Solving the problem of adhesion to plastics and rubber.

Why is bonding to plastics and rubber so difficult?

The age old problem of obtaining good adhesion of paints, coatings, sealants and glues to traditionally hard to bond to materials like polypropylene has challenged engineers ever since its development and introduction by ICI (language) ICI - An extensible, interpretated language by Tim Long with syntax similar to C. ICI adds high-level garbage-collected associative data structures, exception handling, sets, regular expressions, and dynamic arrays.  in the late 1930's. Examples of the materials in question are Polypropylene (PP), Polyethylene (PE), High-Density Polyethylene high-density polyethylene
n. Abbr. HDPE
A strong, relatively opaque form of polyethylene having a dense structure with few side branches off the main carbon backbone.
 (HDPE HDPE
abbr.
high-density polyethylene
) and EPDM EPDM Ethylene-Propylene-Diene-Monomer
EPDM Enterprise Product Data Management
EPDM Ethylene Propylene Dimonomer (industrial/commercial piping/plumbing components)
EPDM Engineering Product Data Management
, all of which have low surface energies of between 29 - 36 Dynes/ [cm.sup.2] (mN/m).

Achieving any level of adhesion to low surface energy materials such as PR PE or PTFE PTFE

polytetrafluoroethylene.
 is difficult at the best of times and sometimes near impossible, basically as these materials are non-stick, meaning printing inks rub off, glued parts fail, gaskets and seals won't bond and paint and coating will not adhere. Typically these problems are experienced throughout the automotive industry The automotive industry is the industry involved in the design, development, manufacture, marketing, and sale of motor vehicles. In 2006, more than 69 million motor vehicles, including cars and commercial vehicles were produced worldwide. , medical device manufacturing industry and, in fact, in any industry that has to bond, print, or coat plastic or rubber components. These problems are becoming increasingly commonplace

with the increase in usage of polyolefins.

Generally polyolefins have what is called 'low surface energy' or 'non-polar' surfaces and no matter how much you attempt to clean or abrade a·brade
v.
1. To wear away by mechanical action.

2. To scrape away the surface layer from a part.


abrade (
 the surface, they remain hard or often impossible to paint, coat, print or bond to without resorting to harsh, environmentally damaging chemicals or high temperature flame torch treatments. A major UK automotive sub-supplier recently experienced this problem when they attempted to glue coverings to a range of polypropylene door panels and other internal passenger compartment parts. The PP injection moulded components were sprayed with an adhesive and then the covering applied. On testing, the finished parts failed due to very poor bond strength between the adhesive and the PP surface of the components; the coverings simply peeled off.

[ILLUSTRATION OMITTED]

To make things worse, the ever increasing drive towards the use of UV curing or water-based adhesives, paints, inks and coatings means that even materials that have traditionally given acceptable bonding results, such as ABS, nylon (PA), glass filled nylon and composites to name but a few, can also become difficult to bond to. This problem was highlighted earlier this year at another major UK automotive component manufacturer when it introduced a new product moulded from glass filled nylon and needed to apply a water-based paint to give a car body-matching paint finish. Quickly the company realised that the paint finish was failing its customer's paint adhesion test.

Along with gluing and painting, printing onto plastics often presents a similar adhesion issue, this can be critical on medical devices or where high print quality is required, for example syringe marking, barcodes etc.

[ILLUSTRATION OMITTED]

The strength of attraction between a material and a coating is determined by the relative surface energy and surface tension of the materials. The higher the solid's surface energy relative to the liquid's surface tension, the greater the molecular attraction; this draws the paint, ink or adhesive closer for high bond strength. The lower the solid's surface energy relative to the liquid's surface tension, the weaker the attractive forces are; this will repel the coating. The challenge faced by producers of extruded or injection moulded components is to increase the surface energy (polarity) of the material to a level significantly higher than that of the surface tension of the paint, coating, adhesive or printing ink, so that the surface acquires a strong chemical attraction chemical attraction
n.
The force of attraction between atoms that causes them to form and maintain certain combinations.
 to paints, coatings, sealants, adhesives etc. leading to significantly enhanced wetting and adhesion. Typically the surface energy of the substrate will need to exceed the surface tension of the ink, paint, coating or adhesive by at least 10 - 15 Dynes/ [cm.sup.2] (mN/m).

How can bond performance to plastics and rubber be improved?

Firstly, we need to understand what surface properties are required to obtain the ideal conditions for adhesion. There are many common misconceptions on what the best conditions required for the strongest bond are; should the surface be heated, abraded, solvent wiped? Sometimes these pre-treatments do no harm and may, on some occasions, even help a little, however, it is widely recognised that the ideal surface to bond to should be clean, dry, dust-free, smooth, non-porous, wettable (high surface energy) and polar.

Preparing a clean, dry, dust free, smooth and non-porous surface requires little discussion, however, creating a surface that exhibits good wettability and is 'polar' clearly does. There are several methods of increasing the surface energy and polarity of plastics and rubbers, including wet chemical treatments which are often harsh and environmentally damaging, high 1 temperature flame torch treatments, high voltage corona treatment and, finally, plasma surface activation which we will discuss in this edition.

[ILLUSTRATION OMITTED]

Plasma surface activation

Exposing low surface energy extruded or injection moulded components to the highly active environment of either vacuum or atmospheric plasma is a very effective and long-lasting method of increasing their surface energy and polarity. The component undergoes a very efficient surface treatment that is environmentally friendly, does not alter the bulk properties of the treated part and does not mark or discolour discolour or US discolor
Verb

to change in colour; to fade or stain

discoloration n

Verb 1.
 it in any way. The resulting highly activated surface will now have the required high surface energy and polarity necessary to ensure good wetting and adhesion of printing inks, paints, adhesives, coatings, potting materials etc. Plasma surface modification is widely used throughout a diverse range of industries and onto an ever-increasing range of substrates. In simple terms, plasma is generally described as a super ionised gas or as an electrically neutral medium of positive and negative particles and neutrals (atoms, radicals and molecules) and can react with a wide range of materials. 'Ionised' refers to the presence of free electrons, which are not bound to an atom or molecule. Plasma is created when a gas is subjected to a high-energy discharge; the gas breaks up into electrons, ions, highly reactive free radicals, short wave UV light photons and other excited particles. In general terms, when you subject atoms or molecules to enough energy, what happens very quickly is that the electrons around the nucleus start to 'boil off', the temperature becomes too high for them to stay contained in orbit around the nucleus. Plasma is not new; it was first described by Sir William Crook way back in 1879 and is the most common type of matter in the known universe whether measured by mass or volume. Every star is a giant ball of plasma; even the space between all of the stars is composed of plasma. Plasma is considered to be the fourth state of matter after solid, liquid and gas.

The free radicals and other particles that exist in the highly active plasma discharge can attach to the material's surface, resulting in the formation of additional polar groups, these have a strong chemical attraction to paints, coatings, sealants, inks and adhesives leading to significantly enhanced surface energy, polarity and therefore adhesion. Plasma surface modification equipment is available in two industrial configurations; vacuum plasma chambers that can process large volumes of parts in a single operation, and atmospheric plasma nozzles that can be fixed and are ideal for extruded parts, or robot mounted for parts with more complex geometries or where selective treatment is required.

FURTHER INFORMATION: WWW WWW or W3: see World Wide Web.


(World Wide Web) The common host name for a Web server. The "www-dot" prefix on Web addresses is widely used to provide a recognizable way of identifying a Web site.
.DYNETECHNOLOGY.CO.UK

BY CHRIS LINES, MANAGING DIRECTOR, DYNE dyne (dīn), unit of force in the cgs system of units, which is based on the metric system; an acceleration of 1 centimeter per second per second is produced when a force of 1 dyne is exerted on a mass of 1 gram.  TECHNOLOGY LTD LTD 1 Laron-type dwarfism 2 Leukotriene D 3 Long-term depression, see there 4. Long-term disability  
COPYRIGHT 2012 Euro Publishing Consultancy
No portion of this article can be reproduced without the express written permission from the copyright holder.
Copyright 2012 Gale, Cengage Learning. All rights reserved.

 Reader Opinion

Title:

Comment:



 

Article Details
Printer friendly Cite/link Email Feedback
Title Annotation:PLASMA FEATURE
Comment:Solving the problem of adhesion to plastics and rubber.(PLASMA FEATURE)
Author:Lines, Chris
Publication:British Plastics & Rubber
Article Type:Interview
Date:May 1, 2012
Words:1214
Previous Article:Polymer coating helps make phones water repellent.
Next Article:Fruit for schools packed in compostable film.
Topics:

Terms of use | Copyright © 2014 Farlex, Inc. | Feedback | For webmasters