Creating crystals to study quantum effects.

Small gatherings of atoms tend to behave differently from huge crowds: So-called bulk properties can change quite a bit when the sample contains just a few hundred or thousand atoms. And researchers seeking to shrink computer chips to angstrom sizes want to know exactly how these properties differ.

Toward that goal, two research groups have reported progress in making semiconductors in sizes small enough that their dimensions affect the wave-like nature of their electrons.

"We clearly see quantum-size effects in the little crystallites," says Louis Brus, a physical chemist at AT&T Bell Laboratories in Murray Hill, N.J.

Study of these crystallites may explain puzzling phenomena such as photoluminescence in silicon made porous by acid etching. Some scientists have suggested that etching leaves quantum-size wires or dots whose dimensions limit the movements of electrons and lead to light emission; others attribute silicon's glow to other causes (SN: 5/16/92, p.324).

Brus and Bell Labs colleague Karl Littau made silicon crystals with diameters ranging from less than 2 nanometers to about 8 nanometers by heating a gaseous silicon-hydrogen compound called disilane to 850 [degrees] C. This high temperature yields an aerosol of crystals that the scientists sort by size.

Spectroscopic studies of the sorted crystals reveal that the tiniest crystals luminesce a visible red. Larger particles emit infrared light. "This is very similar to what you see in porous silicon," Brus says. He reported these results in Chicago last week at the Sixth International Symposium on Small Particles and Inorganic Clusters. Brus plans ever more precise spectroscopic analyses of these crystallites.

Taking a different tack, James R. Heath makes small crystals from solution. "I'm aiming for complete chemical control of the surface structure as well as of the size," says Heath, a chemist at the IBM Thomas J. Watson Research Center in Yorktown Heights, N.Y. "With wet synthesis, you can [use] a lot of different kinds of molecules and can control the parameters to a much finer degree."

Techniques such as molecular beam epitaxy also offer that kind of control, but only for building thin films, not for tiny, three-dimensional crystals, he adds.

At the Chicago meeting, Heath described success in making 5-nanometer silicon crystals from a hexane solution containing both silicon tetrachloride and a silicon compound with three chlorine atoms and an organic side chain attached. He seals the solution in a special beaker and heats it to 400 [degrees] C. That high temperature causes the pressure inside to build to several hundred times that of the atmosphere, he says. Adding sodium causes the chlorine to break away and precipitate as table salt, leaving behind very reactive silicon. That silicon condenses and anneals.

The bulkiness of the organic side groups causes them to stick out from the surface of the silicon crystal that forms. Thus, by altering the proportions of these two silicon compounds in the hexane solution, Heath can control the surface-to-volume ratio and consequently the size of the crystals formed. Increasing the relative amount of the organic silicon chloride results in smaller crystals.

"If you choose your organic group wisely, you may be able to use it to size the crystal and to glue it to a surface," he adds. By attaching these silicon crystals to a metal, he hopes to make miniature circuits--like shrunken computer chips.

Last week, he succeeded in making a germanium "quantum wire," the first produced through wet synthesis, Heath told SCIENCE NEWS. This demonstrates that the technique lets researchers customize the shape as well as the size of the crystals, he says. The wire's small diameter should inhibit the movement of electrons in that direction, so that they can flow freely only along the wire's few-micron length. Heath expects to find interesting quantum-size effects on the germanium's conduction properties.

Other scientists have generated beams of clusters even smaller than Heath's or Brus', but "[ours] are the only approaches where you get macroscopic samples," says Brus.
COPYRIGHT 1992 Science Service, Inc.
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 1992, Gale Group. All rights reserved. Gale Group is a Thomson Corporation Company.

Article Details
Printer friendly Cite/link Email Feedback
Author:Pennisi, Elizabeth
Publication:Science News
Date:Oct 3, 1992
Previous Article:The warped world of mental maps; students worldwide share a skewed vision of the continents.
Next Article:Social ties boost immune function.

Related Articles
Shaking up quasicrystals.
New approach makes silicon's red glow blue.
Whipping up atomic crystals bound by light.
Quiet times in iron-walled quantum corrals.
Bringing nanomagnets into quantum step.
Impurities give crystals that special glow.
High vacuum produces ultrapure crystals.
A crystal takes on an unusual topology. (Chemistry).

Terms of use | Privacy policy | Copyright © 2021 Farlex, Inc. | Feedback | For webmasters |