Casting mold dryers help increase efficiency.

To achieve the highest throughput in a sand casting shop, the refractory wash could be force-dried using a convection oven. These ovens are called sand core dryers, mold dryers or core drying ovens. They operate at 200-400F and dry the cores or molds in 10-30 minutes, as opposed to the 10-20 hours required by passive drying at ambient temperature. The oven temperature and drying time depend on the mold size, sand porosity, and the efficiency of the oven delivering the heat. To minimize energy use and reduce operating costs, the oven should be designed with tight temperature uniformity, high air velocity (velocities greater than 5,000 ft. per minute are common) and good end seals to prevent hot air loss. This design provides good results with a lower operating temperature.

Common accessories used with sand core dryers are forced air coolers to cool the sand molds for handling, humidity sensing systems to optimize the exhaust rate, belt conveyors, slat conveyors, and PLC control.

Due to high production rate requirements, many casters utilize conveyors to carry the molds through the dryer. A company in Milwaukee needed to dry a zircon-based core wash on sand molds used in the manufacture of large gears. The molds had dimensions of 70 x 50 x 40 in. (1,778 x 1,270 x 1,016 mm) and weighed 3,000 lbs. each. They needed to be dried at the rate of one every 5 minutes, for a total production rate of 36,000 lbs. per hour. Conventional conveyor designs were not up to the task. The traditional design utilized a flat wire belt conveyor riding on a friction style slide bed, a structural steel frame to support the moving conveyor belt. At this combination of mold weight and conveyor speed (1 foot per minute), a conventional design would quickly wear out due to the heavy load on the conveyor and the resulting friction between the belt and slide bed.

[FIGURA 1 OMITTED]

[FIGURA 2 OMITTED]

Wisconsin Oven (East Troy, Wisconsin) met the challenge with a roller belt support system whereby the conveyor belt rode on top of specially designed high temperature rollers (Fig. 1).

The rollers utilized a high temperature lubricant that reduced the friction by a factor of eight in comparison to a conventional friction style slide bed arrangement. In addition to significantly extending the life of the conveyor belt, this reduced design allowed the use of a smaller conveyor drive motor. The result was a long-lasting conveyor design that was also rugged and energy efficient.

The conveyor oven had an operating temperature of 575F (302C), and a heated length of 21 ft. (6,400mm), which required 42 support rollers located on 6-in. centers.

In another instance, a manufacturer of sensors located in the Midwest needed to expand their production capacity. A conveyorized mold drying oven with a production rate of 3,000 lbs. per hour provided an effective solution to increase their production rate. The company processed two different molds with different heating times. Mold A required a 45-minute drying time and mold B required 22.5 minutes. Based on the part size and production rate, an oven heated length of 24 ft. was necessary to achieve 45 minutes of heating, and a 12 ft. length was sufficient for 22.5 minutes of heating. Traditional conveyor ovens use a conveyor belt running through the oven chamber, whereby all the molds running through the oven at the same time are exposed to the heat for the same duration. Since they all ride on the same conveyor belt, traditional oven designs prohibit different heating times for different molds being run through the oven at the same time.

In order to provide different heating times for the two different molds types, Wisconsin Oven provided a unique bi-directional dual conveyor oven (Fig. 2). The mold drying oven utilizes two independently powered belt conveyors, each with its own drive system and speed control. Additionally, they run in opposite directions. After mold A exits conveyor #1, the operator places it on conveyor #2 to travel back through the oven to achieve the entire 45 minute drying time. When the B molds exit the oven, they are removed from the conveyor, since they had completed their 22.5 minute drying time.
COPYRIGHT 2016 American Foundry Society, Inc.
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2016 Gale, Cengage Learning. All rights reserved.

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:CASTING INNOVATIONS
Publication:Modern Casting
Date:Oct 1, 2016
Words:711
Previous Article:Metalcasting process control: American Foundry Society Technical Department.
Next Article:Safety animations for manufacturing.

Terms of use | Copyright © 2017 Farlex, Inc. | Feedback | For webmasters