Al in an FeMn-Al alloy. As expected, the effect of the deformation on the trap site diffusion is weak; see Figure 8. At room temperature, the ratio of the apparent diffusion coefficients is changed by less than order of magnitude.

The picture is different when we consider the effect of the deformation on Einstein diffusion processes. As shown in Figure 9, variations in the relative orientation of the preferred elongation axis can result in a shift of the diffusion barriers by two orders of magnitude at low temperatures. The chemical shift at zero pressure is larger, yielding a possible decrease of the diffusion coefficient in the vicinity of Al atoms up to three orders of magnitude. Again, the chemical contribution to the solution energy is dominant in the nonstressed state.

4. Summary and Conclusions

In the present paper we have discussed the influence of Al alloying and deformations on hydrogen absorption and diffusion in high manganese steels, represented by [Fe.sub.24] [Mn.sub.8] and [Fe.sub.23][Mn.sub.8]Al systems. In the considered configurations, the substitution with Al leads to two counteracting effects on the hydrogen dissolved on interstitial sites in the matrix. On the one hand, at low Al concentrations of about 3 at%, the number of trap sites, which increase the hydrogen solubility and decrease the diffusivity, is large. On the other hand, at larger Al concentrations an effective blocking of paths for the hydrogen diffusion could lead to a drastic reduction of the diffusivity, caused by the high barrier of the transition path between octahedral and tetrahedral sites in the direct vicinity of aluminum atoms. Here we note that the high Mn contents in TWIP steels allow for high Al additions without destabilizing the austenite.

In general, the influence of volumetric changes during isotropic deformations has larger influence on the diffusivity of hydrogen compared to volume preserving tetragonal strains. While the volumetric deformation typically results in a linear dependence of the solution energy on the volume, the influence of tetragonal strains yields effects of second order. This is in agreement with the notion that hydrogen leads to an isotropic expansion of the host alloy.

Spatially inhomogeneous Al distributions lead to an orientation dependent influence of a tetragonal distortion on the diffusion of hydrogen. High local aluminum concentrations have the potential to reduce the diffusion coefficient locally by up to three orders of magnitude in the room temperature regime. For a careful investigation of this effect, large scale Monte Carlo simulations with an emphasis on percolation effects may shed further light on this issue.

Competing Interests

The authors declare that they have no competing interests.


This work has been supported by the Collaborative Research Center (SFB) 761 Steel ab initio of the German Research Foundation (DFG). The authors gratefully acknowledge the computing time granted on the supercomputer JURECA at the Julich Supercomputing Centre (JSC). Discussions with Tilmann Hickel are highly appreciated by the authors.


[1] M. Koyama, H. Springer, S. V. Merzlikin, K. Tsuzaki, E. Akiyama, and D. Raabe, "Hydrogen embrittlement associated with strain localization in a precipitation-hardened Fe-MnAl-C light weight austenitic steel," International Journal of Hydrogen Energy, vol. 39, no. 9, pp. 4634-4646, 2014.

[2] C. Scott, S. Allain, M. Faral, and N. Guelton, "The development of a new Fe-Mn-C austenitic steel for automotive applications," Revue de Metallurgie, vol. 103, no. 6, pp. 293-302, 2006.

[3] B. De Cooman, J. Kim, and K.-G. Chin, High Mn TWIP Steels for Automotive Applications, InTech, Rijeka, Croatia, 2011.

[4] D. Barbier, N. Gey, S. Allain, N. Bozzolo, and M. Humbert, "Analysis of the tensile behavior of a TWIP steel based on the texture and microstructure evolutions," Materials Science and Engineering: A, vol. 500, no. 1-2, pp. 196-206, 2009.

[5] M. Koyama, T Sawaguchi, and K. Tsuzaki, "TWIP effect and plastic instability condition in an Fe-Mn-C austenitic steel," ISIJ International, vol. 53, no. 2, pp. 323-329, 2013.

[6] I. Gutierrez-Urrutia and D. Raabe, "Dislocation and twin substructure evolution during strain hardening of an Fe-22wt.% Mn-0.6 wt.% C TWIP steel observed by electron channeling contrast imaging," Acta Materialia, vol. 59, no. 16, pp. 6449-6462, 2011.

[7] D. R. Steinmetz, T Japel, B. Wietbrock et al., "Revealing the strain-hardening behavior of twinning-induced plasticity steels: theory, simulations, experiments," Acta Materialia, vol. 61, no. 2, pp. 494-510, 2013.

[8] M. Koyama, T Sawaguchi, T Lee, C. S. Lee, and K. Tsuzaki, "Work hardening associated with -martensitic transformation, deformation twinning and dynamic strain aging in Fe-17Mn-0.6C and Fe-17Mn-0.8C TWIP steels," Materials Science and Engineering: A, vol. 528, no. 24, pp. 7310-7316, 2011.

[9] S. Allain, J.-P. Chateau, and O. Bouaziz, "A physical model of the twinning-induced plasticity effect in a high manganese austenitic steel," Materials Science and Engineering: A, vol. 387-389, no. 1-2, pp. 143-147, 2004.

[10] G. Frommeyer, U. Brux, and P. Neumann, "Supra-ductile and high-strength manganese-TRIP/TWIP steels for high energy absorption purposes," ISIJ International, vol. 43, no. 3, pp. 438-446, 2003.

[11] A. Grajcar, S. Kolodziej, and W. Krukiewicz, "Corrosion resistance of high-manganese austenitic steels," Archives of Materials Science and Engineering, vol. 41, no. 2, pp. 77-84, 2010.

[12] R. Frohmberg, W. Barnett, and A. Troiano, "Delayed failure and hydrogen embrittlement in steel," Defense Technical Information Center (DTIC Document) 54-320, 1954.

[13] T P Perng and C. J. Altstetter, "Comparison of hydrogen gas embrittlement of austenitic and ferritic stainless steels," Metallurgical Transactions A, vol. 18, no. 1, pp. 123-134, 1987

[14] I.-J. Park, K.-H. Jeong, J.-G. Jung, C. S. Lee, and Y.-K. Lee, "The mechanism of enhanced resistance to the hydrogen delayed fracture in Al-added Fe-18Mn-0.6C twinning-induced plasticity steels," International Journal of Hydrogen Energy, vol. 37, no. 12, pp. 9925-9932, 2012.

[15] M. Koyama, E. Akiyama, and K. Tsuzaki, "Effects of static and dynamic strain aging on hydrogen embrittlement in TWIP steels containing al," ISIJ International, vol. 53, no. 7, pp. 1268-1274, 2013.

[16] M. Koyama, E. Akiyama, T. Sawaguchi, D. Raabe, and K. Tsuzaki, "Hydrogen-induced cracking at grain and twin boundaries in an Fe-Mn-C austenitic steel," Scripta Materialia, vol. 66, no. 7, pp. 459-462, 2012.

[17] M. Koyama, E. Akiyama, K. Tsuzaki, and D. Raabe, "Hydrogen-assisted failure in a twinning-induced plasticity steel studied under in situ hydrogen charging by electron channeling contrast imaging," Acta Materialia, vol. 61, no. 12, pp. 4607-4618, 2013.

[18] M. Koyama, E. Akiyama, and K. Tsuzaki, "Hydrogen embrittlement in a Fe-Mn-C ternary twinning-induced plasticity steel," Corrosion Science, vol. 54, no. 1, pp. 1-4, 2012.

[19] A. Grajcar, "Corrosion resistance of high-Mn austenitic steels for the automotive industry," Corrosion Resistance, pp. 353-376, 2012.

[20] A. Grajcar, R. Kuziak, and W. Zalecki, "Third generation of AHSS with increased fraction of retained austenite for the automotive industry," Archives of Civil and Mechanical Engineering, vol. 12, no. 3, pp. 334-341, 2012.

[21] H. Hata, T. Murakami, A. Ibano, F. Yuse, and J. Kinugasa, "Cold-rolled steel sheet," US Patent 8,876,986, 2014.

[22] T. Michler and J. Naumann, "Hydrogen environment embrittlement of austenitic stainless steels at low temperatures," International Journal of Hydrogen Energy, vol. 33, no. 8, pp. 2111-2122, 2008.

[23] M. Louthan Jr., R. McNitt, and R. Sisson Jr., "Environmental degradation of engineering materials in hydrogen," Tech. Rep., Laboratory for the Study of Environmental Degradation of Engineering Materials, Virginia Polytechnic Institute and State University, Blacksburg, Va, USA, 1981.

[24] C. San Marchi, B. P. Somerday, X. Tang, and G. H. Schiroky, "Effects of alloy composition and strain hardening on tensile fracture of hydrogen-precharged type 316 stainless steels," International Journal of Hydrogen Energy, vol. 33, no. 2, pp. 889-904, 2008.

[25] V G. Gavriljuk, V N. Shivanyuk, and J. Foct, "Diagnostic experimental results on the hydrogen embrittlement of austenitic steels," Acta Materialia, vol. 51, no. 5, pp. 1293-1305, 2003.

[26] L. Ismer, T Hickel, and J. Neugebauer, "Ab initio study of the solubility and kinetics of hydrogen in austenitic high Mn steels," Physical Review B, vol. 81, no. 9, Article ID 094111, 2010.

[27] J. von Appen, R. Dronskowski, A. Chakrabarty, T Hickel, R. Spatschek, and J. Neugebauer, "Impact of Mn on the solution enthalpy of hydrogen in austenitic Fe-Mn alloys: a first-principles study," Journal of Computational Chemistry, vol. 35, no. 31, pp. 2239-2244, 2014.

[28] G. Kresse and J. Furthmuller, "Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set," Physical Review B, vol. 54, no. 16, pp. 11169-11186, 1996.

[29] P. E. Blochl, "Projector augmented-wave method," Physical Review B, vol. 50, no. 24, pp. 17953-17979, 1994.

[30] J. P. Perdew, K. Burke, and M. Ernzerhof, "Generalized gradient approximation made simple," Physical Review Letters, vol. 77, no. 18, pp. 3865-3868, 1996.

[31] H. J. Monkhorst and J. D. Pack, "Special points for Brillouinzone integrations," Physical Review B, vol. 13, no. 12, pp. 5188-5192, 1976.

[32] M. Methfessel and A. T Paxton, "High-precision sampling for Brillouin-zone integration in metals," Physical Review B, vol. 40, no. 6, pp. 3616-3621, 1989.

[33] A. Sieverts, "Absorption of gases by metals," Zeitschrift fur Metallkunde, vol. 21, pp. 37-46, 1929.

[34] E. Sjostedt and L. Nordstrom, "Noncollinear full-potential studies of y-Fe," Physical Review B, vol. 66, no. 1, Article ID 014447, 10 pages, 2002.

[35] E. J. Song, H. K. D. H. Bhadeshia, and D.-W. Suh, "Interaction of aluminium with hydrogen in twinning-induced plasticity steel," Scripta Materialia, vol. 87, pp. 9-12, 2014.

[36] F. Kormann, T. Hickel, and J. Neugebauer, "Inuence of magnetic excitations on the phase stability of metals and steels," Current Opinion in Solid State and Materials Science, vol. 20, no. 2, pp. 77-84, 2016.

[37] Y. Fukai, The Metal-Hydrogen System, Springer, Berlin, Germany, 2nd edition, 2005.

[38] R. A. Oriani, "The diffusion and trapping of hydrogen in steel," Acta Metallurgica, vol. 18, no. 1, pp. 147-157, 1970.

[39] G. Henkelman, B. P. Uberuaga, and H. Jonsson, "Climbing image nudged elastic band method for finding saddle points and minimum energy paths," The Journal of Chemical Physics, vol. 113, no. 22, pp. 9901-9904, 2000.

[40] G. Henkelman and H. Joonsson, "Improved tangent estimate in the nudged elastic band method for finding minimum energy paths and saddle points," The Journal of Chemical Physics, vol. 113, no. 22, pp. 9978-9985, 2000.

[41] D. Sheppard, P. Xiao, W. Chemelewski, D. D. Johnson, and G. Henkelman, "A generalized solid-state nudged elastic band method," The Journal of Chemical Physics, vol. 136, no. 7, Article ID 074103, 2012.

C. Huter, (1,2) S. Dang, (1) X. Zhang, (2) A. Glensk, (2) and R. Spatschek (1,2)

(1) Institute for Energy and Climate Research, Forschungszentrum Julich GmbH, 52425 Julich, Germany

(2) Computational Materials Design Department, Max-Planck Institut fur Eisenforschung, 40237 Dusseldorf, Germany

Correspondence should be addressed to R. Spatschek;

Received 15 May 2016; Accepted 7 August 2016

Academic Editor: Pavel Lejcek

Caption: Figure 1: The supercell of the austenitic Fe-Mn system; Fe atoms are shown in yellow and Mn atoms in purple. The distribution of the Mn atoms yields only two types of octahedral interstices and one inequivalent site for the substitution Fe [right arrow] Al which makes it an ideal reference for the study of the [Fe.sub.23] [Mn.sub.8]Al system.

Caption: Figure 2: The [Fe.sub.23][Mn.sub.8]Al austenitic supercell. Fe atoms are yellow, Mn atoms are purple, and blue marks Al. The four different octahedral sites we consider are highlighted by polyhedra. The hydrogen atom can be located in direct neighbourhood of 3 Fe, 2 Mn, and 1 Al atoms ("oc1"), 4 Fe and 2 Mn atoms ("oc2"), 6 Fe atoms ("oc3"), or 5 Fe and 1 Al atom ("oc4"). Not shown here are the tetrahedral sites. We note that the oc2 configuration has the same next neighbour configuration as our reference octahedral site in the [Fe.sub.24]Mn, system, 4 Fe and 2 Mn atoms, but differs by the substitution of one Fe by Al. The oc1 case corresponds to the substitution of one Fe atom at the reference site with an Al atom, changing the next neighbourhood configuration as 4 Fe 2 Mn [right arrow] 3Fe2 Mn 1 Al.

Caption: Figure 3: Hydrogen solution energies for the different octahedral interstitial sites in [Fe.sub.24][Mn.sub.8] and [Fe.sub.24][Mn.sub.8]Al versus lattice constant []. The different curves demonstrate the effect of aluminum on the solution energy. The latter is split into a chemical and a volumetric contribution; see main text. For all configurations the variation of the solution energy with the lattice constant is similar, as well as the volumetric contributions, whereas the chemical contributions differ significantly, indicating the strong preference of H to avoid an aluminum rich nearest neighbour environment. The vertical lines show the equilibrium lattice constants of the different configurations.

Caption: Figure 4: The total energy of the [Fe.sub.23][Mn.sub.8]Al system with hydrogen at the oc1 site. The coloured curves show the dependence of the energy on the orientation of the strain relative to the preferred elongation axis of the system. The dashed black curve shows the averaged energy.

Caption: Figure 5: Hydrogen solution energy for the octahedral interstitial sites as function of the applied tetragonal distortion. The effect of the strain is much smaller than the chemical effect due to the substitution of Fe by Al.

Caption: Figure 6: Ratio of the diffusion coefficients according to Oriani's theory as described by (6). The isotropic deformation leads to changes of the apparent diffusion coefficient by about one order of magnitude for a strain [delta] = [+ or -]0.01 at room temperature. In all cases the presence of Al reduces the diffusion coefficient also by one order of magnitude in comparison to the [Fe.sub.24][Mn.sub.8] at ambient temperature.

Caption: Figure 7: The diffusion barriers [E.sub.Diff] for the system before Al alloying, see the lower curve, and the site oc1 in vicinity of the Al atom, see the upper curve. The grey bars mark from left to right the optimal volume of the reference site and oc1. We recall that, at zero pressure, the shift in barrier height due to substituting an Fe atom in the reference system by an Al atom is about 126 meV.

Caption: Figure 8: Ratio of diffusion coefficients corresponding to Oriani's theory for tetragonal strain. We note that the tetragonal deformation has a comparably weak effect on the apparent diffusivity. The ratio of the diffusion coefficients in the deformed systems varies by less than one order of magnitude.

Caption: Figure 9: The diffusion barriers [E.sub.Diff] for the system before Al alloying, see the two middle curves in yellow and orange (ref), the diffusion barrier for the alloyed system from the octahedral site oc1 in direct vicinity of an Al atom to a tetrahedral site with 1 neighbouring Fe, 2 neighbouring Mn, and 1 neighbouring Al atoms (three upper curves oc1), and the diffusion barriers for the alloyed system from the octahedral site oc2 distant to an Al atom to a tetrahedral site with 2 neighbouring Fe and 2 neighbouring Mn atoms (three lower curves oc2). Note that the shift in the diffusion barrier for the sites in the vicinity of the Al atom is about 126 meV. We recognise that the orientation of the tetragonal strain relative to the stiff axis of the system has appreciable influence especially for sites in the neighbourhood of the Al atom.
Table 1: The solution enthalpies of hydrogen at the four
investigated octahedral sites and in the Fe-Mn reference system.
The second row describes the nearest neighbour (n.n.) chemical
environment of the hydrogen atom in the octahedral position,
where, for example, 4-2-0 denotes that it is surrounded by 4 Fe,
2 Mn, and no Al atoms.

[sigma]                     Fe-Mn     oc1      oc2      oc3      oc4

n.n. (Fe-Mn-Al)             4-2-0    3-2-1    4-2-0    5-0-1    6-0-0
[E.sup.[sigma]] (P = 0)     0.054    0.140    -0.010   0.130    0.073

Table 2: Energies at equilibrium volume, bulk modulus, and its
derivative with respect to pressure as obtained from Murnaghan
fits of the ab initio data.

System                            [E.sub.0] (eV)    [B.sub.0] (GPa)

[Fe.sub.24][Mn.sub.8]                -265.581            176.6
[Fe.sub.24][Mn.sub.8]H               -268.922            175.6
[Fe.sub.23][Mn.sub.8]Al              -261.717            168.5
[Fe.sub.23][Mn.sub.8]AlH (oc1)       -264.992            168.3
[Fe.sub.23][Mn.sub.8]AlH (oc2)       -265.141            167.4

System                            [partial derivative]B/
                                  [partial derivative]P

[Fe.sub.24][Mn.sub.8]                      4.78
[Fe.sub.24][Mn.sub.8]H                     4.70
[Fe.sub.23][Mn.sub.8]Al                   4.847
[Fe.sub.23][Mn.sub.8]AlH (oc1)            4.763
[Fe.sub.23][Mn.sub.8]AlH (oc2)            4.910
COPYRIGHT 2016 Hindawi Limited
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2016 Gale, Cengage Learning. All rights reserved.

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:Research Article
Author:Huter, C.; Dang, S.; Zhang, X.; Glensk, A.; Spatschek, R.
Publication:Advances in Materials Science and Engineering
Date:Jan 1, 2016
Previous Article:Research on the impact of 3D printing on the international supply chain.
Next Article:Effect of rubberized bitumen blending methods on permanent deformation of SMA rubberized asphalt mixtures.

Terms of use | Privacy policy | Copyright © 2021 Farlex, Inc. | Feedback | For webmasters